Antistatic and heat-transfer-printable label tape and manufacturing method thereof

Abstract

The invention relates to a trademark tape and a manufacturing method thereof, in particular to an antistatic and heat-transfer-printable trademark tape and a manufacturing method thereof. The thickness of the trademark tape is 0.100mm-0.165mm, and the weight is 90g / m2-150g / m2; the base fabric is made of PET material, the yarn specification of the base fabric is 60D-150D, and the warp density is 85 threads / cm -160 yarns / cm, weft yarn density is 30 yarns / cm-45 yarns / cm; antistatic agent is attached to the base fabric, and the weight of antistatic agent accounts for 0.5-1.5% of the weight of the base fabric. Production method, including gray cloth weaving: after weaving, the base fabric for making trademark tapes is obtained; dyeing and finishing treatment: including pre-dyeing and finishing treatment, dyeing and post-dyeing and finishing treatment, pre-dyeing and finishing treatment adopts alkali desizing method, and post-dyeing and finishing treatment includes Continuous segmental shaping and pre-shrinking process; electrostatic treatment, and then bake at 170-210°C for 1-2 minutes to dry the base fabric; calendering treatment: adopt calendering process, and install static eliminator in the calendering machine, after After chemical and mechanical double destaticization, it is made into trademark cloth. The trademark tape is safe and convenient to operate, antistatic and can be thermally transferred and printed.

Description

technical field [0001] The invention relates to a trademark tape and a manufacturing method thereof, in particular to an antistatic and heat-transfer-printable trademark tape and a manufacturing method thereof. Background technique [0002] Printing trademark tape is a special kind of textile. With the continuous development of my country's commodity economy, the awareness of trademarks and signs is increasing, and higher requirements are also put forward for the materials and functions of trademarks and labels. In order to change the expensive and complicated machine embroidery labels and ribbon labels with poor printing effect used in clothing, textile and other light textile industries in the past, and with the development of information and information industry, the demand for industrial typing tape (cloth) Therefore, there is a great social demand for the development of trademark cloth for printing, which has good printing adaptability, strong washability, allows a larg...

AI Technical Summary

Problems solved by technology

[0003] During the weaving and post-processing of the fabric, static electricity is generated and accumulated due to the friction between the fabric material itself or the fabric and the production machine. Due to the principle of heteropolar attraction in static electricity, it causes a lot of trouble in the production and processing of the fabric, such as fiber entanglement during processing. Machine parts and yarn hairs cannot be bundled, the warp opening is not clear during weaving, the fabric is vacuumed and stained, causing fabric surface defects, and increasing the difficulty of slitting and finishing. The most important thing is to color and cut during the product printing process. Inaccurate and difficult to sort

In TTR printing, the surface of the printed matter is required to be flat, smooth and full, so that the surface of the printed matter will not appear white. According to this characteristic, coated products and paper occupy a dominant position in TTR printing, and these two products are on the use surface. , each has its own defects, such as paper products are not suitable for water washing requirements, although coated products are suitable for water washing requirements, but coated products lack a soft feel, and some relatively high-end towels, clothes are relatively required to use a A comfortable feeling, so this soft and comfortable feeling is also required for trademark products

[0004] Our company disclosed an environmentally friendly non-scattering printed trademark tape and its manufacturing method in CN102031701B (2010-9-5), but the antistatic property and overall preparation process of the trademark tape still need to be improved

Images