Method for improving reconstituted tobacco paper-base quality through adding calcium carbonate and reconstituted tobacco paper-base

A technology for reconstituted tobacco leaves and calcium carbonate, which is applied in the fields of tobacco, tobacco preparation, and tobacco treatment. It can solve the problems of lack of stable and feasible technical solutions with clear effects, lack of analysis and research, and unclear impact mechanism, so as to improve surface properties and Effect of internal structure, improved running performance and effectiveness, improved air permeability

Active Publication Date: 2012-10-10
CHINA TOBACCO GUANGDONG IND +1
View PDF4 Cites 44 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Although studies have shown that the addition of calcium carbonate and the use of auxiliary agent guar gum will have a significant impact on the performance of the reconstituted tobacco paper base, but the mechanism of the impact is not clear. Is the compatibility mechanism of the auxiliary agent and calcium carbonate reasonable? Excessive or improper use of tobacco will bring many uncertain factors to the tobacco sheet paper base, so there is...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for improving reconstituted tobacco paper-base quality through adding calcium carbonate and reconstituted tobacco paper-base
  • Method for improving reconstituted tobacco paper-base quality through adding calcium carbonate and reconstituted tobacco paper-base
  • Method for improving reconstituted tobacco paper-base quality through adding calcium carbonate and reconstituted tobacco paper-base

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Example 1 Preparation of reconstituted tobacco leaf paper base by conventional method

[0023] (1) Dipping and extracting tobacco stems and tobacco powder respectively;

[0024] Dipping and extracting tobacco stems and tobacco powder respectively. The conditions for the steeping and extraction of the tobacco stems are that the ratio of solid to liquid is 1:7 (mass ratio), the extraction temperature is 60°C, and the extraction time is 100 minutes (min); the conditions for the steeping and extraction of the tobacco powder are that the ratio of solid to liquid is 1: 10. The extraction temperature is 70°C, and the extraction time is 60 min; the extracts of tobacco stems and tobacco powder obtained after the impregnation treatment are mixed according to a volume ratio of 1:1, and then conventionally evaporated and concentrated to obtain a coating liquid; after the impregnation treatment, the tobacco stems, Tobacco solids are used for refining.

[0025] (2) Refining: the ...

Embodiment 2

[0032] The particle size distribution of embodiment 2 calcium carbonate particles

[0033] Take calcium carbonate powder, add water and be mixed with the calcium carbonate solution that the mass percentage concentration is 0.0016%, carry out particle size analysis, the analysis result of calcium carbonate particle size distribution sees figure 1 .

[0034] attached by figure 1 It can be seen that calcium carbonate for papermaking itself is not a spherical particle, and its diameter does not represent an absolute diameter in the usual sense. Integral curves, where the diameter can only be the statistical mean of all changing values. The particle size value is not unique, it is related to the instrument and statistical method used for measurement. No matter what kind of particle size analyzer (laser or sedimentation) is used, it is impossible to measure the distance between two points connecting the particle surface through the center of gravity, so the measured particle si...

Embodiment 3

[0043] Example 3 Effect of adding different amounts of guar gum on the quality of reconstituted tobacco paper base

[0044] Prepare the reconstituted tobacco leaf paper base according to the steps in Example 1, wherein in step (4), add the tobacco mixed slurry to tap water to prepare a tobacco slurry suspension with a solid content of 0.5 wt.%, disperse evenly, and add to it under low-speed stirring Calcium carbonate aqueous solution (concentration is 20g / L, stir the solution to make it evenly mixed), so that the final mass percentage of the added calcium carbonate in the mixed slurry is 50%. Stir for 30 seconds, add the guar gum suspension, continue to stir for 1 minute, and quickly make a tablet. The other steps are the same as in Example 1. The amount of guar gum added is increased from 0% to 1.5% (based on the final mass percentage of guar gum in the mixed slurry), and a variety of reconstituted tobacco leaf paper bases are prepared, and thin paper is obtained after the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tear indexaaaaaaaaaa
Bulkaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for improving the reconstituted tobacco paper-base quality through adding calcium carbonate and a reconstituted tobacco paper-base, belonging to the technical field of cigarette production. The method for improving the reconstituted tobacco paper-base quality through adding calcium carbonate comprises the steps of soaking and extracting tobacco stems and tobacco powder, grinding, pulping, sheet making, squeezing and drying, wherein in the sheet making step, the calcium carbonate and guar gum which respectively occupies 10-70% and 0.05-0.5% of the mass percent of the tobacco raw pulp are added into the tobacco raw pulp. Researches show that after the calcium carbonate and the guar gum are added according to an appropriate proportion, the tensile index, tear index and air permeability of the produced reconstituted tobacco paper-base are obviously improved, the whole water-absorption performance of the reconstituted tobacco paper-base is also improved, the tar yield, CO content and total particle matter content of the sheet paper-base are obviously decreased, so that the tar and harm reduction function of the reconstituted tobacco is better played, the combination property of the tobacco sheet is effectively improved, and the operation performance and effectiveness of a reconstituted tobacco production line are improved.

Description

technical field [0001] The invention belongs to the technical field of cigarette production, and in particular relates to a method for adding calcium carbonate to improve the quality of a reconstituted tobacco leaf paper base and the reconstituted tobacco leaf paper base. Background technique [0002] The production of reconstituted tobacco leaves by the papermaking method means that the tobacco stems, tobacco powder and some low-grade tobacco leaves in the cigarette production process are first processed into a base sheet (base paper) according to the papermaking method, and the base sheet is coated and dried, and finally made into a close An advanced reconstituted tobacco production process in which thin slices of natural tobacco leaves are applied to cigarette production. A certain amount of fillers are usually added in the production of paper-based tobacco sheets to increase the ash content of the paper base and improve other physical properties, such as liquid absorptio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A24B3/14A24B15/12
Inventor 曾健许光陈克复谢剑平饶国华李军杨飞韩迎迎
Owner CHINA TOBACCO GUANGDONG IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap