High-efficiency short-process heat treatment technology for marine titanium alloy

A titanium alloy, short-process technology, applied in the field of material processing, can solve the problems of low annealing efficiency, difficulty in achieving performance indicators, and difficult control of plate shape, etc., and achieve the effect of increased annealing efficiency and good performance uniformity

Active Publication Date: 2012-07-11
LUOYANG SUNRUI TI PRECISION CASTING
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the increase in the use of ships and civilian ships, the application of TA5 alloy plates is increasing, but the requirements for comprehensive performance indicators such as mechanical properties and process properties are relatively high, which results in a wide range of heat treatment for TA5 alloy plates. Narrow, the performance index is not easy to meet the requirements of GB / T3621
At present, the TA5 alloy sheet is mainly annealed in a continuous annealing furnace, but the price of the continuous annealing furnace is much higher than that of the ordinary roller hearth furnace, and the continuous annealing furnace is only used for continuous annealing of a single sheet, and the annealing efficiency is low. not easy to control

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] First, stack 12 pieces of 4mm TA5 alloy plates together, place a 50mm thick plain carbon steel plate on the top, raise the furnace temperature to 500°C and put it into the furnace. The heating rate is raised to 700°C, and the temperature is kept at this temperature for 200 minutes. The roller rotation frequency is 6Hz. Sampling tests were carried out according to GB / T3621-2007, and the results showed that the difference in yield strength and tensile strength of TA5 alloy plates stacked at different positions was not more than 25Mpa, the elongation was 20~22%, and the mechanical and process properties met GB / According to the requirements of T3621-2007, the unevenness of the plate is less than 8mm / m.

Embodiment 2

[0016] First, stack 11 pieces of 4mm TA5 alloy plates together, place a 30mm thick plain carbon steel plate on the top, raise the furnace temperature to 450°C and put it into the furnace. The heating rate is raised to 700°C, and the temperature is kept at this temperature for 160 minutes. The roller rotation frequency is 6 Hz. The TA5 alloy plate treated by this heat treatment process, the difference in yield strength and tensile strength of the TA5 alloy plate stacked in different positions is not more than 15Mpa, the elongation is between 19.5 and 22%, and the mechanical and process properties meet GB / According to the requirements of T3621-2007, the unevenness of the plate is less than 8mm / m.

Embodiment 3

[0018] First, stack eight 5mm TA5 alloy plates together, place a 50mm thick plain carbon steel plate on top, raise the furnace temperature to 500°C and put it into the furnace. The heating rate is raised to 700°C, and the temperature is kept at this temperature for 150 minutes. The roller rotation frequency is 5 Hz. The TA5 alloy plate treated by this heat treatment process, the difference in yield strength and tensile strength of the TA5 alloy plate stacked at different positions is not more than 20Mpa, the elongation is between 19% and 23%, and the mechanical properties and process properties meet GB / T3621-2007 requirements, plate unevenness is less than 10mm / m.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-efficiency short-process heat treatment technology for marine titanium alloy, wherein a plurality of TA5 (Titanium Alloy5) plates are overlapped, a Q235 pressing plate is arranged on the TA5 plates, the thickness of the Q235 pressing plate ranges from 30 to 50 mm, the roughness degree of the pressing plate is less than or equals to 5 mm / m, the charging is performed at the temperature ranging from 400 to 500 DEG C, heat preservation is performed for 50 to 70 minutes at the temperature of 550 DEG C, and temperature rises at the speed of 4 to 5 DEG C / min until reaching 700 DEG C and then heat preservation is performed for 150 to 200 minutes; in addition, the TA5 plates move about in a roller hearth furnace in a reciprocating manner during the whole heat treatment process, the rotational frequency of a roller ranges from 5 to 6 Hz, and the rotational frequency of the roller ranges from 10 to 15 Hz in a wind cooling stage. The TA5 plates that are processed through the high-efficiency short-process heat treatment technology achieve good performance uniformity, the shear strength of all parts of the TA5 plates ranges from 680 to 700 Mpa, the tensile strength ranges from 700 to 725Mpa, the elongation percentage ranges from 19 to 23 percent, and the high-efficiency short-process heat treatment technology is a plurality of times the annealing efficiency of a continuous annealing furnace.

Description

technical field [0001] The invention relates to a material processing technology, in particular to a high-efficiency short-flow heat treatment process for marine titanium alloys. Background technique [0002] With the increase in the use of ships and civilian ships, the application of TA5 alloy plates is increasing, but the requirements for comprehensive performance indicators such as mechanical properties and process properties are relatively high, which results in a wide range of heat treatment for TA5 alloy plates. Narrow, the performance index is not easy to meet the requirements of GB / T3621. At present, the TA5 alloy sheet is mainly annealed in a continuous annealing furnace, but the price of the continuous annealing furnace is much higher than that of the ordinary roller hearth furnace, and the continuous annealing furnace is only used for continuous annealing of a single sheet, and the annealing efficiency is low. Not easy to control either. Contents of the inventi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22F1/18
Inventor 王树军包淑娟刘茵琪王非顾新盛李渤渤
Owner LUOYANG SUNRUI TI PRECISION CASTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com