Infrared-ray heating cloth and manufacturing method thereof

A manufacturing method and heating cloth technology, applied in textiles, papermaking, fabrics, textiles, etc., can solve problems such as flammability, safety hazards, and non-blocking water, and achieve the effect of simple manufacturing process

Inactive Publication Date: 2014-04-30
SHANXIAN TIANCHENG FIBERGLASS
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the popular electric blankets on the market are prone to aging and do not block water, so there are many safety hazards in use.
In addition, according to national policies, boilers are not allowed to be used for heating in many areas of our country, and these areas lack convenient and applicable heating equipment. In order to meet the heating needs of these areas, some manufacturers have developed heating cloth with polyester yarn as the main raw material. , used to make wall-mounted and carpet-type heating equipment, such as the products produced in Korea that are widely used in the market, but this product is not resistant to high temperature and is flammable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The manufacture method of infrared heating cloth, its steps are:

[0013] (1) Warping: According to customer needs, according to the length, width and area of ​​the heating cloth required, warping is carried out according to the traditional weaving process, and the warp and weft are all glass fiber filaments;

[0014] (2) Weaving and inserting carbon fiber: According to customer needs, the density of carbon fiber is determined according to the heating effect (power) required by the infrared heating cloth. The greater the density, the greater the heating effect; the smaller the density, the smaller the heating effect. Using traditional technology, Shuttleless loom is used for warp and weft weaving. During the weaving process, it is controlled by computer, and carbon fiber is automatically inserted in the weft direction according to the designed program (carbon fiber density requirement). The density is to insert a carbon fiber filament every 0.5-3cm, and get off the machi...

Embodiment 2

[0018] In step (2), the gray fabric after getting off the machine, 170g / m 2 , the addition amount of silica gel and polyurethane composite materials in step (3) is 60 g / m 2 , others are identical with embodiment 1.

Embodiment 3

[0020] In step (2), the gray cloth after getting off the machine, 140g / m 2 , the addition amount of silica gel and polyurethane composite materials in step (3) is 50 g / m 2 , others are identical with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to weaving technology, and discloses infrared-ray heating cloth and a manufacturing method thereof. The manufacturing method of the infrared-ray heating cloth is characterized by comprising the following steps: (1) warping, wherein warp and weft are both glass fiber filament; (2) inserting carbon fiber filament; (3) compositing, specifically utilizing a heat-resistant material to compositing grey fabric unloaded from a machine; and (4) decorating, preparing into needed products from woven grey fabric according to different size and client demands. The beneficial effects comprise that the manufacturing technology of the infrared-ray heating cloth is simple, and the infrared-ray heating cloth product is resistant to high temperature, not easy to burn, safe and reliable.

Description

(1) Technical field [0001] The invention relates to weaving technology, especially infrared heating cloth and its manufacturing method. (2) Background technology [0002] At present, the popular electric blankets on the market are prone to aging and do not block water, so there are many safety hazards in use. In addition, according to national policies, boilers are not allowed to be used for heating in many areas of our country, and these areas lack convenient and applicable heating equipment. In order to meet the heating needs of these areas, some manufacturers have developed heating cloth with polyester yarn as the main raw material. , used to make wall-mounted and carpet-type heating equipment, such as the products produced in South Korea that are widely used in the market, but this product is not resistant to high temperature and is flammable. This issue needs to be resolved as soon as possible. (3) Contents of the invention [0003] In order to make up for the d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B5/24D03D15/00D03D13/00D03D15/267D03D15/275D03D15/513
Inventor 夏鲁北王少青
Owner SHANXIAN TIANCHENG FIBERGLASS