Non-primer coating method for self-adhesive polyvinylidene chloride emulsion and coating system for implementing non-primer coating method

A technology of polyvinylidene chloride and coating method, which is applied in the field of coating system, can solve problems such as film shrinkage deformation, adhesion, tension and film difficulty, and achieve the effect of good uniformity and improved adhesion

Active Publication Date: 2013-04-03
HAINAN SHINER IND
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the self-adhesive PVDC emulsion has a certain viscosity, it is easy to appear sticky rollers or adhesion between film coating surfaces during the coating process, which will affect the appearance, quality and other physical and mechanical properties of the coating film such as barrier properti

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-primer coating method for self-adhesive polyvinylidene chloride emulsion and coating system for implementing non-primer coating method

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0022] Example 1:

[0023] 1. Unwinding process: Under a constant unwinding tension of 15N, the BOPP reel-shaped film with a thickness of 19 μm is flatly unwound into a continuous and stable operation;

[0024] 2. Corona treatment process: the corona treatment power is set to 6.0kW, and the corona value of the base film after treatment reaches 41dyn / cm;

[0025] 3. Top coating process: The corona-treated film enters the top coating process, adopts reverse gravure coating, and through the cooperation of the coating roller and the scraper, the PVDC emulsion of the top coating is transferred from the trough to the surface of the film through the coating roller. The coating process is transferred to the surface of the film through the coating roller and the coating is controlled at 2.5g / m 2 , the coating thickness is 2 μm, and the tension of the coating film is controlled at 80N; wherein wax emulsion and silicon dioxide anti-adhesive agent are added to the oxygen-resistant PVDC e...

Example Embodiment

[0028] Example 2:

[0029] 1. Unwinding process: Under a constant unwinding tension of 30N, the BOPET reel-shaped film with a thickness of 12 μm is flatly unrolled into a continuous and stable operation;

[0030] 2. Corona treatment process: the corona treatment power is set to 6kW, and the corona value of the treated base film reaches 41dyn / cm;

[0031]3. Top coating process: the coating film after primer coating enters the top coating process, adopts reverse gravure coating, and through the cooperation of coating roller and scraper, the top coating PVDC emulsion is transferred from the trough to the film through the coating roller The surface, where the coating process is transferred to the film surface by the coating roller, the coating is controlled at 3.0g / m 2 , the thickness of the coating is 2 μm, and the tension of the coating film is controlled at 80N; wherein wax emulsion and silicon dioxide anti-sticking agent are added to the oxygen-resistant PVDC emulsion of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Widthaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a non-primer coating method for a self-adhesive polyvinylidene chloride (PVDC) emulsion and a coating system for implementing the method. Kiss type coating is adopted for top coating, and an appropriate quantity of wax emulsion and silicon dioxide anti-sticking agent are added into the top coating self-adhesive PVDC emulsion in a top coating process, so that an obtained coating film has the characteristics of high resistance and high heat-sealing property and can compound with a carton through an UV (Ultraviolet) adhesive; the surface of the coating film is smooth, so that the film can easily move on equipment without greater tension; and the film is not subjected to remarkable contraction deformation after being heated through a baking oven, so the product performance is not influenced.

Description

technical field [0001] The invention relates to a primerless coating method of self-adhesive polyvinylidene chloride emulsion and a coating system for implementing the method. Background technique [0002] In the plastic coating industry, before coating functional coatings, it is necessary to apply a layer of primer to enhance the adhesion between the coating and the plastic substrate film. When producing barrier coating films, PVDC coatings with very good oxygen barrier properties on the market are selected, and the primer layer must be used to make the PVDC coatings firmly adhere to the plastic film. [0003] Patent CN03263561 relates to the reverse (reverse) gravure roller kiss coating device of the coating machine, which is composed of a support plate, a transmission gear, a pressure roller, a cooling roller, a coating roller, and a regulating roller. Among them, the pressure roller, the cooling roller, the coating The two ends of the roller are installed on the support...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B05D7/04B05D3/14B05C9/10B05C13/02
Inventor 杨强符师林鹏
Owner HAINAN SHINER IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap