Urushiol-cardanol bio-based resin and synthesis method thereof

A technology of bio-based resin and cardanol resin, which is applied in the direction of coating, can solve the problems of limited development, high price, low output, etc., and achieve the effect of mechanized operation and excellent comprehensive anti-corrosion performance

Inactive Publication Date: 2013-04-17
中华全国供销合作总社西安生漆涂料研究所
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Raw lacquer is a special product in my country, with a history of 8,000 years of use. Raw lacquer film has excellent performance, bu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The urushiol-cardanol bio-based resin weight percent formula of the present embodiment is as follows:

[0025] component name

[0026] According to the above mass ratio formula, heat urushiol, cardanol and xylene to 60°C, add formaldehyde and ammonia water to react for 2.5 hours, heat up and dehydrate to obtain urushiol-cardanol resin condensation polymer, and then add cobalt naphthenate to prepare become.

Embodiment 2

[0028] Urushiol-cardanol bio-based resin weight percent formula of the present invention is as follows:

[0029] component name

[0030] According to the above mass ratio formula, heat urushiol, cardanol and xylene to 60°C, add furfural and sodium hydroxide to react for 2.5 hours, heat up and dehydrate to obtain urushiol-cardanol resin condensation polymer, and then add manganese dioxide to prepare Serve.

Embodiment 3

[0032] The urushiol-cardanol bio-based resin weight percent formula of the present embodiment is as follows:

[0033] component name

[0034] According to the above mass ratio formula, heat cardanol and xylene to 70°C, add formaldehyde and potassium hydroxide to react for 2 hours to obtain the cardanol reactant; then add urushiol, react at 70°C for 2 hours, then heat up and dehydrate to obtain Urushiol-cardanol resin polycondensate, then add lead naphthenate to prepare.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses urushiol-cardanol bio-based resin and a synthesis method thereof. The prepared urushiol-cardanol bio-based resin comprises the following raw materials in mass percentage: 20-40% of urushiol, 5-20% of cardanol, 4-8% of aldehyde compound, 0.5-3% of catalyst, 40-60% of diluting agent, 0-20% of epoxy resin and 0.1-5% of curing agent, with the total percentage of 100%. The urushiol-cardanol bio-based resin solves the problems that a raw lacquer product is insufficient in supply and high in price, can be sprayed, coated and brushed, has a low requirement on a construction technology, can realize mechanized operation, does not require specific temperature and humidity conditions and can be dried under a natural condition, and a lacquer film remains the excellent performance of the urushiol resin; and the urushiol-cardanol bio-based resin has excellent comprehensive anti-corrosion performance and is an excellent intermediate of the urushiol resin.

Description

technical field [0001] The invention relates to a resin and the technical field of its preparation, in particular to an urushiol-cardanol bio-based resin and a synthesis method thereof. The urushiol-cardanol bio-based resin is an intermediate and is particularly suitable for preparing heavy-duty anti-corrosion resins Coatings and other special functional coating resins. Background technique [0002] Raw lacquer is a special product in my country, with a history of 8,000 years of use. Raw lacquer film has excellent performance, but its unique source method leads to its development mode of low output and high price, which limits its development in the industrial field. In order to expand the application of raw lacquer in the industrial field and solve the problem of high supply and price, a new type of urushiol-cardanol was synthesized by copolymerizing cheap and easy-to-obtain biomass materials such as cardanol and urushiol through the application of combinatorial chemical re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G8/24C08G8/06C09D161/12C09D161/08
Inventor 贺娜张飞龙
Owner 中华全国供销合作总社西安生漆涂料研究所
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products