Method for preparing nano calcium carbonate for anti corrosive paints

A nano-scale calcium carbonate and anti-corrosion technology, applied in the field of coatings, can solve the problems of troublesome configuration and single function of calcium carbonate, and achieve good lipophilic and hydrophobic effects

Inactive Publication Date: 2014-02-05
ANHUI SHENGJIA COLOR PRINTING PACKING
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing calcium carbonate applied to the coating has a single function and is troublesome to use and configure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] A kind of preparation method of nanoscale calcium carbonate for anti-corrosion coating, preparation method comprises the following steps:

[0012] (1) Add 120 parts (kg) of light calcium carbonate to an appropriate amount of water, grind it into a nano-slurry, add 1 part of silane coupling agent KH580 at 45°C, stir for 50 minutes, and then add 0.5 part of antioxidant 1076, 1.3 parts of antioxidant BHT, stirred for 15 minutes, filtered, dried, and pulverized;

[0013] (2) Mix 0.1 part of ammonium molybdate, 2 parts of isobutyl methacrylate, 7 parts of rosin resin, and 15 parts of solvent to obtain a modified solution for later use;

[0014] (3) Add the powder obtained in step (1) into a high-speed mixer, keep the temperature at 80°C, add the modification solution, stir for 30 minutes, dry, and grind into nano-powder.

[0015] Adding the coating prepared in this embodiment, the salt spray test result was 22 days, and the salt spray test result was 29 days, which was sig...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing nano calcium carbonate for anti corrosive paints, wherein the method comprises the following steps of: (1) adding a proper amount of water in light calcium carbonate, grinding the mixture into nano slurry, adding 1-2 parts of silane coupling agent KH580 under 40-50 DEC C, stirring for 30-50 min, then adding 0.3-0.5 parts of anti-oxidant 1076, and 1-2 parts of anti-oxidant BHT, stirring for 10-20min, filtrating, drying and grinding; (2) uniformly mixing 0.1-0.2 parts of ammonium molybdate, 1-2 parts of isobutyl methacrylate, 5-7 parts of rosin resin, and 10-15 parts of solvent, to obtain a modified liquid for standby application; and (3) adding the powder prepared in the step (1) into a high speed mixer, maintaining temperature at 70-80 DEG C, adding the modified liquid, drying after stirring for 20-30min, and grinding to form a nano powder.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a method for preparing nanoscale calcium carbonate for anti-corrosion coatings. Background technique [0002] The existing calcium carbonate applied to the coating has a single function and is cumbersome to use and configure. Contents of the invention [0003] purpose of the present invention. [0004] The above purpose is achieved through the following schemes: [0005] A kind of preparation method of nanoscale calcium carbonate for anti-corrosion coating, it is characterized in that: preparation method comprises the following steps: [0006] (1) Add 100-120 parts of light calcium carbonate to an appropriate amount of water, grind it into a nano-slurry, add 1-2 parts of silane coupling agent KH580 at 40-50 ° C, stir for 30-50 minutes, and then add 0.3- 0.5 parts of antioxidant 1076, 1-2 parts of antioxidant BHT, after stirring for 10-20 minutes, filter, dry and pulverize; [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D5/08
Inventor 王明竹
Owner ANHUI SHENGJIA COLOR PRINTING PACKING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com