A New Method for Controlling the Billet Pulling Speed ​​of Continuous Casting Round Billet Machine

A casting billet drawing speed and continuous casting round billet technology, which is applied in the field of continuous casting of alloy steel, can solve the problems of different lengths, different shapes, easy cracking, etc., and achieve the goals of increasing the yield of casting billets, being easy to popularize, and improving the quality of objects Effect

Active Publication Date: 2015-09-02
SHANDONG XIWANG SPECIAL STEEL
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0018] The purpose of the present invention is to solve the defects that the surface of the continuous casting slab, especially the large round billet of medium and high alloy steel is easy to crack, and the surface of the finished steel product after rolling is easy to produce various cracks of different shapes and lengths, and provides a A relatively new method of controlling the casting speed of the continuous casting round slab is more reasonable, which is convenient to effectively improve or basically solve the phenomenon of cracks on the surface of the arc continuous casting machine slab, and greatly improve the continuous casting process under the premise of ensuring the quality of the casting slab. Improve the overall production efficiency of the casting machine, further improve the slab yield, and better improve the surface quality of the continuous casting slab

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Example 1 GCr15 Bearing Steel Bullet Continuous Casting Technology (??500mm)

[0043] The specific steps are:

[0044] The qualified molten steel is transferred to the tundish through the ladle turret, then enters the crystallizer from the submerged nozzle, and then enters the tension leveler after cooling. The control method of the pulling speed is divided into two stages;

[0045] In the first stage, the time range is 20 minutes before the continuous casting slab is detached from the dummy head, and the casting speed control of the casting slab is formulated according to the traditional method, that is, the temperature of the tundish is controlled, and the casting speed is 0.30 m / Min - 0.35 m / min.

[0046] The second stage is specifically: after the slab is separated from the dummy head, the casting slab casting speed is adjusted based on the surface temperature of the slab entering the first straightening machine, so that the slab leaves the theoretical brittle t...

Embodiment 2

[0056] Example 2 27SiMn Coal Mine Special Hydraulic Prop Continuous Casting Technology (??500mm)

[0057] The specific steps are:

[0058] Qualified molten steel is transferred to the tundish through the ladle turret, then enters the vibrating crystallizer from the submerged nozzle, and then enters the tension leveler after cooling. The control method of the pulling speed is divided into two stages;

[0059] In the first stage, the time range is 30 minutes before the continuous casting slab is detached from the dummy head. The casting speed control of the casting slab is formulated according to the traditional method, that is, the temperature of the tundish is controlled, and the casting speed is 0.30-0.35 m / min.

[0060] The second stage is specifically: after the slab is separated from the dummy head, the casting slab casting speed is adjusted based on the surface temperature of the slab entering the first straightening machine, so that the slab leaves the theoretical br...

Embodiment 3

[0070] Example 3 Sucker rod 20CrMoA continuous casting technology for oil field (??310mm)

[0071] The specific steps are:

[0072] Qualified molten steel is transferred to the tundish through the ladle turret, then enters the vibrating crystallizer from the submerged nozzle, and then enters the tension leveler after cooling. The control method of the pulling speed is divided into two stages;

[0073] In the first stage, the time range is 10 minutes before the continuous casting slab is detached from the dummy head. The casting speed control of the casting slab is formulated according to the traditional method, that is, the temperature of the tundish is controlled, and the casting speed is 0.70-0.75 m / min.

[0074] The second stage is specifically: after the slab is separated from the dummy head, the casting slab casting speed is adjusted based on the surface temperature of the slab entering the first straightening machine, so that the slab leaves the theoretical brittle t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of alloy steel continuous casting, and specifically relates to a new method for controlling the casting speed of continuous casting round billets, which divides the method for controlling the casting speed of continuous casting billets into two stages. In the first stage, before the continuous casting slab is detached from the dummy head (about 10-30 minutes), the casting speed control of the slab is determined according to the actual superheat of the molten steel in the tundish. In the second stage, after the slab is detached from the dummy head, the actual casting speed of the slab should be determined according to the actual temperature of the slab surface in the straightening section, that is, adjusted according to the actual surface data of the slab at the straightening section The actual casting speed data of the slab makes the slab leave the dangerous temperature range of the theoretical brittle temperature range of 723°C-912°C as soon as possible, which greatly reduces the probability of cracks on the surface of the slab due to its own structural phase transformation. Tundish molten steel temperature. It is convenient to effectively improve or basically solve the phenomenon that the surface cracks of the billet surface of the arc-shaped large round billet continuous casting machine are prone to occur. On the premise of ensuring the quality of the billet, it can greatly improve the overall production efficiency of the continuous casting machine and further improve the yield of the billet. Better Improve the surface quality of large round continuous casting slabs.

Description

technical field [0001] The invention belongs to the technical field of alloy steel continuous casting, and in particular relates to a new method for controlling the casting speed of continuous casting round billets. Background technique [0002] At present, the continuous casting round billet machines of various sizes are running in various domestic iron and steel enterprises, and the basic production process technology guiding ideology principles adopted in the actual production process of continuous casting are: [0003] In the actual production process, generally the technical process planner subjectively determines or adjusts the continuous casting process in the entire continuous casting machine production process based on the degree of superheat of the molten steel in the tundish of the continuous casting machine and the technical experience accumulated in the previous production process. The only basis for the casting speed of the slab. Secondly, according to the cast...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/16
Inventor 赵福生王洪钦朱林林信霖颜鹏飞
Owner SHANDONG XIWANG SPECIAL STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap