A kind of polypropylene composition with high fluidity and high dimensional stability and preparation method thereof
A technology for polypropylene composition and dimensional stability, which is applied in the field of high-flow and high-dimensional-stable polypropylene composition and its preparation, can solve problems such as easy appearance and defects, and achieve wide injection molding process range and low shrinkage rate , The effect of simple extrusion process
Active Publication Date: 2016-03-16
株洲时代工程塑料实业有限公司
View PDF12 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0014] The technical problem to be solved by the present invention is to provide a high flow and high dimensional stability polypropylene composition and its preparation method, which can better control the dimensional fluctuations of large thin-walled sprayed products during injection molding and baking spraying Scope; solve the problem of appearance defects that are easy to occur when large thin-walled sprayed products are injection molded
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
preparation example Construction
[0038] The preparation method of described high flow high dimensional stability polypropylene composition comprises the following steps:
[0039] Step 1. Add the homopolypropylene, copolymerized polypropylene, thermoplastic elastomer, and linear low-density polyethylene into the mixer for uniform mixing according to the weight ratio, then add the coupling agent for uniform mixing, and then add other additives , heat stabilizer, light stabilizer, mineral filler, mixed at a low speed for 2-8 minutes to obtain a premix.
[0040]Step 2. Add the premix obtained in step 1 to the twin-screw extruder, set the feeding frequency to 6-10Hz, the frequency of the host machine to 22-26Hz, and set the temperature of the extrusion section to 170-180°C, 190-230°C , 190-230°C, 190-230°C, 190-230°C, 185-225°C, 185-225°C, 185-225°C, 200-240°C, the extruded plastic strips are water-cooled, the water tank temperature is 20-60°C, Air-dried and pelletized to obtain a polypropylene composition with h...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| melt flow index | aaaaa | aaaaa |
| melt flow index | aaaaa | aaaaa |
| particle diameter | aaaaa | aaaaa |
Login to View More
Abstract
The invention discloses polypropylene composition with high fluidity and high dimensional stability and a preparation method thereof. The polypropylene composition with high fluidity and high dimensional stability comprises components in parts by weight as follows: 10-60 parts of homo-polypropylene, 10-40 parts of co-polypropylene, 10-25 parts of thermoplastic elastomer, 3-8 parts of polyethylene, 0-35 parts of mineral fillers, 0.2-1 part of a heat stabilizer, 0.2-1 part of a light stabilizer, 0.3-1 part of a coupling agent and 0.5-3 parts of other auxiliaries. The preparation method comprises the steps as follows: raw materials are weighed in the ratio in parts by weight; the raw materials are stirred and mixed for 2-8 min at a low speed to obtain a premixed material; and the premixed material is added into a double-screw extruder for melt blending and extruding granulation. According to the invention, a product has high fluidity, low shrinking percentage and good dimensional stability; and a production formula is mature, an extrusion process is simple, the product performance can be regulated according to the formula and is controllable, and an injection molding process has a wide range.
Description
technical field [0001] The invention relates to the technical field of polymer composite materials, in particular to a polypropylene composition with high fluidity and high dimensional stability and a preparation method thereof. Background technique [0002] With the rapid development of the automobile industry, polypropylene (PP) composite materials with light weight, corrosion resistance, heat resistance, aging resistance, impact resistance, and balance of rigidity and toughness have been increasingly used. Modified PP is used in automobiles today. There are more than a dozen parts of the material, and the automobile bumper formed by modified PP material is the most representative part, and the design of the current bumper tends to be thinner, which requires the material to have good fluidity and high toughness. Good dimensional stability. Automobile bumper products have two shrinkage processes before assembly, that is, shrinkage after demoulding and cooling during inject...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/12C08L23/14C08L23/16C08L23/08C08L23/20C08L53/02B29C47/92B29C48/92
CPCB29C48/04B29C48/92B29C2948/92704B29C2948/92895
Inventor 杨治陈如意孟凡地韩领王雄刚黄安民
Owner 株洲时代工程塑料实业有限公司