Sintered flux for stainless steel surfacing with band electrode

A technology of sintering flux and stainless steel strip, which is applied in the direction of welding medium, welding equipment, welding/cutting medium/material, etc. It can solve the problems of uneven flux quality, corrosion resistance and hydrogen stripping resistance that cannot meet the design requirements of pressure vessels, etc.

Active Publication Date: 2012-07-18
BEIJING JINWEI WELDING MATERIAL +1
View PDF6 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The quality of domestic matching flux is uneven, and the welding process, weld quality, especially the corrosion resistanc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sintered flux for stainless steel surfacing with band electrode
  • Sintered flux for stainless steel surfacing with band electrode
  • Sintered flux for stainless steel surfacing with band electrode

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0138] Example 1

[0139] According to the composition content designed in the present invention, six flux powders are prepared for each of the two fluxes. The sintered flux for submerged arc (SAW) is denoted as S1~S6; the sintered flux for electroslag surfacing (ESW) is denoted as E1~E6.

[0140] The flux components and the weight percentages of each component are shown in Table 1. The flux preparation method is as follows:

[0141] The required raw materials are sieved and weighed according to the formula. After the total weight is rechecked, the dry powder is put into a dry mixer for dry mixing. After dry mixing, put it into a wet mixer, and add about 20% water glass for wet After the wet mixing is uniform, the wet powder is sent to the granulation tray through the conveyor belt for granulation. After the granulation is completed, the conveyor belt is sent to the drying oven and dried at 250℃~300℃. After removing the moisture, the flux is screened. The sieved flux within the st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a sintered flux for stainless steel surfacing with band electrode. One technical scheme of the sintered flux for stainless steel surfacing with band electrode includes that the sintered flux is formed by sintering the following components and the proportioned raw materials or materials, including 15-30 parts of CaF2, 20-50 parts of MgO, 1-10 parts of Al2O3, 15-30 parts of CaO, 25-50 parts of SiO2, and 1-5 parts of alloy powder. The another technical scheme includes that the sintered flux for stainless steel surfacing with band electrode comprises the following components and the proportioned raw materials or materials including 60-80 parts of CaF2,20-40 parts of Al2O3, 1-5 parts of CaO, 1-5 parts of SiO2, and 1-5 parts of alloy powder. The sintered flux has excellent performance and can meet the service requirements completely.

Description

technical field [0001] The invention belongs to the field of welding materials, and in particular relates to a sintered flux for surfacing welding of stainless steel strips. The sintered flux for surfacing welding of stainless steel strips is widely used in the surfacing welding of stainless steel on the inner wall of thick-walled pressure vessels in the fields of petroleum and chemical industry. Background technique [0002] In recent years, with the development of the petrochemical industry, high-temperature, high-pressure, and corrosion-resistant pressure vessels tend to be large-scale and large-scale, such as thick-walled pressure vessels such as hydrogenation reactors, raw flow synthesis towers, and coal liquefaction reactors. In the manufacture of such thick-walled pressure vessels, in order to reduce costs, the common manufacturing method is to use low-alloy steel forging or thick plate coiling to make the cylinder and head, and then surfacing stainless steel lining o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K35/362
Inventor 夏毅冰王学东李伟陈波王士山李柱王磊卢兰志李钊
Owner BEIJING JINWEI WELDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap