Aluminum alloy cable core and method for preparing same

Abstract

The invention discloses an aluminum alloy cable core and a method for preparing the aluminum alloy cable core. The cable core is composed of 0.06wt% of Si, 0.40-1.2wt% of Fe, 0.05wt% of Cu, 0.01-0.05wt% of Mg, 0.01-0.3wt% of RE, 0.05wt% of Zn, 0.04wt% of B and the rest of Al. According to the aluminum alloy cable core and the method for preparing the aluminum alloy cable core, rare earth resources in China are utilized; after rare earth elements are added to conductor materials, aluminum alloy conductors which are extremely competitive in conductivity, flexibility, bending property, tensile property, creep resistance and connecting stability and excellent in resistance to corrosion are prepared through the smelting process, the rod drawing process, the wire drawing process, the compressing process and the stranding process and special annealing treatment; after being detected and verified by authorities at home and abroad, the compensative performance of the aluminum alloy cable core is far beyond current industry standards at home and abroad; high-tech aluminum alloy cable products can be widely applied to fields like electric power, automobiles, traffics, mineral products, ships, chemical industries and military, and the advantages of the high-tech aluminum alloy cable products are more obvious when the high-tech aluminum alloy cable products are used in complex and severe engineering environments.

Description

technical field [0001] The invention relates to a cable core, in particular to an aluminum alloy cable core and a preparation method thereof. Background technique [0002] Copper is listed as a strategic reserve material second only to petroleum in my country, and my country is a country lacking in copper ore resources and a big copper-consuming country. According to statistics from the China Nonferrous Metals Industry Association, as of 2009, China's reserves of copper resources were about 30 million tons, accounting for about 5% of the world's total reserves. At present, the annual domestic copper consumption is about 7 million tons, of which the copper consumption for wires and cables accounts for about 65% of the national copper consumption, accounting for a large proportion. If it is not imported, my country's copper resources can only be used for 5 years. In this way, my country needs to spend a large amount of foreign exchange to import copper every year, accounting ...

AI Technical Summary

Problems solved by technology

The disadvantage is that the creep resistance is poor. The thermal expansion and contraction caused by power-on and power-off will cause creep at the joint, and it will relax after a long time. Cause accidents; the materials of the bolts connecting the terminals to the equipment or the busbar are uneven, even iron bolts, the expansion coefficients of the me

Images