Abrasion resistant cast tube with high temperature oxidation resistant anticorrosive coating

A high-temperature oxidation-resistant and anti-corrosion layer technology, applied to anti-corrosion coatings, coatings, pipes, etc., can solve the problems of anti-corrosion coatings that are difficult to balance water resistance and anti-fouling effects, and achieve excellent high-temperature oxidation resistance and friction resistance. Reduce segregation and improve surface quality

Active Publication Date: 2013-09-04
江阴德耐特重工科技有限公司
View PDF4 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] However, anti-corrosion coatings in the prior art are usually difficult to balance water resistance, anti-fouling effect, and high temperature resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Abrasion resistant cast tube with high temperature oxidation resistant anticorrosive coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] A) Preparation of wear-resistant pipe body

[0065] 1) To obtain materials, select raw materials with the following chemical composition weight percentages:

[0066] C: 1.6%, V: 4.5%,

[0067] W: 9.1%, Mo: 7.6%,

[0068] Cr: 3.8%, RE: 0.15%,

[0069] Mn: 0.7%, Si: 0.05%,

[0070] B: 0.02%, Al: 0.2%,

[0071] Nb: 0.08%, Ni: 0.1%,

[0072] The balance is Fe and trace unavoidable impurities;

[0073] 2) Mix and heat ordinary steel scrap, micro-carbon ferrochromium, ferroniobium, ferronickel, ferrotungsten, ferromolybdenum, ferrochromium, ferroniobium, ferronickel and ferromanganese, add carbon with pig iron or graphite, mix and heat and melt into molten steel After the molten steel is melted, ferrosilicon is added for pre-deoxidation;

[0074] 3) According to the distribution ratio of raw materials, adjust the composition in front of the furnace and raise the temperature to 1580°C, then add aluminum blocks for final deoxidation, and then leave the furnace;

[0075]...

Embodiment 2

[0100] A) Preparation of wear-resistant pipe body

[0101] 1) To obtain materials, select raw materials with the following chemical composition weight percentages:

[0102] C: 2.7%, V: 6.0%,

[0103] W: 6.9%, Mo: 5.3%,

[0104] Cr: 5.4%, RE: 0.23%,

[0105] Mn: 0.6%, Si: 0.08%,

[0106] B: 0.01%, Al: 0.5%,

[0107] Nb: 1.1%, Ni: 0.2%,

[0108] The balance is Fe and trace unavoidable impurities;

[0109] 2) Mix and heat ordinary steel scrap, micro-carbon ferrochromium, ferroniobium, ferronickel, ferrotungsten, ferromolybdenum, ferrochromium, ferroniobium, ferronickel and ferromanganese, add carbon with pig iron or graphite, mix and heat and melt into molten steel After the molten steel is melted, ferrosilicon is added for pre-deoxidation;

[0110] 3) According to the distribution ratio of raw materials, adjust the composition in front of the furnace and raise the temperature to 1600°C, then add aluminum blocks for final deoxidation, and then leave the furnace;

[0111] ...

Embodiment 3

[0136] A) Preparation of wear-resistant pipe body

[0137] 1) To obtain materials, select raw materials with the following chemical composition weight percentages:

[0138] C: 3.7%, V: 8.5%,

[0139] W: 3.2%, Mo: 2.4%,

[0140] Cr: 8.9%, RE: 0.4%,

[0141] Mn: 0.3%, Si: 1.0%,

[0142] B: 0.01%, Al: 0.8%,

[0143] Nb: 2.4%, Ni: 0.3%,

[0144] The balance is Fe and trace unavoidable impurities;

[0145] 2) Mix and heat ordinary steel scrap, micro-carbon ferrochromium, ferroniobium, ferronickel, ferrotungsten, ferromolybdenum, ferrochromium, ferroniobium, ferronickel and ferromanganese, add carbon with pig iron or graphite, mix and heat and melt into molten steel After the molten steel is melted, ferrosilicon is added for pre-deoxidation;

[0146] 3) According to the distribution ratio of raw materials, adjust the composition in front of the furnace and raise the temperature to 1630°C, then add aluminum blocks for final deoxidation, and then leave the furnace;

[0147] 4)...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to an abrasion resistant cast tube with a high temperature oxidation resistant anticorrosive coating. An abrasion resistant cast tube body is produced through centrifugal casting and is subjected to quenching, high-temperature tempering, solution strengthening thermal treatment and twice tempering dispersion hardening thermal treatment, then a rustproof coating is coated on the outer wall of the tube through electrostatic spraying, finally a water glass nanometer composite coating prepared through testing is sprayed on the inner wall of the tube, and a high temperature oxidation resistant anticorrosive coating film inner layer is obtained after high temperature curing and cooling. The obtained metal tube has high hardness and abrasion resistance, and the anticorrosive coating of the metal tube has excellent waterproof performance, antifouling effect and high temperature resistance.

Description

technical field [0001] The invention relates to a pipe, in particular to a wear-resistant cast pipe with a high-temperature oxidation-resistant anti-corrosion layer. Background technique [0002] There are three main forms of material failure: fracture, corrosion, and wear. Although unlike the other two forms, material wear rarely causes catastrophic damage to metal workpieces, but the economic losses it causes are quite staggering. According to statistics, about 75%-80% of the failed mechanical parts are caused by metal wear. About 30%-50% of the energy supplied to the machine is consumed in the process of friction and wear. Parts wear out After that, it will not only affect the use efficiency of machinery and equipment, but also consume a lot of manpower and material resources to replace parts and repair equipment. The economic losses caused by wear and tear are about 120 billion US dollars per year in the United States and about 50 billion marks per year in Germany. Acco...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): F16L58/10F16L9/02C22C38/56C22C38/54C09D5/08C09D1/00
Inventor 严建山
Owner 江阴德耐特重工科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com