A vanadium-precipitating wastewater and acidic technology, applied in chemical instruments and methods, water/sewage multi-stage treatment, water/sludge/sewage treatment, etc., can solve problems such as blocked pipes and washing water outlets

Active Publication Date: 2012-12-26
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF4 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to overcome the deficiency of above-mentioned method, provide a kind of method for recycling acidic vanadium precipitation wastewater, this method has effectively controlled the calcium ion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] 500mL acidic vanadium precipitation wastewater (containing Ca 2+ 0.486g / L, Mn 2+ 8.32g / L, Mg 2+ 1.49g / L), under the condition of stirring, adjust the pH value to 9 with milk of lime, and then carry out solid-liquid separation to obtain gypsum slag and 492mL alkaline solution (containing Ca 2+ 0.772g / L, Mn 2+ 0.75g / L, Mg 2+ 0.51g / L); add 1.70g of ammonium carbonate to the obtained alkaline solution, stir for 10min, let it stand, filter off the decalcification residue, and obtain the supernatant (Ca 2+ 0.144g / L, Mn 2+ 0.08g / L, Mg 2+ 0.46g / L); use sulfuric acid to adjust the pH value of the supernatant to 3.2, and let it stand still, no precipitation is found, and finally return the supernatant to the leaching process for recycling.

Embodiment 2

[0024] 500mL acidic vanadium precipitation wastewater (containing Ca 2+ 0.486g / L, Mn 2+ 8.32g / L, Mg 2+ 1.49g / L), under the condition of stirring, adjust the pH value to 10 with milk of lime, and then carry out solid-liquid separation to obtain gypsum slag and 495mL alkaline solution (containing Ca 2+ 0.847g / L, Mn 2+ 0.38g / L, Mg 2+ 0.34g / L); add 1.20g ammonium bicarbonate to the obtained alkaline solution, stir for 10min, let it stand, filter off the decalcification residue, and obtain the supernatant (Ca 2+ 0.152g / L, Mn 2+ 0.08g / L, Mg 2+ 0.31g / L); use sulfuric acid to adjust the pH value of the supernatant to 4.5, and let it stand still, no precipitation is found, and finally return the supernatant to the leaching process for recycling.

Embodiment 3

[0026] 500mL acidic vanadium precipitation wastewater (containing Ca 2+ 0.486g / L, Mn 2+ 8.32g / L, Mg 2+ 1.49g / L), adjust the pH value to 11 with milk of lime under stirring conditions, and then carry out solid-liquid separation to obtain gypsum slag and 495mL alkaline solution (containing Ca 2+ 0.847g / L, Mn 2+ 0.38g / L, Mg 2+0.34g / L); add 1.00g oxalic acid to the obtained alkaline solution, stir for 10min, let it stand, filter off the decalcification residue, and obtain the supernatant (Ca 2+ 0.092g / L, Mn 2+ 0.37g / L, Mg 2+ 0.30g / L); use sulfuric acid to adjust the pH value of the supernatant to 6, and let it stand still, no precipitation is found, and finally return the supernatant to the leaching process for recycling.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method for recycling acidic vanadium deposit wastewater. The method comprises the following steps: adjusting the acidic vanadium deposit wastewater to be alkaline by lime milk, then carrying out solid-liquid separation to obtain an alkaline solution and a gypsum residue; adding a decalcifying agent into the alkaline solution for decalcifying, then carrying out solid-liquid separation to obtain a supernatant liquor and a decalcified residue; and adjusting the pH of the supernatant liquor to be 3-7 by sulfuric acid, then returning the supernatant liquor to the leaching step for recycling. Due to the adoption of the method for recycling the acidic vanadium deposit wastewater, concentration of calcium ions in the solution returned to the leaching step can be effectively controlled, calcium sulfate deposit is prevented from being formed, a pipeline and a water outlet are prevented from being blocked due to calcium sulfate scale, and the production equipment is guaranteed to run normally.

Description

technical field [0001] The invention relates to a treatment method for vanadium-precipitation wastewater, in particular to a treatment method for recycling acidic vanadium-precipitation wastewater. Background technique [0002] At present, there are two main treatment methods for the vanadium precipitation wastewater generated by the production of vanadium oxide from vanadium slag in industry: [0003] One is based on vanadium slag sodium roasting-water leaching vanadium extraction as the main process. The wastewater produced by this process is generally used to reduce vanadium-chromium-neutralization, filtration-evaporation and concentration. This technology is relatively mature but the cost of wastewater treatment is high; [0004] The other is the main process of vanadium slag calcification roasting-acid leaching vanadium extraction. The vanadium precipitation wastewater produced by this process is currently neutralized with lime, filtered-adjusting pH, and then returned ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C02F9/04
Inventor 付自碧何文艺申彪卢晓林高官金彭毅张林彭一村
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap