Ultraviolet wear resistant primer and preparation method thereof

A wear-resistant primer and photoinitiator technology, applied in polyurea/polyurethane coatings, coatings, etc., can solve the problems of insufficient wear-resistant hardness of the paint, blurred board surface, and increased overall cost, and achieve convenient processing, The formula is simple and reasonable, and the effect of wear resistance is good

Active Publication Date: 2012-08-01
上海蓝宝涂料有限公司
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Many of the existing paints used on the surface of wooden floors are not wear-resistant and hard enough, which leads to the fact that after the wooden floor is paved, it is easy to wear the paint when stepping on it, which affects the overall aesthetic feeling; in order to overcome this problem, some The coating amount of the paint is enlarged to increase the wear resistance and hardness, which will lead to an increase in the overall cost
There are also some hard powders added to the paint, but this approach often leads to blurred boards after painting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultraviolet wear resistant primer and preparation method thereof
  • Ultraviolet wear resistant primer and preparation method thereof
  • Ultraviolet wear resistant primer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The UV wear-resistant primer of the present invention consists of the following components in parts by weight:

[0024]

[0025]

[0026] Preparation method: Mix and dissolve tripropylene glycol diacrylate and trimethylolpropane triacrylate according to the above ratio, then add photoinitiator and stir again, then add polyurethane acrylate and mix and stir, then add gas phase two while stirring Silicon oxide and aluminum oxide, after adding, stir for 10 minutes, then stand still for 1-2 hours and filter through a 150-mesh filter.

Embodiment 2

[0028] The UV wear-resistant primer of the present invention consists of the following components in parts by weight:

[0029]

[0030] Preparation method: Mix and dissolve tripropylene glycol diacrylate and trimethylolpropane triacrylate according to the above ratio, then add photoinitiator and stir again, then add polyurethane acrylate and mix and stir, then add gas phase two while stirring Silicon oxide and aluminum oxide, after adding, stir for 15 minutes, then stand still for 1-2 hours and filter through a 150-mesh filter.

Embodiment 3

[0032] The UV wear-resistant primer of the present invention consists of the following components in parts by weight:

[0033]

[0034]

[0035] Preparation method: Mix and dissolve tripropylene glycol diacrylate and trimethylolpropane triacrylate according to the above ratio, then add photoinitiator and stir again, then add polyurethane acrylate and mix and stir, then add gas phase two while stirring Silica and Al2O3, after adding, stir for 10-20 minutes, then stand still for 1-2 hours and filter through a 150-mesh filter.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an ultraviolet wear resistant primer and a preparation method thereof. The ultraviolet wear resistant primer comprises the following components in parts by weight: 55-75 of urethane acrylate, 10-20 of tripropylene glycol diacrylate, 5-15 of trimethylolpropane triacrylate, 1-5 of photoinitiator, 10-40 of aluminum oxide and 0.5-3 of fumed silica. The preparation method provided by the invention comprises the following steps of: firstly mixing, dissolving and stirring the tripropylene glycol diacrylate and the trimethylolpropane triacrylate, then adding the photoinitiator and stirring, adding the urethane acrylate for blending and stirring, adding the fumed silica and the aluminum oxide while stirring, stirring for 10-20 minutes after addition, resting for 1-2h, and filtering by using a filter screen to obtain the ultraviolet wear resistant primer. The ultraviolet wear resistant primer provided by the invention has good wear-resistant performance and high hardness; after wood floors are coated by the ultraviolet wear resistant primer, and the wood floors have good whole definition; and the formula is simple and reasonable. The preparation method provided by the invention has the advantages that the technology is simple and the processing is convenient.

Description

technical field [0001] The invention relates to a UV wear-resistant primer, and also relates to a method for preparing the UV wear-resistant primer. Background technique [0002] Many of the existing paints used on the surface of wooden floors are not wear-resistant and hard enough, which leads to the fact that after the wooden floor is paved, it is easy to wear the paint when stepping on it, which affects the overall aesthetic feeling; in order to overcome this problem, some The amount of paint applied is enlarged to increase wear resistance and hardness, which will lead to an increase in overall cost. There is also adding some hard powder to the paint, but this approach often leads to blurred board surface after painting. [0003] The wear-resistant primer of the present invention increases the wear resistance after painting and does not affect the overall clarity after painting. Contents of the invention [0004] The purpose of the present invention is to overcome the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D7/12
Inventor 冯士国
Owner 上海蓝宝涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap