High-performance anti-static PP (Propene Polymer) polymer as well as preparation method and application thereof

An antistatic and polymer technology, which is applied in the field of high performance antistatic PP polymer and its preparation, can solve the problems of low temperature resistance, poor notch impact resistance, antistatic PP easy aging, etc., to improve the impact resistance , Improve the effect of antistatic effect and high impact resistance effect

Inactive Publication Date: 2014-02-05
HUIZHOU CHANGYI NEW MATERIALS
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although the antistatic measures in the prior art have reduced the accumulation of static electricity on the PP surface to a certain extent, the effect is still unsatisfactory, and it is prone to failure. Antistatic standards for special cabinets and other products
The existing antistatic PP also has disadvantages such as easy aging, poor notch impact resistance, and low low temperature resistance, and the products produced are easily damaged and have poor performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] This embodiment provides a kind of high-performance antistatic PP polymer, and its raw material formula is made up of each component of following parts by weight:

[0035] Antioxidant 0.38 parts;

[0036] 3.2 parts of toughening agent;

[0037] PP 92.8 parts;

[0038] Antistatic agent 1 1 parts;

[0039] Antistatic agent 2 1.9 parts;

[0040] Described toughening agent is the POE8150 that U.S. Dow produces, and described antioxidant is the compound antioxidant K25 that Hongjiang Changhe Chemical Co., Ltd. produces; Described antistatic agent 1 is antistatic agent AM; Described antistatic agent Static agent 2 is H-S1 produced by Clariant, Switzerland.

[0041] The above-mentioned PP adopts commercially available products.

[0042] The preparation method of the above-mentioned high-performance antistatic PP polymer specifically includes the following steps: according to the ratio, antioxidant, toughening agent, PP, antistatic agent 1, and antistatic agent 2 are loade...

Embodiment 2

[0052] This embodiment provides a kind of high-performance antistatic PP polymer, and its raw material formula is made up of each component of following parts by weight:

[0053] 0.5 part of antioxidant;

[0054] 1 part of toughening agent;

[0055] PP 98.7 parts;

[0056] 12 parts of antistatic agent;

[0057] Antistatic agent 2 1 part;

[0058] Described toughening agent refers to POE8150 produced by U.S. Dow, and described antioxidant is the compound antioxidant K25 produced by Hongjiang Changhe Chemical Co., Ltd.; Described antistatic agent 1 is antistatic agent AM; The antistatic agent 2 is H-S1 produced by Clariant, Switzerland.

[0059] The above-mentioned PP adopts commercially available products.

[0060] The preparation method of the above-mentioned high-performance antistatic PP polymer specifically includes the following steps: according to the ratio, antioxidant, toughening agent, PP, antistatic agent 1, and antistatic agent 2 are loaded into the mixer repeat...

Embodiment 3

[0070] This embodiment provides a kind of high-performance antistatic PP polymer, and its raw material formula is made up of each component of following parts by weight:

[0071] 0.5 part of antioxidant;

[0072] 5 parts of toughening agent;

[0073] PP 88.5 parts;

[0074] Antistatic agent 1 1.5 parts;

[0075] Antistatic agent 2 2 parts;

[0076] Described toughening agent refers to POE8150 produced by U.S. Dow, and described antioxidant is the compound antioxidant K25 produced by Hongjiang Changhe Chemical Co., Ltd.; Described antistatic agent 1 is antistatic agent AM; The antistatic agent 2 is H-S1 produced by Clariant, Switzerland.

[0077] The above-mentioned PP adopts commercially available products.

[0078] The preparation method of the above-mentioned high-performance antistatic PP polymer specifically includes the following steps: according to the ratio, antioxidant, toughening agent, PP, antistatic agent 1, and antistatic agent 2 are loaded into the mixer repe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-performance conductive PP (Propene Polymer) polymer which is prepared from the following raw materials: an antioxidant, a toughening agent, PP, an anti-static agent 1 and an anti-static agent 2. The high-performance conductive PP polymer disclosed by the invention has high impact resistance and wear resistance properties, is especially good in anti-static property, and is especially applicable to applications in manufacturing precise instrument and meter shells and panels, military special boxes, aerospace craft trims, automobile trims, vessel trims, electric appliance shells, component and panels, and anti-static package, and the resistance on the surface of a product is as low as 1*10<10>omega.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to the field of PP polymer materials, in particular to a high-performance antistatic PP polymer and its preparation method and application. Background technique [0002] Polypropylene (PP) is a linear polymer with high density, no side chains, and high crystallinity. Compared with ordinary plastic materials, it has higher impact resistance and has the advantages of heat resistance and corrosion resistance. Because it usually has strong insulation properties, it is widely used in the production of instruments and electrical equipment. [0003] Although the antistatic measures in the prior art have reduced the accumulation of static electricity on the PP surface to a certain extent, the effect is still unsatisfactory, and it is prone to failure. Antistatic standards for special cabinets and other products. The existing antistatic PP also has the disadvantages of easy aging...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/08B29B9/06B29C47/92B29C48/40B29C48/92
CPCB29C48/92B29B9/06C08L23/12B29C2948/92561B29C2948/92704B29C2948/9258C08L2201/08C08L2201/04C08L2205/03C08L23/0815B29C48/40B29C2948/926B29C2948/92809B29C2948/92923
Inventor 林湖彬杜崇铭李华军
Owner HUIZHOU CHANGYI NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap