Oil-resistant silicon rubber
A silicone rubber and oil-resistant technology, applied in the field of oil-resistant silicone rubber, can solve the problems of high cost and low temperature resistance of rubber materials
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0087] The third aspect of the present invention provides a method for preparing the oil-resistant silicone rubber of the present invention, which includes the following steps:
[0088] Provide the components of the present invention;
[0089] The components are kneaded at 110-175°C, and then vacuumed and molded to obtain oil-resistant silicone rubber.
[0090] Preferably, the components are kneaded at 110-120°C.
[0091] In a specific embodiment of the present invention, the components are fed in a multiple feeding manner.
[0092] In a specific embodiment, the raw rubber 0.08% and 0.16% are put into the kneader, and the white carbon black is added in batches about 3-4 times. After each agglomeration, the next white carbon black is added. When adding white carbon black, start adding hydroxy silicone oil, and finally adding hydrogen-containing silicone oil and dimethyl silicone oil when forming a dough. Finally, the temperature in the kneader is about 110-120°C, the rubber material bec...
Example Embodiment
[0098] Example 1
[0099] Summary of the invention: The formula is as follows by improving the ratio of silica gel and raw materials:
[0100] Use methyl vinyl rubber 0.08% 71 parts, 0.16% 29 parts, molecular weight 580-62 million, hydroxy silicone oil 2.2 parts, hydrogen silicone oil 1.4 parts, methyl silicone oil 1.1 parts, zinc stearate 0.42 parts, Degu 42 parts of Sai 928 white carbon black, 29 parts of 3000 mesh clay, 9 parts of polytetrafluoroethylene, silane coupling agent A-1721.2 parts.
[0101] The glue process is as follows:
[0102] Put the raw rubber 0.08% and 0.16% into the kneader, add the white carbon black in batches about 3-4 times, add the next white carbon black after each agglomeration, and start adding the white carbon black the second time Hydroxy silicone oil, add hydrogen-containing silicone oil and methyl silicone oil when the final agglomeration is formed, and finally the temperature in the kneader is about 110-120℃, the rubber material becomes a large grou...
Example Embodiment
[0106] Example 2
[0107] Summary of the invention: The formula is as follows by improving the ratio of silica gel and raw materials:
[0108] Use methyl vinyl raw rubber 0.07% 71 parts, 0.15% 29 parts, molecular weight between 580 and 620,000, hydroxy silicone oil 2.2 parts, hydrogen silicone oil 1.4 parts, methyl silicone oil 1.1 parts, precipitation method white carbon black 42 parts, 3000 29 parts of mesh clay, 9 parts of polytetrafluoroethylene, and silane coupling agent A-1721.2 parts.
[0109] The glue process is as follows:
[0110] Put the raw rubber 0.08% and 0.16% into the kneader, add the white carbon black in batches about 3-4 times, add the next white carbon black after each agglomeration, and start adding the white carbon black the second time Hydroxy silicone oil, add hydrogen-containing silicone oil and methyl silicone oil when the final agglomeration is formed, and finally the temperature in the kneader is about 110-120℃, the rubber material becomes a large group, a...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap