Low-temperature quenching method for medium-carbon steel workpiece

A low-temperature quenching and carbon steel technology, applied in the field of quenching, can solve the problems of difficulty in controlling the deformation of steel, easy deformation of steel, waste of resources, etc., and achieve the effect of reaching the standard and stable workpiece quality, controlling shrinkage and deformation, and controlling internal stress.

Active Publication Date: 2015-05-27
凌伯勇
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the cost of oil quenching is high, and the oil used at the same time remains on the workpiece, causing environmental pollution and waste of resources. In addition, the workpiece after oil quenching has disadvantages such as low hardness points, and the quality is not up to standard
[0005] Figure 7.18 on "Metallic Materials and Heat Treatment" discloses a schematic diagram of the ideal quenching rate of steel, such as figure 1 As shown, but the cooling rate of the steel is too fast, the internal stress is large, it is difficult to control the deformation of the steel, and the steel after quenching is easy to deform

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-temperature quenching method for medium-carbon steel workpiece
  • Low-temperature quenching method for medium-carbon steel workpiece
  • Low-temperature quenching method for medium-carbon steel workpiece

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] like Figure 5 Shown, according to the method for low-temperature quenching of medium carbon steel workpiece of the present invention, the step of 45# steel workpiece quenching is as follows:

[0035] (1) Heat the 45# steel workpiece to 840° in the mesh belt furnace, and heat preservation treatment after heating, so that the internal structure of the workpiece is transformed into a uniform unsaturated austenite structure;

[0036] (2) Cool the medium-carbon steel workpiece in a constant temperature state to 727°C by slow cooling method, and then cool the workpiece temperature from 727°C to 650°C at the sealing barrel. The interior of the workpiece is a supercooled austenite quenching structure;

[0037] (3) The workpiece leaves the sealed barrel and goes straight into the deep water area. The solution in the deep water area can be water or 251AQ quenching agent aqueous solution, and the water temperature in the deep water area is 28°C. The cooling process is that the ...

Embodiment 2

[0039] According to the method for low-temperature quenching of carbon steel workpiece in the present invention, the step of 60# steel workpiece quenching is as follows:

[0040] (1) Heat the 60# carbon steel workpiece to 810° in the mesh belt furnace, heat preservation treatment after heating, and the internal structure of the workpiece is transformed into a uniform unsaturated austenite structure;

[0041] (2) Cool the medium-carbon steel workpiece in a constant temperature state to 727°C by slow cooling method, and then cool the workpiece temperature from 727°C to 650°C at the sealing barrel. The interior of the workpiece is a supercooled austenite quenching structure;

[0042] (3) The workpiece leaves the sealed barrel and goes straight into the deep water area. The solution in the deep water area can be water or 251AQ quenching agent aqueous solution, and the water temperature in the deep water area is 32°C. The cooling process is that the workpiece is rapidly cooled fro...

Embodiment 3

[0044] According to the method for low-temperature quenching of carbon steel workpiece in the present invention, the step of 25# steel workpiece quenching is as follows:

[0045] (1) Heat the 25# carbon steel workpiece to 890° in the mesh belt furnace, heat preservation treatment after heating, and the internal structure of the workpiece is transformed into a uniform unsaturated austenite structure;

[0046] (2) Cool the medium-carbon steel workpiece in a constant temperature state to 727°C by slow cooling method, and then cool the workpiece temperature from 727°C to 650°C at the sealing barrel. The interior of the workpiece is a supercooled austenite quenching structure;

[0047] (3) The workpiece leaves the sealed barrel and goes straight into the deep water area. The solution in the deep water area can be water or 251AQ quenching agent aqueous solution, and the water temperature in the deep water area is 32°C. The cooling process is that the workpiece is rapidly cooled from ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a low-temperature quenching method for a medium-carbon steel workpiece, which comprises the following steps of: (I) heating a medium-carbon steel workpiece and preserving heat so as to convert the internal structure of the workpiece into a uniform and consistent unsaturated austenite structure; (II) cooling the obtained medium-carbon steel workpiece by a slow cooling method, wherein the inside of the workpiece is a cold austenite quenching structure; and (III) putting the obtained medium-carbon steel workpiece into water or an aqueous solution of a quenching agent for quick cooling to finish the quenching. The low-temperature quenching method for a medium-carbon steel workpiece, disclosed by the invention, can reduce internal stress of the workpiece in quenching and control the deformation quantity, has low cost, realizes up-to-standard workpiece quality, and is environment-friendly and stable.

Description

technical field [0001] The invention relates to the technical field of quenching, in particular to a method for low-temperature quenching of medium-carbon steel workpieces. Background technique [0002] At present, there are two methods of quenching medium carbon steel workpieces: water quenching and oil quenching. The faster the cooling rate, the greater the internal stress and the larger the deformation. When the deformation exceeds a certain strength of the material, the workpiece will crack. [0003] When using medium-carbon molten steel for quenching, the cooling rate is too fast, resulting in excessive internal stress, medium-carbon steel workpieces will be deformed, or even cracked, or because the workpiece is small and difficult to operate, quench with a lead wire string machine, such as 481H gasket 45# For steel workpieces, the heating temperature is set at 780°C, combined with stringing and binding, heating in a salt bath furnace, and cooling in a water pool. Altho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/00C21D1/19
Inventor 凌伯勇
Owner 凌伯勇
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com