Soldering flux for submerged arc horizontal position welding of steel containment, preparation method and welding method

A technology of containment and horizontal welding, applied in arc welding equipment, welding medium, welding equipment, etc., can solve the problems of high flux cost and poor performance, and achieve excellent weld performance, excellent weld mechanical properties, and good welding process. sexual effect

Inactive Publication Date: 2014-04-23
ATLANTIC CHINA WELDING CONSUMABLES +1
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Under the current situation of massive application of clean energy such as nuclear power in my country, nuclear power projects will be the focus of clean energy development in my country in the future, and the development of submerged arc welding consumables for nuclear power steel containment SA738Gr.B steel and other materials will have a great impact There is still room for development. In nuclear power products, the existing flux has high cost and poor performance after welding.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0080] The component composition is: SiO 2 14kg, MgO 30kg, Al 2 O 3 20kg, ΣCaO 25kg, MnO 0.5 kg, Na 2 O 0.5 kg, K 2 O 0.2kg, TiO 2 0.5kg, Fe 2 O 3 1.0kg, S 0.020kg and P 0.026kg of pure powder are placed in the mixer, stirred and mixed evenly, then 18kg of sodium water glass is added to mix and granulate, then baked at 350℃, sintered at 750℃, and sieved , That is, a flux with an alkalinity of 2.3.

Embodiment 2

[0082] The component composition is: SiO 2 18kg, MgO 25kg, Al 2 O 3 24kg, ΣCaO 22kg, MnO 0.8kg, Na 2 O 1.0 kg, K 2 O 0.4kg, TiO 2 0.5 kg, Fe 2 O 3 0.6kg, S 0.020kg and P 0.026kg of pure powder are placed in the mixer, stirred and mixed uniformly, 16kg potassium water glass is added to mix and granulate, and then baked at 350℃, sintered at 750℃, and sieved. The flux with a basicity of 2.1 is obtained.

Embodiment 3

[0084] The component composition is: SiO 2 10kg, MgO 35kg, Al 2 O 3 18 kg, ΣCaO 20kg, MnO 1.2 kg, Na 2 O 1.1 kg, K 2 O 0.5kg, TiO 2 2.0 kg, Fe 2 O 3 1.5kg, S 0.018kg and P 0.028kg of pure powder are placed in the mixer, stirred and mixed uniformly, 17kg of potassium sodium water glass is added to mix and granulate, then baked at 350℃, sintered at 750℃, and sieved , That is, a flux with a flux alkalinity of 2.6.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a soldering flux and discloses a soldering flux for submerged arc horizontal position welding of a steel containment. The soldering flux for submerged arc horizontal position welding of the steel containment comprises the following components of, by mass, 6-18% of SiO2, 22-40% of MgO, 12-28% of Al2O3, 15-30% of sigma CaO, 0.5-4% of MnO, 0.5-2% of Na2O, 0.2-2% of K2O, 0<TiO2<=3%, 0<Fe2O3<=3.0%, 0<S<=0.030%, and 0<P<=0.030%. Compared with soldering fluxes in prior art, the submerged arc soldering flux for submerged arc horizontal position welding of the steel containment is special for welding the steel containment for nuclear power and has the advantages of good welding manufacturability, slag removal effects and mechanical properties and attractive shaping.

Description

Technical field [0001] The invention relates to a flux, in particular to a flux for submerged arc transverse welding of steel containment, a preparation method and a welding method using the flux in conjunction with a welding wire CHW-S62HRF. Background technique [0002] Under the current situation of large-scale application of clean energy such as nuclear power in my country, nuclear power projects will be the focus of my country’s future clean energy development. The development of submerged arc welding materials for nuclear power steel containment SA738Gr.B steel and other materials will be very large. In the current nuclear power products, the existing flux has high cost and poor performance after welding. Summary of the invention [0003] One of the objectives of the present invention is to provide a flux for submerged arc transverse welding of steel containment. The flux used for submerged arc transverse welding of steel containment is specially used for steel containment SA...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/22B23K35/40B23K35/30B23K35/32B23K9/18
CPCB23K35/3602B23K9/18B23K35/362B23K2103/04
Inventor 毛兴贵张效宁兰志刚张俊宝蒋勇余燕
Owner ATLANTIC CHINA WELDING CONSUMABLES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products