Fingerprint-resistant metal powder coating with chromium plating effect and preparation method thereof

A metal powder, anti-fingerprint technology, applied in powder coating, epoxy resin coating, coating, etc., can solve the problem of metal powder coating being easy to rub off and unstable

Active Publication Date: 2013-06-05
NINGBO SOUTH SEA CHEM
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] For this reason, the technical problem to be solved by the present invention is the problem that the metal powder coating is easy to rub off and unstable in the prior art, and then a kind of metal powder coating with chrome plating effect that is wear-resistant and not easy to rub off is provided;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fingerprint-resistant metal powder coating with chromium plating effect and preparation method thereof
  • Fingerprint-resistant metal powder coating with chromium plating effect and preparation method thereof
  • Fingerprint-resistant metal powder coating with chromium plating effect and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0069] The anti-fingerprint metal powder coating with chrome plating effect described in this embodiment is obtained by dry mixing an epoxy resin particle system and a fluorocarbon resin particle system at a ratio of parts by weight of 1:1.

[0070] Described epoxy resin particle system is made up of the component of following parts by weight:

[0071] Bisphenol A type epoxy resin E-12 and dicyandiamide curing agent A total of 70 copies of 100S;

[0072] Leaving aluminum powder Eckart pc 1006 parts with a particle size of 10-12 μm;

[0073] 13.2 parts of pigments and fillers, including pigments and fillers. The fillers are selected from barium sulfate such as W-44HB, and the pigments are selected from titanium dioxide CR826. The pigments and fillers can be added and set according to the needs of those skilled in the art. This implementation The addition ratio of the pigment and the filler described in the example is 1:1;

[0074] 0.8 part of auxiliary agent A, said auxilia...

Embodiment 2

[0088] The anti-fingerprint metal powder coating with chrome plating effect described in this embodiment is obtained by dry mixing an epoxy resin particle system and a fluorocarbon resin particle system at a ratio of parts by weight of 7:3.

[0089] Described epoxy resin particle system is made up of the component of following parts by weight:

[0090] A total of 35 parts of bisphenol A epoxy resin NPES-903 and substituted dicyandiamide curing agent (CASAMID710 from THOMAS S WAN);

[0091] 3 parts of leafing aluminum powder Eckart pc200 with a particle size of 6-8 μm;

[0092] 2 parts of auxiliary agent A, said auxiliary agent A includes corner coverage modifier 0.5 parts of Mowital, 0.5 parts of curing accelerator BASF2-MI, wetting and dispersing agent 0.5 part of ST, 0.5 part of flow aid alumina C;

[0093] 30 parts of pigments and fillers, including pigments and fillers, the fillers are selected from aluminum hydroxide such as A40, the pigment is selected from carbon...

Embodiment 3

[0105] The anti-fingerprint metal powder coating with chrome plating effect described in this embodiment is obtained by dry mixing an epoxy resin particle system and a fluorocarbon resin particle system at a ratio of parts by weight of 3:7.

[0106] Described epoxy resin particle system is made up of the component of following parts by weight:

[0107] Novolac epoxy resin (KUKDO YDPN series) and phenolic hydroxyl resin curing agent (KUKD OKD-420, a total of 85 parts;

[0108] 8 parts of leafing aluminum powder Eckart pc100 with a particle size of 4-6 μm;

[0109] 3 parts of pigments and fillers, including pigments and fillers, the fillers are selected from aluminum hydroxide such as A40, the pigment is selected from carbon black 330R, wherein the pigment and filler can be added and set according to the needs of those skilled in the art for the product, and the addition ratio of the pigment and the filler in this embodiment is 1:2;

[0110] 0.5 part of auxiliary agent A, sai...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of metal powder coating, and particularly relates to fingerprint-resistant metal powder coating with a chromium plating effect. The fingerprint-resistant metal powder coating with the chromium plating effect comprises an epoxy resin particle system containing epoxy resin, adaptive curing agent A and chromium plating effect pigment, and a fluorocarbon resin particle system containing fluorocarbon resin and adaptive curing agent B, wherein the ratio of parts by weight between the epoxy resin particle system and the fluorocarbon resin particle system is 7-3 / 3-7. The fingerprint-resistant metal powder coating with the chromium plating effect forms an epoxy resin layer and a fluorocarbon resin layer which are separated in the solidification process, floating type aluminum powder is bonded regularly by means of a bonding process to form the chromium plating effect, the fluorocarbon resin layer at the outer layer has the functions of a transparent protective film, and the epoxy resin layer at the inner layer forms a bonding layer and is favorable for bonding with a layer to be coated.

Description

technical field [0001] The invention belongs to the field of metal powder coatings, in particular to a metal powder coating with chrome plating effect and anti-fingerprint performance and a preparation method thereof. Background technique [0002] With the development of the economy and the improvement of people's living standards, people's requirements for comfort and aesthetics in their own living areas are also getting higher and higher, which makes the application of metal powder coatings in the entire decorative coating more and more widely. At present, it is the mainstream product of powder for art decoration. Metal powder coatings refer to various powder coatings containing metal pigments (such as: copper gold powder, silver aluminum powder, etc.). Because metal powder coatings can show a bright and luxurious decorative effect, they are very suitable for spraying indoor and outdoor objects such as furniture, accessories and cars. Metal powder coatings are widely use...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/00C09D163/02C09D163/04C09D127/12C09D127/18C09D5/03
Inventor 张云伟
Owner NINGBO SOUTH SEA CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com