Method for preparing honeycomb enhanced phenolic foam composite materials

A composite material and phenolic foam technology, which is applied in the field of composite material preparation, can solve problems such as waterproof and poor flame retardancy, and achieve the effects of increasing heat insulation, simple operation process, and reducing costs

Inactive Publication Date: 2013-07-17
ARAMICORE COMPOSITE
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing composite materials are obtained by impregnating honeycombs with phenolic foam foaming materials and then heating and curing them separately. The composite materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing honeycomb enhanced phenolic foam composite materials
  • Method for preparing honeycomb enhanced phenolic foam composite materials
  • Method for preparing honeycomb enhanced phenolic foam composite materials

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0028] Example 1:

[0029] A method for preparing honeycomb reinforced phenolic foam composite material includes the following steps:

[0030] (1) Pour the phenolic resin foaming composition into the mold 1 so that the phenolic resin foaming composition maintains the same level of liquid level in the mold 1. Such as Figure 3-4 As shown, the mold 1 is in the shape of an open box with a mold cover 2 that fits with the open end of the mold 1. The open end of the mold 1 is provided with an outward flange 3, and corresponding positions of the flange 3 and the mold cover 2 are provided with a pin hole 4 for connecting and fixing the mold 1 and the mold cover 2.

[0031] (2) Will be as figure 2 The illustrated honeycomb is placed vertically into the mold 1 and placed into the phenolic resin foaming composition, so that the amount of the phenolic resin foaming composition is the same in each cell of the honeycomb.

[0032] Specifically, the honeycomb is an aramid paper honeycomb, the cell...

Example Embodiment

[0036] Example 2:

[0037] A preparation method of honeycomb reinforced phenolic foam composite material, which is different from Example 1 in:

[0038] In step (1), the bottom surface of the mold 1 is placed on a horizontal surface, and then the phenolic resin foaming composition is poured into the mold 1, so that the phenolic resin foaming composition can be easily maintained at the same level in the mold 1.

[0039] In step (2), the specification of the honeycomb is 2600*1300*20mm of NH-3.67-40.

Example Embodiment

[0040] Example 3:

[0041] A preparation method of honeycomb reinforced phenolic foam composite material, which is different from Example 2 in:

[0042] In step (2), the size of the honeycomb is 4.5-45 1000*500*20mm, and the honeycomb is a glass fiber honeycomb.

[0043] It should be noted that in Examples 1-3, the phenolic resin foaming composition is prepared from the following parts by weight of raw materials using a common method in this industry: 100 parts of phenolic resin, 0.05-1 part of emulsifier, and curing agent 0.05-1 part, 5-20 parts foaming agent. Phenolic resin, emulsifier, curing agent, foaming agent can be selected from the corresponding raw materials commonly used in the industry. Specifically, in Examples 1-3 of the present invention, the phenolic resin, emulsifier, curing agent, and foaming agent selected by the inventors were all purchased from Langfang Yiruida Thermal Insulation Building Materials Co., Ltd., and the phenolic resin was an expandable phenolic re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing honeycomb enhanced phenolic foam composite materials. The method is characterized by including the steps of: (1) pouring phenolic resin foam composite into a die; (2) vertically placing a honeycomb in the phenolic resin foam composite in the die; (3) placing the die with the phenolic resin foam composite and the honeycomb in the step (2) into a baking oven at the temperature of 50-100 DEG C for foaming for 5-10h, and obtaining the honeycomb enhanced phenolic foam composite material. Via one-time soaking and heating consolidation, the method is capable of preparing the honeycomb enhanced foam composite materials with phenolic foam ingredients in the honeycomb materials and phenolic foam filled in honeycomb lattice holes, the operation procedure is extremely simple, only the die and the baking oven are utilized as equipment, so that the method has the advantages of efficiency and low cost, meanwhile, the composite material products can be guaranteed to have the advantages of good combination properties like light weight, sound insulation, heat insulation, specific strength, specific modulus, water resistance and flame retardance.

Description

technical field [0001] The invention relates to a method for preparing a composite material, in particular to a method for preparing a reinforced phenolic foam composite material. Background technique [0002] Phenolic foam has excellent characteristics such as light weight, sound insulation and heat insulation, among which the most prominent features are flame retardant, low smoke and high temperature disparity resistance; at the same time, because the foam of phenolic foam is closed-cell, it is difficult for moisture and moisture to enter, Therefore, it has the advantage of good moisture absorption resistance. However, phenolic foam also has the disadvantages of poor mechanical properties such as shear strength and compressive strength. [0003] Honeycomb materials have excellent characteristics such as high specific strength and specific modulus, but there are also many disadvantages. For example, because the honeycomb is an open-pore structure, the air can convect in th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C70/42B29K61/04B29K105/04
Inventor 穆举杰
Owner ARAMICORE COMPOSITE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap