Heavy anticorrosion super weatherproof powder coating as well as preparation method and application thereof

A powder coating and super weather-resistant technology, which is applied in powder coatings, anti-corrosion coatings, epoxy resin coatings, etc., can solve the impact of weather resistance, lack of anti-corrosion performance of architectural coatings, and can not solve the problems of anti-corrosion of epoxy resin powder coating outdoor materials, etc. , to achieve the effect of protection and anti-aging

Active Publication Date: 2015-06-03
NINGBO SOUTH SEA CHEM
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since the coating is mainly used for pipeline anticorrosion, there is no problem that the epoxy resin coating cannot be exposed to light, and it can be predicted based on the prior art and the properties of the epoxy resin that if the coating is used for building anticorrosion coating When layering, the coating on the outer surface contains both epoxy resin and fluorocarbon resin. The weather resistance of the coating will be affected by the presence of epoxy resin, so it still cannot solve the problem that powder coatings containing epoxy resin are not suitable. The problem of anti-corrosion applied to outdoor materials, and the lack of anti-corrosion performance of architectural coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heavy anticorrosion super weatherproof powder coating as well as preparation method and application thereof
  • Heavy anticorrosion super weatherproof powder coating as well as preparation method and application thereof
  • Heavy anticorrosion super weatherproof powder coating as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] The heavy-duty anti-corrosion and super-weather-resistant powder coating described in this embodiment is obtained by dry mixing the epoxy resin particle system and the fluorocarbon resin particle system with a ratio of parts by weight of 6:4.

[0058] Described epoxy resin particle system is made up of the component of following parts by weight:

[0059] Bisphenol A type epoxy resin (E-12) and curing agent A dicyandiamide A total of 80 copies;

[0060] Anti-corrosion zinc powder (Umicore FH800) is 70 parts;

[0061] 70 parts of pigment and filler A, said pigment and filler A includes pigment and filler, said filler selects barium sulfate such as W-44HB for use, and said pigment selects titanium dioxide CR826 for use, and wherein said pigment and filler can be according to those skilled in the art to the demand of product Adding settings, the addition ratio of the pigment and the filler in the present embodiment is 1:1;

[0062] 2 parts of auxiliary agent A, said aux...

Embodiment 2

[0073] The heavy-duty anti-corrosion and super-weather-resistant powder coating described in this embodiment is obtained by dry mixing the epoxy resin particle system and the fluorocarbon resin particle system with a ratio of parts by weight of 1:1.

[0074] Described epoxy resin particle system is made up of the component of following parts by weight:

[0075] Novolac epoxy resin (KUKDO YDPN series) and curing agent A hydrazide (ADH) total 60 parts;

[0076] Anti-corrosion zinc powder (Umicore FH800) is 40 parts;

[0077] 20 parts of pigment and filler A, described pigment and filler A comprises pigment and filler, and described filler selects aluminum hydroxide such as The pigment is selected from carbon black 330R, wherein the pigment and filler can be added and set according to the needs of those skilled in the art for the product, and the addition ratio of the pigment and the filler in this embodiment is 1:2;

[0078] 1 part of auxiliary agent A, said auxiliary agent A...

Embodiment 3

[0089] The heavy-duty anti-corrosion and super-weather-resistant powder coating described in this embodiment is obtained by dry mixing the epoxy resin particle system and the fluorocarbon resin particle system with a ratio of parts by weight of 4:6.

[0090] Described epoxy resin particle system is made up of the component of following parts by weight:

[0091] Novolac epoxy resin (KUKDO YDPN series) and curing agent A-terminated carboxyl polyester P5980) a total of 30 copies;

[0092] 60 parts of pigment and filler A, said pigment and filler A includes pigment and filler, said filler selects nepheline for use such as minex-10, and said pigment selects iron red for use Wherein the pigment and the filler can be added and set according to the needs of those skilled in the art for the product, and the addition ratio of the pigment and the filler in this embodiment is 3:2;

[0093] 0.5 part of auxiliary agent A, said auxiliary agent A includes corner coverage modifier Curing...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a heavy anticorrosion super weatherproof powder coating. The heavy anticorrosion super weatherproof powder coating comprises the following components of: an epoxy resin particle system containing epoxy resin and an adaptive curing agent A and a fluorocarbon resin particle system containing fluorocarbon resin and an adaptive curing agent B, wherein the weight part ratio of the epoxy resin particle system to the fluorocarbon resin particle system is (6-4):(4-6). The heavy anticorrosion super weatherproof powder coating provided by the invention has excellent weatherproof and anticorrosion properties and also can realize automatic stratification after once coating is carried out, and construction is simple.

Description

technical field [0001] The invention belongs to the field of powder coatings, and in particular relates to a heavy-duty anti-corrosion super-weather-resistant powder coating and a preparation method and application thereof. Background technique [0002] Heavy-duty anti-corrosion coating is a kind of coating that can be used effectively for a long time in a severe corrosive environment. In order to achieve the purpose of heavy-duty anti-corrosion, on the one hand, it is necessary to thicken the coating, on the other hand, the selection of coating resins and additives, the substrate The requirements for surface treatment, coating construction and maintenance are also very strict. At present, most of the coatings used in heavy-duty anti-corrosion are liquid coatings. However, liquid coatings contain a large amount of organic solvents (most of them contain more than 50% of solvents), and they must be completely volatilized in the coating process before they can form a film. This...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D127/12C09D163/00C09D163/02C09D163/04C09D7/12C09D5/03C09D5/08
Inventor 张云伟
Owner NINGBO SOUTH SEA CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com