Production process of cashmere and marine cell blending yarn

A technology of blended yarn and production process, applied in the field of dyeing and spinning, can solve the problems of poor mixing uniformity, affecting the wide application of cashmere and marine cell fiber blended products, and difference in dyeing fastness, so as to reduce chromatic aberration and reduce pilling. and hairiness, the effect of improving color fastness

Active Publication Date: 2014-04-09
河北浩丽羊绒科技有限公司
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the different composition of the two fibers, there will be problems of dyeing fastness difference and poor mixing uniformity during dyeing and mixing, which affects the wide application of cashmere and marine cell fiber blended products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production process of cashmere and marine cell blending yarn
  • Production process of cashmere and marine cell blending yarn

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A kind of production technology of cashmere marine cell blended yarn is characterized in that the steps are as follows:

[0040] The following percentages are mass percentages;

[0041] A. Open

[0042] The cashmere raw material and the marine cell fiber raw material are respectively opened; the beater used for the cashmere raw material is a drum beater, and the beater speed is controlled at 470r / min; the beater used for the marine cell fiber raw material is a porcupine beater, and the beater speed is controlled at 230r / min;

[0043] B. Pretreatment

[0044] Put the cashmere raw material and marine cell fiber raw material treated in step A into acetic acid for acid etching treatment, the pH value is controlled at 4.5, soak for 6 minutes, then take it out and rinse with deionized water for 20 minutes;

[0045] C. Cashmere dyeing

[0046] Put the cashmere raw material into deionized water, control the bath ratio at 1:15, add 2% of alkyl polyoxyethylene ether, 0.09 of s...

Embodiment 2

[0064] A kind of production technology of cashmere marine cell blended yarn is characterized in that the steps are as follows:

[0065] The following percentages are mass percentages;

[0066] A. Open

[0067] The cashmere raw material and the marine cell fiber raw material are respectively opened and loosened. The beater used for the cashmere raw material is a drum beater, and the beater speed is controlled at 550r / min; the beater used for the marine cell fiber raw material is a porcupine beater, and the beater speed is controlled at 300r / min;

[0068] B. Pretreatment

[0069] The cashmere raw material and marine cell fiber raw material processed in step A are put into tannic acid for acid etching treatment, the pH value is controlled at 4.7, soaked for 7 minutes, and then rinsed with deionized water for 20 minutes after taking it out;

[0070] C. Cashmere dyeing

[0071] Put the cashmere raw material into deionized water, control the bath ratio at 1:16, add 2.3% alkyl pol...

Embodiment 3

[0089] A kind of production technology of cashmere marine cell blended yarn is characterized in that the steps are as follows:

[0090] The following percentages are mass percentages;

[0091] A. Open

[0092] The cashmere raw material and the marine cell fiber raw material are respectively opened and loosened. The beater used for the cashmere raw material is a drum beater, and the beater speed is controlled at 630r / min; the beater used for the marine cell fiber raw material is a porcupine beater, and the beater speed is controlled at 330r / min;

[0093] B. Pretreatment

[0094] Put the cashmere raw material and marine cell fiber raw material treated in step A into formic acid for acid etching treatment, the pH value is controlled at 4.2, soak for 8 minutes, then take it out and rinse with deionized water for 20 minutes;

[0095] C. Cashmere dyeing

[0096]Put the cashmere raw material into deionized water, control the bath ratio at 1:17, add 2.7% alkyl polyoxyethylene ether...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a production process of a cashmere and marine cell blending yarn. The production process comprises the steps of A. loosening; B. pretreating; C. carrying out cashmere dyeing; D. carrying out marine cell fiber dyeing; E. carrying out secondary dyeing; F. combining; G, carrying out gilling; H. combing; I. spinning; and J. drawing. As the production process is adopted, the color aberration of cashmere and marine cell fiber blending product is reduced; the color fastness and the blending uniformity are improved.

Description

technical field [0001] The invention relates to the field of dyeing and spinning, in particular to a production process of cashmere marine cell blended yarn. Background technique [0002] Cashmere is a thin layer of fine velvet that grows on the outer skin of goats and covers the roots of goats' coarse hair. It grows out when it is cold in winter to resist the wind and cold. It falls off after the warming of spring and naturally adapts to the climate. It is a rare special animal fiber. The reason why cashmere is very precious is not only due to the scarcity of output (accounting for only 0.2% of the world's total animal fiber production), but more importantly, its excellent quality and characteristics. "Fiber Queen", "Soft Gold". [0003] Pure cashmere products are soft, comfortable, and warm-keeping, but they have high shrinkage rate, poor air permeability and easy to produce peculiar smell. They are prone to static electricity after wearing in winter. At the same time, pu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/04D06B3/02D06M13/188D06M13/238D06P1/673D06P3/82D06P5/00D06M101/12D06M101/04
Inventor 武彩艳崔应国
Owner 河北浩丽羊绒科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap