Human hairpiece smoothing agent as well as preparation process thereof and method for tidying hairpieces

A slip agent, wig technology, applied in fiber processing, textiles and papermaking, animal fibers, etc., can solve the problems of human hair wigs with poor hair quality and gloss, no longer soft and smooth, and can not be restored, etc. Good hair care effect, prolonged wearing time and enhanced adsorption

Active Publication Date: 2014-07-23
XUCHANG HENGYUAN HAIR PROD
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] High-end wig products made of human hair feel soft and smooth after being processed during production, but after the user wears them for 3 months or more, the hair is no longer soft and smooth, and the hair is frizzy and easy to knot. After the human hair wig is treated with slip agent, the smoothness, durability and washability of the human hair wig can be restored to a certain extent, but it still cannot be restored to the state when it was just shipped from the factory. Hair quality and luster of hair wigs are also getting worse

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Embodiment 1: a kind of human hair wig slippery agent, it is characterized in that: it is the polydimethylsiloxane cationic microbe that is 25% with cetyltrimethylammonium bromide, terpolymeric silicone oil and concentration Emulsion is the main raw material, and Cathone is used as a preservative. The above-mentioned raw materials are specifically prepared as follows in percentage by weight: 6 grams of cetyltrimethylammonium bromide, 3 grams of ternary copolymerized silicone oil, and polydimethylformaldehyde with a concentration of 25%. 3 grams of siloxane cationic microemulsion, 0.3 grams of Kathon and 87.7 grams of deionized water.

[0027] Its preparation process of the human hair wig slippery agent configured by above-mentioned formula is as follows:

[0028] Step 1), the preparation of polydimethylsiloxane cationic microemulsion, using D4 silicone oil as the main raw material, high-temperature ring-opening polymerization reaction occurs under acidic conditi...

Embodiment 2

[0038]Embodiment 2: A kind of human hair wig slippery agent is characterized in that: it is 25% polydimethylsiloxane cationic microbe with cetyltrimethylammonium bromide, terpolymeric silicone oil and concentration Emulsion is the main raw material, and Cathone is used as a preservative. The above-mentioned raw materials are specifically prepared as follows in percentage by weight: 6 grams of cetyltrimethylammonium bromide, 3 grams of ternary copolymerized silicone oil, and polydimethylformaldehyde with a concentration of 25%. 4 grams of siloxane cationic microemulsion, 0.3 grams of Cathone and 86.7 grams of deionized water, the hardness of the deionized water is not more than 0.03 milliequivalents / liter.

[0039] The preparation process of the human hair wig slipping agent and the method of finishing the wig by using the human hair wig slipping agent of this embodiment are the same as in Example 1, and the following examples are also the same as in Example 1.

Embodiment 3

[0040] Embodiment 3: a kind of human hair wig slippery agent is characterized in that: it is the polydimethylsiloxane cationic microbe that is 25% with cetyltrimethylammonium bromide, terpolymeric silicone oil and concentration Emulsion is the main raw material, and Cathone is used as a preservative. The above-mentioned raw materials are specifically prepared as follows in percentage by weight: 6 grams of cetyltrimethylammonium bromide, 3 grams of ternary copolymerized silicone oil, and polydimethylformaldehyde with a concentration of 25%. 5 grams of siloxane cationic microemulsion, 0.3 gram of Cathone and 85.7 grams of deionized water. The hardness of the deionized water is not more than 0.03 meq / L.

[0041] Embodiment 4: a kind of human hair wig slippery agent is characterized in that: it is 25% polydimethylsiloxane cationic microbe with cetyltrimethylammonium bromide, terpolymeric silicone oil and concentration Emulsion is the main raw material, and Cathone is used as ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a human hairpiece smoothing agent of hairpieces made of human hairs as well as a preparation process of the human hairpiece smoothing agent and a method for tidying the hairpieces. The human hairpiece smoothing agent is characterized by being prepared from cetyl trimethyl ammonium bromide, ternary copolymerization silicone oil and a poly dimethyl siloxane cationic microemulsion serving as main raw materials and casson serving as a preservative, wherein all the raw materials are proportioned according to the weight percent: 6% to 10% of cetyl trimethyl ammonium bromide, 3% to 5% of ternary copolymerization silicone oil, 3% to 10% of 25% poly dimethyl siloxane cationic microemulsion, 0.3% of casson and 74% to 87% of deionized water. The human hairpiece smoothing agent is prepared from easily available raw materials by a simple preparation method, and has a good hair caring effect when used.

Description

technical field [0001] The invention belongs to the intercrossing technical field of dyeing and finishing technology, polymer chemistry technology, and daily chemicals, and in particular relates to a kind of hair dye with wide range of raw materials and simple preparation process, which can be specially treated by simple compounding technology and made of human hair. A human hair wig smoothing agent for a wig, a preparation process thereof and a method for arranging the wig. Background technique [0002] High-end wig products made of human hair feel soft and smooth after being processed during production, but after the user wears them for 3 months or more, the hair is no longer soft and smooth, and the hair is frizzy and easy to knot. After the human hair wig is treated with slip agent, the smoothness, durability and washability of the human hair wig can be restored to a certain extent, but it still cannot be restored to the state when it was just shipped from the factory. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M13/463D06M15/643C08G77/04D06M101/12
Inventor 赵见栓季书国刘小东
Owner XUCHANG HENGYUAN HAIR PROD