Anti-dazzle glass processing method and anti-dazzle glass

Abstract

The invention relates to an anti-dazzle glass processing method and anti-dazzle glass and discloses the anti-dazzle glass processing method. The method comprises the following steps: S1, providing a silicon resin material and a glass substrate; S2, spraying the silicon resin material to the surface of the glass substrate by a low pressure atomizing spray gun to form a silicon resin film which is a coarse film; and S3, roasting the glass substrate at 200-400 DEG C for 20-80 minutes. The method can effectively avoid conditions of lines and uneven thicknesses and the like of the glass and is free from environmental pollution, and the glass has high glossiness and high transmittance.

Description

technical field [0001] The invention relates to glass, in particular to an anti-glare glass and a processing method thereof. Background technique [0002] Anti-glare glass processing technology is to process the glass to form a relatively rough surface, so that the glass can achieve the effect of diffuse reflection, thereby reducing the glare reflected by the glass and obtaining a good visual effect. It is mainly used in the protective glass of the touch screen, such as: mobile phone , GPS navigator, touch screen computer, bank teller machine, switch panel, photo frame, medical equipment, etc. The current anti-glare glass processing technology is to use hydrofluoric acid, frosting powder and other chemical corrosion methods to process the glass surface into a relatively rough surface. Specifically, it is to blend hydrofluoric acid, frosting powder and water in a certain proportion The final chemical solution is sprayed on the glass surface, and then the surface is polished ...

AI Technical Summary

Problems solved by technology

[0003] 1. The uneven flow of liquid medicine on the glass surface will cause the processed glass to have certain lines and cause defects;

[0004] 2. It is difficult to control the spraying time of the liquid medicine on the glass surface. If the time is short, the effect will not be achieved, and if the time is long, the glass will be thinned or have inconsistent thickness due to excessive corrosion;

[0005] 3. When processing single-sided anti-glare glass, it will cause defects due to the liquid medicine penetrating into the back of the glass;

[0006] 4. Because the chemical corrosion method is to process the glass surface into a rough translucent frosting effect and then polish it with polishing liquid, it cannot pr

Images