Acidizing fluid thickener synthetic process based on control of reaction time

A technology of acid thickener and reaction time, which is applied in the direction of coating, etc., can solve the problems of low industrial concentration and lack of economies of scale, and achieve the effects of low synthesis cost, short synthesis time and simple operation

Inactive Publication Date: 2013-04-17
何阳
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0019] Studies have shown that in my country's thickener enterprises, the industry concentration has always been low, and the lack of economies of scale

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acidizing fluid thickener synthetic process based on control of reaction time

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0045] The acid liquid thickener synthesis technique based on the control reaction time that the present invention relates to, its concrete steps are as follows:

[0046] (a) at first, carry out the purification of reaction monomer;

[0047] (b) preparation of initiator solution;

[0048] (c) according to proportioning, take the 2-methyl-2-acrylamidopropanesulfonic acid solid of certain quality and be dissolved in distilled water;

[0049] (d) adding a certain amount of acrylic acid and dimethyl diallyl ammonium chloride to the solution of step (c), and fully dissolving the three reaction monomers;

[0050] (e) After mixing evenly, adjust the pH value of the solution;

[0051] (f) then move the reaction mixed solution into a constant temperature reaction vessel, exhaust oxygen and stir;

[0052] (g) adding the initiator solution dropwise;

[0053] (h) Finally, under the protection of an inert gas, the reaction system is heated to carry out polymerization reaction for 4-5 h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an acidizing fluid thickener synthetic process based on control of reaction time. The process comprises the following steps: (a) purifying a reaction monomer; (b) preparing an initiator liquor; (c) weighing a certain amount of 2-methyl-2-acrylamidyl propanesulfonic acid solid and dissolving the solid in distilled water; (d) adding a certain amount of acrylic acid and dimethyl diallyl ammonium chloride into the liquor in the step (c), and dissolving adequately; (e) adjusting the pH value of the liquor; (f) shifting the mixed liquid for reaction to a reaction container, deoxygenating and stirring; (g) adding the initiator liquor; and (h) heating the reaction system for polymerization reaction for 4-5 hours to obtain a target product. According to the process provided by the invention, the acidizing fluid thickener can be successfully synthesized, and the synthetic process is simple in step, simple to operate, short in synthetic time, high in synthetic efficiency and low in synthetic cost. Performance parameters of the synthetic product are superior to those of current acidizing fluid thickener, and the conversion rate and intrinsic viscosity are improved by controlling the polymerization reaction time.

Description

technical field [0001] The invention relates to a synthesis process of acid liquid thickener based on controlling reaction time. Background technique [0002] Thickener is a kind of rheological additive, which can not only thicken the coating and prevent sagging during construction, but also endow the coating with excellent mechanical properties and storage stability. It is a very important class of additives for water-based paints with low viscosity. [0003] At present, there are many kinds of thickeners available in the market, mainly including inorganic thickeners, celluloses, polyacrylates and associative polyurethane thickeners. Cellulosic thickeners have a long history of use and there are many varieties, including methyl cellulose, carboxymethyl cellulose, hydroxyethyl cellulose, hydroxypropyl methyl cellulose, etc., which used to be the mainstream of thickeners. The most commonly used of these is hydroxyethyl cellulose. Polyacrylate thickeners can basically be di...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F226/02C08F220/06C08F220/58C08F2/00C09D7/12
Inventor 何阳
Owner 何阳
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap