Method for obtaining shrinkage strain ratio in continuous change of titanium alloy tube

A shrinkage strain, titanium alloy tube technology, applied in the direction of applying stable tension/pressure to test material strength, etc., can solve problems such as constant shrinkage strain ratio

Active Publication Date: 2013-05-22
NORTHWESTERN POLYTECHNICAL UNIV
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the deficiency in the prior art that the constant shrinkage strain ratio of the titanium alloy pipe can only be obtained under the condition of small plastic deformation, the present invention proposes a method for obtaining the continuously changing shrinkage strain ratio of the titanium alloy pipe

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for obtaining shrinkage strain ratio in continuous change of titanium alloy tube
  • Method for obtaining shrinkage strain ratio in continuous change of titanium alloy tube
  • Method for obtaining shrinkage strain ratio in continuous change of titanium alloy tube

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] This embodiment is a method for obtaining a continuously variable shrinkage strain ratio of the titanium alloy tube, and the range of the shrinkage strain ratio is from initial plastic deformation to plastic deformation of 0.174.

[0037] Under the concrete steps of this embodiment:

[0038] Step 1, making a tube sample. Sampling according to GB / T228-2002 tensile standard for pipes with stopper rods. The length of the tube sample is 130 mm, the wall thickness is 0.5 mm, the outer diameter is 6 mm, and the inner diameter is 5 mm. The tube sample is shown in Figure l.

[0039] Two gauge points are determined on the tube sample. When determining the two gauge points, take the center of the length direction of the pipe sample as the reference, and take 0.5mm to both sides of the center as the gauge point A and the gauge point B respectively, and the gauge length Point A and gauge point B are marked with dashed lines. The gauge length between the gauge point A and the g...

Embodiment 2

[0064] This embodiment is a method for obtaining a continuously variable shrinkage strain ratio of the titanium alloy tube, and the range of the shrinkage strain ratio is from initial plastic deformation to plastic deformation of 0.175.

[0065] The concrete steps of this embodiment are as follows:

[0066] Step 1, making a tube sample. Sampling according to GB / T228-2002 tensile standard for pipes with stopper rods. The length of the tube specimen was 155 mm, the wall thickness was 0.6 mm, the outer diameter was 8 mm, and the inner diameter was 6.8 mm. Tube samples such as figure 1 shown.

[0067] Two gauge points are determined on the tube sample. When determining the two gauge points, take the center of the length direction of the pipe sample as the reference, and take 0.5mm to both sides of the center as the gauge point A and the gauge point B respectively, and the gauge length Point A and gauge point B are marked with dashed lines. The gauge length between the gauge...

Embodiment 3

[0093] This embodiment is a method for obtaining a continuously variable shrinkage strain ratio of the titanium alloy tube, and the range of the shrinkage strain ratio is from initial plastic deformation to plastic deformation of 0.180.

[0094] The concrete steps of this embodiment are as follows:

[0095] Step 1, making a tube sample. Sampling according to GB / T228-2002 tensile standard for pipes with stopper rods. The length of the tube sample is l80mm, the wall thickness is 0.9mm, the outer diameter is 12mm, and the inner diameter is 10.2mm. The tube sample is shown in Figure l.

[0096] Two gauge points are determined on the tube sample. When determining the two gauge points, take the center of the length direction of the pipe sample as the reference, and take 0.5mm to both sides of the center as the gauge point A and the gauge point B respectively, and the gauge length Point A and gauge point B are marked with dashed lines. The gauge length between the gauge point A ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for obtaining a shrinkage strain ratio in continuous change of a titanium alloy tube. A tube test sample is machined according to the size of a metal tube test sample in GB/T228-2002. A tensile test is carried out on a tensile test machine in a set tensile speed. The changes of the circumferential strain and the axial strain of the tube test sample in the tensile process are both precisely obtained through a CCD (Charge Coupled Device) camera. The circumferential strain and axial strain values of the tube test sample are precisely measured by using the camera in the one-way tensile process, and are subjected to elastic corrosion so as to accurately obtain the shrinkage stain ratio of the titanium alloy tube under a large plasticity deformation condition in the tensile process through formulas; and moreover the shrinkage strain ratio of the titanium alloy tube is decreased, that is, in the primary deformation period of the tube test sample, the shrinkage stain ratio is decreased dramatically, however, in later deformation, the decrease tendency of the shrinkage stain ratio is gradually reduced, and the decrease tendency of the shrinkage stain ratio in later deformation is gradually stable.

Description

technical field [0001] The invention belongs to the field of metal plastic forming processing, and is used for main performance detection during plastic forming processing of titanium alloy pipes, in particular to a method for continuously measuring the shrinkage strain ratio change of titanium alloy pipes under large plastic deformation conditions. Background technique [0002] In high-tech fields such as aviation, aerospace, energy, etc., titanium alloy elbow fittings are an indispensable and widely used type of component. The shrinkage strain ratio is one of the important indicators to measure the deformation performance of metal pipes. Its size is usually expressed by the ratio of the strain in the width direction and the strain in the thickness direction of the sample during uniaxial tension. The shrinkage strain ratio can be expressed as CSR. In the existing research, the shrinkage strain ratio of titanium alloy pipes is mainly obtained according to the aviation standa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G01N3/08
Inventor 詹梅皇涛谭金强杨合
Owner NORTHWESTERN POLYTECHNICAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap