Hydrolysis-resistant nylon composite material and preparation method thereof

A nylon composite material, hydrolysis-resistant technology, applied in the field of polymer materials, can solve the problems of difficult hydrolysis and nylon difficulty, and achieve the effect of improving heat resistance temperature, hydrolysis resistance and superior mechanical strength

Inactive Publication Date: 2013-04-17
ANHUI KEJU NEW MATERIALS
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This process also has certain conditions for the selection of materials, which must not be easily hydrolyzed, so it is very difficult for nylon

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrolysis-resistant nylon composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] 69.3% of nylon 66 resin; 0.1% of heat stabilizer; 0.1% of coupling agent; 0.2% of antioxidant; Good raw materials are placed in the twin-screw extruder and fed through the main feeding port; 30% of the hydrolysis-resistant glass fiber is fed through the measuring feeding port, and extruded through the twin-screw extruder with a melting temperature of 200-300 ° C to produce grain.

[0045] The temperature of each section is: 200°C in the first zone, 280°C in the second zone, 285°C in the third zone, 200°C in the fourth zone, 200°C in the fifth zone, and the residence time is 90 seconds.

Embodiment 2

[0047] Mix nylon 66 resin 69.2% by weight; heat stabilizer 0.2%; coupling agent 0.1%; antioxidant 0.2%; It is placed in a twin-screw extruder and fed through the main feeding port; 30% of the hydrolysis-resistant glass fiber is fed through the measuring feeding port, extruded through a twin-screw extruder with a melting temperature of 200-300 ° C, and pelletized.

[0048] The temperature of each section is: 200°C in the first zone, 280°C in the second zone, 285°C in the third zone, 200°C in the fourth zone, 200°C in the fifth zone, and the residence time is 90 seconds.

Embodiment 3

[0050] Mix nylon 66 resin 69.1% by weight; heat stabilizer 0.3%; coupling agent 0.1%; antioxidant 0.2%; It is placed in a twin-screw extruder and fed through the main feeding port; 30% of the hydrolysis-resistant glass fiber is fed through the measuring feeding port, extruded through a twin-screw extruder with a melting temperature of 200-300 ° C, and pelletized.

[0051] The temperature of each section is: 200°C in the first zone, 280°C in the second zone, 285°C in the third zone, 200°C in the fourth zone, 200°C in the fifth zone, and the residence time is 90 seconds.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses a hydrolysis-resistant nylon composite material and a preparation method thereof. The material comprises the following components in percentage by weight: 45-75 percent of nylon resin, 0.1-1 percent of hydrolysis resisting agent, 0.1-1 percent of heat stabilizer, 0.1-1 percent of antioxidant, 0.1-1 percent of coupling agent, 0.1-5 percent of lubricant and 20-50 percent of hydrolysis-resistant glass fiber. The hydrolysis-resistant nylon composite material solves the difficulties of the water assistance technique, improves the heat resisting temperature and the hydrolysis resistance of nylon, and maintains higher mechanical performance at the same time of obtaining high-temperature resistance and hydrolysis resistance.

Description

[technical field] [0001] The invention relates to the field of polymer materials, in particular to a hydrolysis-resistant nylon composite material and a preparation method thereof. [Background technique] [0002] As the most important variety of engineering plastics, nylon has strong vitality, mainly because it achieves high performance after modification, and secondly, the automobile, electrical appliance, communication, electronics, machinery and other industries themselves have more and more high-performance requirements for products. strong. The rapid development of related industries has promoted the process of high-performance engineering plastics. With the development of injection molding technology, a new injection molding process, water-assisted process, has been proposed on many occasions. This process has brought great benefits to customers. Benefits, it can greatly shorten the injection molding time which also reduces the cost accordingly. This process also has...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/00C08L77/06C08K13/04C08K7/14B29B9/06B29C47/92B29C48/92
CPCB29C48/04B29C48/40B29C48/875B29C48/92B29C2948/92704B29C2948/92895
Inventor 徐东徐永罗彧斌
Owner ANHUI KEJU NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap