Preparation method and device of toughened ceramic

A technology of tempering and ceramics, applied in the field of preparation of tempered ceramics, which can solve the problems of high cost and high energy consumption

Inactive Publication Date: 2014-06-11
尤潘垦
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a method and device for preparing toughened ceramics to solve the problem of high cost and high energy consumption in the production of toughened ceramics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and device of toughened ceramic
  • Preparation method and device of toughened ceramic

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Embodiment 1 A kind of preparation method of tempered ceramics

[0019] The technical solution adopted by the present invention is: the raw materials and the preparation method comprising the following parts by weight:

[0020] Raw material formula

[0021] Coal gangue: 99kg

[0022] Neodymium oxide: 0.1kg

[0023] Cerium oxide: 0.1kg

[0024] The preparation method is as follows:

[0025] (1) The pulverizing machine makes coal gangue into 80-mesh fine powder and sends it into the powder bin, and the pulverizing machine sends it into the primary plasma burner for high-temperature gasification and combustion, decarburization, and enters the boiler liquefaction chamber. The combustible gas enters the combustion chamber of the boiler to fully burn the combustible gas, and the generated steam enters the drum and then goes to the generator set;

[0026] (2) The flue gas generated by combustion enters the denitrification device and is taken away by the induced draft ...

Embodiment 2

[0027] Embodiment 2 A kind of preparation method of toughened ceramics

[0028] The technical solution adopted by the present invention is: the raw materials and the preparation method comprising the following parts by weight:

[0029] Raw material formula

[0030] Coal gangue: 99.5kg

[0031] Neodymium oxide: 2.5kg

[0032] Cerium oxide: 4kg

[0033] The preparation method is as follows:

[0034] (1) The pulverizing machine makes coal gangue into 200-mesh fine powder and sends it into the powder bin. The powder feeder sends it into the primary plasma burner for high-temperature gasification and combustion, decarburization, and enters the boiler liquefaction chamber. The generation of boiler liquefaction chamber The combustible gas enters the combustion chamber of the boiler to fully burn the combustible gas, and the generated steam enters the drum and then goes to the generator set;

[0035] (2) The flue gas generated by combustion enters the denitrification device and i...

Embodiment 3

[0036] Embodiment 3 A kind of preparation method of tempered ceramics

[0037] The technical solution adopted by the present invention is: the raw materials and the preparation method comprising the following parts by weight:

[0038] Raw material formula

[0039] Coal gangue: 100kg

[0040] Neodymium oxide: 5kg

[0041] Cerium oxide: 8kg

[0042] The preparation method is as follows:

[0043] (1) The pulverizer makes coal gangue into 300-mesh fine powder and sends it into the powder bin, which is sent by the powder feeder into the primary plasma burner for high-temperature gasification and combustion, decarburization, and enters the boiler liquefaction chamber, where the boiler liquefaction chamber produces The combustible gas enters the combustion chamber of the boiler to fully burn the combustible gas, and the generated steam enters the drum and then goes to the generator set;

[0044] (2) The flue gas generated by combustion enters the denitrification device and is ta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
service temperatureaaaaaaaaaa
densityaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method and a preparation device of toughened ceramic, which belong to the field of toughened ceramic. The toughened ceramic comprises the following materials in parts by weight: 99-100 parts of coal gangues, 0.1-5 parts of neodymium oxide and 0.1-8 parts of cerium oxide. The preparation method and the preparation device of toughened ceramic are the production method and the production device of toughened ceramic for carrying out deoxidation and nitridation on aluminum silicon oxide and other ingredients in the coal gangues and converting the aluminum silicon oxide and the other components into aluminum silicon nitride. The preparation method and the preparation device of the toughened ceramic are combination for producing toughened ceramic by virtue of coal gangue power generation and coal gangue liquid, so that heat energy generated in the coal gangue liquefying process is utilized for generating power, and therefore, the energy resources are saved and low-cost production is realized.

Description

technical field [0001] The invention belongs to a preparation method and device of tempered ceramics. Background technique [0002] The calorific value of coal gangue is generally 800-2800 cal / g, and its inorganic components are mainly oxides of silicon, aluminum, calcium, magnesium, iron, vanadium and some rare metals, and the percentage of its inorganic components: SiO 2 52-65; Al 2 o 3 16-46; Fe 2 o 3 0.03~14.63; CaO 0.42~2.32; MgO 0.44~2.41; TiO 2 0.90~4;P 2 o 5 0.007~0.24;K 2 O+Na 2 O is 1.45~3.9; V 2 o 5 0.008 to 0.03. [0003] At present, the physical and chemical characteristics and special properties of tempered ceramics have been recognized by people. There are many production methods for tempered ceramics, but the problem of high cost and high energy consumption has not been solved. At present, there is no deoxidation and nitrogen replacement using mineral components in coal gangue. method. Contents of the invention [0004] The invention provides a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/00C04B35/64
Inventor 尤潘垦赵群房长春潘子成
Owner 尤潘垦
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More