Formula of rubber piston and preparation method thereof

A rubber piston and formula technology, applied in the field of rubber, can solve the problems of loss, unreliable quality, poor piston sealing, etc., and achieve the effect of reasonable formula and wide application range

Inactive Publication Date: 2014-01-15
TAIZHOU GAOGANG ZONE SHENGYUAN RUBBER CO LTD
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It has a wide range of uses, but due to the limitations of the manufacturing process and formula of the piston, the sealing and deformation of the piston cannot reach a relatively best value, so the pistons currently on the market are generally poor in sealing and unreliable in quality, which is easy to cause losses

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The method for preparing a rubber piston comprises the following steps.

[0021] Step 1: Put 320 parts of nitrile rubber into an internal mixer for mastication, and place it for 24 hours after mastication.

[0022] The second step: the plasticized nitrile rubber and 16 parts of zinc oxide, 4 parts of stearic acid, 130 parts of phenolic resin, 130 parts of white carbon black, 7 parts of adhesive RX-80, 6.2 parts of accelerator CZ, 32 parts of dibutyl ester, 7 parts of anti-aging agent 4010 and 0.2 part of epoxy resin were mixed together in an internal mixer, and left for 24 hours after mixing to obtain product A.

[0023] Step 3: Put the above mixed product A into an open mixer, then add 12 parts of sulfur for mixing, and leave it to obtain product B.

[0024] Step 4: Press the above-mentioned product B through a mold or a tablet machine to form a piston to obtain a rubber piston.

[0025] The prepared rubber piston has good sealing performance and the deformation meet...

Embodiment 2

[0029] The method for preparing a rubber piston comprises the following steps.

[0030] The first step: put 288 parts of nitrile rubber into the internal mixer for mastication, and place it for 24 hours after mastication.

[0031] The second step: the plasticized nitrile rubber and 14.4 parts of zinc oxide, 3.6 parts of stearic acid, 117 parts of phenolic resin, 117 parts of white carbon black, 6.3 parts of adhesive RX-80, 5.58 parts of accelerator CZ, 28.8 parts of dibutyl ester and 6.3 parts of anti-aging agent 4010 were mixed together in an internal mixer, and left for 24 hours after mixing to obtain product A.

[0032] Step 3: Put the above mixed product A into an open mixer, add 10.8 parts of sulfur for mixing, and leave it to obtain product B.

[0033] Step 4: Press the above-mentioned product B through a mold or a tablet machine to form a piston to obtain a rubber piston.

[0034] The prepared rubber piston has good sealing performance and the deformation meets the re...

Embodiment 3

[0037] The method for preparing a rubber piston comprises the following steps.

[0038] The first step: put 352 parts of nitrile rubber into the internal mixer for mastication, and place it for 24 hours after mastication.

[0039] The second step: the plasticized nitrile rubber and 17.6 parts of zinc oxide, 4.4 parts of stearic acid, 143 parts of phenolic resin, 143 parts of white carbon black, 7.7 parts of adhesive RX-80, 6.82 parts of accelerator CZ, 35.2 parts of dibutyl ester, 7.7 parts of anti-aging agent 4010 and 0.3 parts of epoxy resin were mixed together in an internal mixer, and left for 24 hours after mixing to obtain product A.

[0040] The third step: put the above-mentioned product A after mixing into an open mixer, then add 13.2 parts of sulfur for mixing, and leave it to obtain product B.

[0041] Step 4: Press the above-mentioned product B through a mold or a tablet machine to form a piston to obtain a rubber piston.

[0042] The prepared rubber piston has g...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses a formula of a rubber piston. According to parts by weight, the formula comprises 288-352 parts of nitrile butadiene rubber, 14.4-17.6 parts of a reinforcing agent, 3.6-4.4 parts of a stearic acid, 117-143 parts of phenolic resin, 117-143 parts of white carbon black, 6.3-7.7 parts of an adhesive agent, 5.58-6.82 parts of a promoting agent, 28.8-35.2 parts of dibutyl ester, 10.8-13.2 parts of sulfur and 0-0.3 part of epoxy resin. The rubber piston has good sealing performance; and the sealing performance and deformation thereof achieve the operating requirements.

Description

technical field [0001] The invention relates to the technical field of rubber, in particular to a rubber formula and a preparation method for making pistons. Background technique [0002] With the advancement of science and technology, the current piston is generally used to isolate the material in the container from the outside world, and can be used to prevent oil, water, corrosion, seal gas or prevent leakage. It has a wide range of uses, but due to the limitations of the manufacturing process and formula of the piston, the sealing and deformation of the piston cannot reach a relatively best value, so the pistons currently on the market are generally poor in sealing and unreliable in quality, which is easy to cause losses. Contents of the invention [0003] The invention provides a formula and a preparation method of a rubber piston with good sealing performance, whose sealing performance and deformation meet the use requirements. [0004] In order to solve the above p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L61/06C08K13/02C08K3/36C08K5/09C08K3/06C08K5/10
Inventor 鲁杰
Owner TAIZHOU GAOGANG ZONE SHENGYUAN RUBBER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap