Method for preparing sand-base water-permeable brick

A permeable brick and sand-based technology, applied in manufacturing tools, ceramic molding machines, etc., can solve the problems of low strength and poor water permeability, and achieve the effect of high strength, good water permeability, and high water permeability coefficient

Active Publication Date: 2012-07-11
RENCHSAND ECO ENVIRONMENT PROTECTION SCI & TECH CO LTD
View PDF6 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the defects of low strength and poor water permeability of sand-based permeable bricks prepared by the existing method, and provide a new preparation method of sand-based permeable bricks. The sand-based permeable bricks prepared by this method have Higher strength and better water permeability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0007] The preparation method of the sand-based permeable brick according to the present invention includes preparing a sand-based permeable brick prefabricated part, and subjecting the sand-based permeable brick prefabricated part to microwave curing, and the microwave curing conditions include: the curing temperature is 80-150°C , The curing time is 3-20 minutes. Preferably, the curing temperature is 100-140° C., and the curing time is 3-15 minutes.

[0008] According to the method provided by the present invention, the thickness of the sand-based permeable brick prefabricated part is not specifically limited, and those skilled in the art can determine it according to the thickness of the sand-based permeable brick in practical application. The thickness of the permeable brick prefabricated part is generally It can be 2-80 cm, preferably 2-40 cm, more preferably 2-20 cm.

[0009] According to the method provided by the present invention, the sand-based permeable brick prefa...

Embodiment 1

[0018] This example is used to illustrate the preparation method of the sand-based permeable brick provided by the present invention.

[0019] Add 0.5 parts by weight of ethanol in 5 parts by weight of bisphenol A epoxy resin (purchased from Zibo Shaohua Industry and Trade Co., Ltd., epoxy value 0.09-0.14mol / 100g), mix well, add 0.6 parts by weight of ethylenediamine to obtain glue. Then, the glue solution was added to 100 parts by weight of silica sand with an average particle diameter of 0.6 mm and mixed uniformly. Pour the resulting mixture into a steel mold with a size of 100×200×45 mm, using a hydraulic press model YAW4605 (purchased from Shanghai Xinsansi Measuring Instrument Manufacturing Co., Ltd.), at 20°C, apply 3000N / cm 2 The pressure is pressed for 1 minute, and then the pressure is released to obtain a sand-based permeable brick prefabricated part.

[0020] Then, the prefabricated sand-based permeable brick was cured by microwave at 130°C for 8 minutes, and demo...

Embodiment 2

[0024] This example is used to illustrate the preparation method of the sand-based permeable brick provided by the present invention.

[0025] Add 0.5 parts by weight of ethanol to 6 parts by weight of phenolic resin (purchased from Shandong Shengquan Chemical Co., Ltd., with a weight average molecular weight of 2000-20000), mix well, add 1.0 parts by weight of hexamethylenetetramine to obtain Glue. Then, the glue solution was added to 100 parts by weight of silica sand with an average particle diameter of 1 mm and mixed uniformly. Pour the resulting mixture into a steel mold with a size of 100×200×45 mm, using a hydraulic press model YAW4605 (purchased from Shanghai Xinsansi Measuring Instrument Manufacturing Co., Ltd.), at 20°C, apply 3000N / cm 2 The pressure is pressed for 1 minute, and then the pressure is released to obtain a sand-based permeable brick prefabricated part.

[0026] Then, the prefabricated sand-based permeable brick was cured by microwave at 100° C. for 15...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Average particle diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Epoxy valueaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for preparing a sand-base water-permeable brick. The method comprises the following steps: preparing a prefabricated part of the sand-base water-permeable brick and performing microwave solidification on the prefabricated part of the sand-base water-permeable brick, wherein the condition of the microwave solidification comprises solidifying temperature at 80-150 DEG C and solidifying time being 3-20 minutes. According to the method, the solidifying time is greatly shortened and the pressure resistance and water permeability of the sand-base water-permeable brick are obviously increased.

Description

technical field [0001] The invention relates to a preparation method of a sand-based permeable brick. Background technique [0002] At present, cement, asphalt, marble and other non-permeable materials are mostly used in urban construction to pave the ground. These hardened pavements make it difficult to exchange heat and moisture between the ground surface and the air, and the ability to naturally adjust the temperature and humidity of the urban ground is very poor, and the surface absorbs heat. Difficulties, resulting in a large amount of waste heat in the urban space, and a large amount of reflection on the ground to radiate solar heat, which leads to the phenomenon that the nighttime temperature in the city is higher than that in the suburbs. Moreover, in rainy days, the hardened pavement will prevent rainwater from infiltrating directly into the ground, causing water to accumulate everywhere, affecting the comfort and safety of the road. The healthy growth of surface v...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B28B11/00
Inventor 秦升益贾屹海秦申二马金奎
Owner RENCHSAND ECO ENVIRONMENT PROTECTION SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com