High performance environment protection ABS/PE composite plastic master batch and preparation method thereof

A high-performance, environmentally friendly technology, applied in the field of ABS/PE composite plastic masterbatch and its preparation

Inactive Publication Date: 2013-02-20
DONGGUAN XINHENG PLASTIC PROD
View PDF1 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Because traditional single plastic materials such as ABS, PE, PC, PVC and other plastic materials are difficult to meet the high strength, high hardness, wear resistance, compression and bending resistance of plastic components used in aerospace industry, shipbuilding industry and automobile industry , heat resistance, flame retardancy, high toughness, acid and alkali resistance, stability, environmental protection and other performance requirements, so the use of composite rubber came into being, but the existing technology has not yet had a high strength, high hardness, wear resistance The formulation and preparation method of good and stable ABS / PE composite plastic masterbatch to meet the needs of plastic parts used in aerospace industry and shipbuilding industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High performance environment protection ABS/PE composite plastic master batch and preparation method thereof
  • High performance environment protection ABS/PE composite plastic master batch and preparation method thereof
  • High performance environment protection ABS/PE composite plastic master batch and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] ABS (acrylonitrile, butadiene, styrene copolymer): 52%

[0022] Polyethylene PE: 14%

[0023] Modifier: 7%

[0024] Nanoscale silica 18%

[0025] Silane coupling agent: 1.5%

[0026] Stearic acid: 1%

[0027] Calcium Stearate 1.5%

[0028] Anti-aging agent 3%

[0029] PE wax: 2%.

[0030] The plastic part made of the functional masterbatch obtained by the formula according to the production method of the present invention can be detected by the detection mechanism, and its index can reach:

[0031]

[0032]

Embodiment 2

[0034] ABS (acrylonitrile, butadiene, styrene copolymer): 62%

[0035] Polyethylene PE: 10%

[0036] Modifier: 8%

[0037] Nanoscale silica 15%

[0038] Silane coupling agent: 1%

[0039] Stearic acid: 1%

[0040] Anti-aging agent 2%

[0041] PE wax: 1%.

[0042] The functional masterbatch obtained by the formula according to the production method of the present invention is detected by a detection mechanism, and its relevant indicators can reach:

[0043]

Embodiment 3

[0045] ABS (copolymer of acrylonitrile, butadiene, styrene): 61%

[0046] Polyethylene PE: 12%

[0047] Modifier: 6%

[0048] Nanoscale silica 14%

[0049] Silane coupling agent: 1%

[0050] Stearic acid: 1%

[0051] Zinc Stearate 1.5%

[0052] Calcium Stearate 0.5%

[0053] Anti-aging agent 2%

[0054] PE wax: 1%.

[0055] The functional masterbatch obtained by the formula according to the production method of the present invention is detected by a detection mechanism, and its relevant indicators can reach:

[0056]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to an ABS / PE composite plastic master batch and a preparation method thereof, particularly to an ABS / PE composite plastic master batch with characteristics of high strength, high hardness, good wear resistance and strong stability, and a preparation method thereof. The ABS / PE composite plastic master batch comprises the following components: ABS (an acrylonitrile-butadiene-styrene copolymer), polyethylene PE, a modifier, nano-scale silica, a silane coupling agent, stearic acid and PE wax. According to the present invention, high strength, high hardness, wear resistance and stability of the ABS / PE composite plastic master batch produced through the technical scheme can meet high requirements, and the ABS / PE composite plastic master batch can meet quality requirements of plastic parts for aerospace industry and ship industry.

Description

technical field [0001] The invention relates to an ABS / PE composite plastic master batch and a preparation method thereof, in particular to an ABS / PE composite plastic master batch with high strength, high hardness, good wear resistance and strong stability and a preparation method thereof. Background technique [0002] Because traditional single plastic materials such as ABS, PE, PC, PVC and other plastic materials are difficult to meet the high strength, high hardness, wear resistance, compression and bending resistance of plastic components used in aerospace industry, shipbuilding industry and automobile industry , heat resistance, flame retardancy, high toughness, acid and alkali resistance, stability, environmental protection and other performance requirements, so the use of composite rubber came into being, but the existing technology has not yet had a high strength, high hardness, wear resistance The formulation and preparation method of the ABS / PE composite plastic m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L23/06C08K13/02C08K3/36C08K5/09C08K5/098C08J3/22B29B9/06
Inventor 彭海涛俞家荣张亚兵曹兴益
Owner DONGGUAN XINHENG PLASTIC PROD