Molybdenum Oxide Direct Alloying Steelmaking Process

A technology of alloying steelmaking and molybdenum oxide, which is applied in the field of iron and steel metallurgy and alloy steel smelting, can solve the problems of increasing the consumption of electric energy and refractory materials, delaying the start time of fluxing and blowing oxygen, prolonging the smelting time, etc., to achieve smelting energy consumption The effect of less amount, reduced ferromolybdenum smelting links, and short alloying smelting time

Active Publication Date: 2016-08-17
JIANGYIN XINGCHENG SPECIAL STEEL WORKS CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this process can realize the direct alloying of molybdenum oxide to smelt molybdenum-containing steel, in order to avoid the oxidation of the reducing agent laid in the bottom of the furnace, it is necessary to delay the start time of fluxing oxygen blowing, thus increasing the consumption of electric energy and refractory materials, and prolonging the production time. Smelting time (for example: when 10t electric arc furnace 18t steel tapping target is smelted with 5.58% molybdenum, the smelting time is ≥15min longer than that of ferromolybdenum process, and the average yield can reach 97.2%

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A process for directly alloying molybdenum oxide to smelt molybdenum-containing steel, which uses molten iron to mix molybdenum oxide raw materials for reduction to realize the alloying of molybdenum elements in molten iron. Molybdenum oxide raw material is added to the empty molten iron tank, and the molybdenum oxide raw material is mixed with molten iron during the tapping process. After the molten iron is sent to the steelmaking furnace for smelting, the content of molybdenum element in the molten steel is detected, and ferromolybdenum is added according to the requirements of the steel type to make up for the lack of molybdenum in the molten steel. .

[0018] The calculation method for adding molybdenum oxide raw material is: ([Mo] e -[Mo] i )×m Fe / T Mo ; where [Mo] e It is the target Mo content of steel or molten iron smelting, %; [Mo] i Mo content in steel or molten iron before adding molybdenum oxide raw material, %; m Fe is the weight of steel or molten ...

Embodiment 2

[0021] A molybdenum oxide direct alloying process for smelting molybdenum-containing steel, using molten steel mixed with molybdenum oxide raw materials for reduction to achieve alloying of molten steel molybdenum elements, the process method is: first, the mass is MoO 3 (Converted to pure substance) Ferrosilicon powder with a mass of 10~20% is mixed with molybdenum oxide and pressed into agglomerates, and the agglomerates are added to the ladle one minute before the end of converter tapping for steel liquid mixing, and monitored after tapping The content of molybdenum element in molten steel, after the molybdenum content is stable, ferromolybdenum is added according to the requirements of the steel type to supplement the insufficient part of molybdenum element in molten steel.

[0022] All the other are with embodiment 1.

Embodiment 3

[0024] A molybdenum oxide direct alloying process for smelting molybdenum-containing steel, using molten steel mixed with molybdenum oxide raw materials for reduction to achieve alloying of molten steel molybdenum elements, the process method is: the mass is MoO 3 (Converted to pure substance) Limestone with a mass of 15~35% and a mass of MoO 3 (Converted to pure substance) Magnesium oxide with a mass of 0.1~5%, and a mass of MoO 3 (Converted to pure substance) 8~10% carbon powder by mass, the mass is MoO 3 (converted into pure substance) silicon carbide and molybdenum oxide with a mass of 2~15% are mixed and pressed into blocks, and added to an empty ladle. During the tapping process of the electric furnace, molten steel is poured into the ladle for mixing. MoO 3 (Converted to pure substance) 3~10% carbon powder by mass, the mass is MoO 3 (Converted to pure substance) 1~5% calcium carbide by mass, MoO by mass 3 (converted into pure substance) aluminum particles with a mas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a direct molybdenum oxide alloying steelmaking process. It is characterized in that: the smelting process consists of the following steps: a. Put the molybdenum oxide raw material into the container or smelting furnace that is not filled or partially filled with steel or molten iron, and then continue to load steel or molten iron to keep the molybdenum oxide raw material in the Mixing in molten steel or iron for a certain period of time; b After steel or molten iron is calmed in a container or smelting furnace, a certain amount of reducing agent is added to the surface of steel or molten iron or slag; c Molybdenum in steel or molten iron in the later stage of smelting After the element content is stable, molybdenum-containing alloy is added to adjust the composition of steel or molten iron. The invention has the characteristics of simple operation of the molybdenum alloying smelting process, high yield of molybdenum alloying elements, short alloying smelting time, less smelting energy consumption, and low smelting cost. 15% steel smelting.

Description

technical field [0001] The invention relates to a direct molybdenum oxide alloying steelmaking process. The invention belongs to the technical field of iron and steel metallurgy alloy steel (iron) smelting. Background technique [0002] Molybdenum is one of the conventional alloying elements in alloy steel because it can work together with other alloying elements in iron and steel materials to improve the performance of iron and steel materials. At present, in the process of smelting molybdenum-containing alloy steel, most alloy steel smelting enterprises adopt the method of adding ferromolybdenum alloy into the smelting furnace to realize the molybdenum element alloying of steel or molten iron, and the ferromolybdenum alloy is passed through the smelting furnace (such as electric furnace) It is produced by reducing molybdenum-containing raw materials (such as molybdenum oxide) with a reducing agent. Therefore, the smelting of molybdenum-containing steels needs to go throug...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C33/04
Inventor 刘吉刚
Owner JIANGYIN XINGCHENG SPECIAL STEEL WORKS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com