A vibrating material and no-baking technology, applied in the field of no-baking vibrating material, can solve the problems of hidden dangers to the health of construction workers, large amount of toxic and harmful gases, collapse or loosening of construction bodies, etc., so as to save the cost of baking medium and reduce Production process and effect of reducing steelmaking costs

Active Publication Date: 2014-12-03
浙江攀盛冶金材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present: In terms of material, the working lining of the tundish used to be mostly siliceous materials, which belong to acidic refractory materials and are not suitable for the current alkaline steelmaking. Therefore, alkaline refractory materials are mostly used now, with magnesium materials as the main Mainly, it is classified from the construction method, including heat insulation board, smear material, spray paint, dry working lining, etc. The use of alkaline heat insulation board is beneficial to clean steelmaking and good heat insulation, but the disadvantage is that the service life is low, and the installation time is relatively low. The labor intensity is relatively high; smearing materials and spray coatings are commonly used at present, and have the advantages of long service life and no pollution to molten steel, etc., but it needs to add about 20% of water during construction, so there are complex maintenance of spraying or mixing equipment, and work maintenance Insufficient for a long time, in addition, in order to reduce the hydrogen absorption of molten steel, it must be baked online at 1200°C and kept for more than 4 hours; the dry material is resistant to erosion, erosion, long service life, and simple construction. The body is prone to local collapse or loosening, which can easily lead to construction quality accidents; the binder of dry materials generally uses solid phenolic resin as raw material, and it emits a large amount of toxic and harmful gases during baking and heating, which pollutes the environment and is not conducive to clean steelmaking and environmental protection. Requirements, while bringing health risks to construction workers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0029] Specific embodiment 1, the weight percent of each component in the vibrating material is: 94% magnesia, 5% composite binder, 0.5% coagulant, and 0.5% polycarboxylate superplasticizer.

specific Embodiment 2

[0030] Specific embodiment 2, the weight percent of each component in the vibrating material is: magnesia 96%, composite binder 3%, coagulant 0.8%, polycarboxylate superplasticizer 0.2%.

specific Embodiment 3

[0031] Specific embodiment 3, the weight percentage of each component in the vibrating material is: magnesia 95%, composite binder 4%, coagulant 0.6%, polycarboxylate superplasticizer 0.4%.

[0032] The method for preparing the above-mentioned no-bake magnesia vibrating material includes the following steps in sequence:

[0033] a) the massive magnesia is broken into large particles with a jaw crusher;

[0034] b) Use a roller crusher to crush the large particles into small particles with a particle size of 0-2 mm;

[0035] c) Sieve the small particles according to different particle sizes, and the small particles with a particle size of 0-2mm are qualified raw materials;

[0036] d) Take small particles with particle diameters other than 0-2 mm to return to the cage, and use a roller crusher to crush unqualified raw materials;

[0037] e) Sieve the small particles according to different particle sizes, and the small particles with a particle size of 0-2mm are qualified raw ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
flexural strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a baking-free magnesium vibration material. The vibration material is prepared from 93-96% of magnesite, 3-6% of composite binder, 0.2-0.8% of setting accelerator and 0.2-0.8% of polycarboxylate water reducing agent. The preparation method has the advantages of single raw material, fewer production steps, less material accumulation and lower cost; and besides, the vibration material is free of baking, thereby saving the baking medium and enhancing the turnover utilization ratio of the tundish.

Description

technical field [0001] The invention relates to a baking-free vibrating material. Background technique [0002] At present: In terms of material, the working lining of the tundish used to be mostly siliceous materials, which belong to acidic refractory materials and are not suitable for the current alkaline steelmaking. Therefore, alkaline refractory materials are mostly used now, with magnesium materials as the main Mainly, it is classified from the construction method, including heat insulation board, smear material, spray paint, dry working lining, etc. The use of alkaline heat insulation board is beneficial to clean steelmaking and good heat insulation, but the disadvantage is that the service life is low, and the installation time is relatively low. The labor intensity is relatively high; smearing materials and spray coatings are commonly used at present, and have the advantages of long service life and no pollution to molten steel, etc., but it needs to add about 20% o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/66
Inventor 江群英于琪芳
Owner 浙江攀盛冶金材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products