Method for preparing high-flatness pure-tungsten metal sheet

A metal plate and flatness technology, applied in the direction of metal rolling, etc., can solve problems such as the difference between the blank and the same plate, long production cycle, large processing site, etc., to shorten the production process and cycle, reduce the number of intermediate annealing, rolling The effect of frequency reduction

Active Publication Date: 2014-08-13
上海六晶科技股份有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] (1) For pure tungsten foils with a thickness less than or equal to 0.08mm, the billet produced by the traditional single-sheet rolling method has a poor difference in the same plate. In order to improve the flatness of the product, a higher leveling temperature is often required. The brittleness of the material increases, making it difficult to meet the performance requirements of the product
[0006] (2) The rolling deformation of pure tungsten is about 35%. Excessive deformation will easily lead to defects such as delamination and peeling
Occupies a large space: a large processing space is required, and each process needs to be isolated from each other
[0007] (3) Multiple annealing is required during rolling with large deformation, which increases the number of furnace passes, consumes a lot of energy, and has a long production cycle

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing high-flatness pure-tungsten metal sheet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] Below in conjunction with specific embodiment, further illustrate the present invention. It should be understood that these examples are only used to illustrate the present invention and are not intended to limit the scope of the present invention. In addition, it should be understood that after reading the teachings of the present invention, those skilled in the art can make various changes or modifications to the present invention, and these equivalent forms also fall within the scope defined by the appended claims of the present application.

[0024] like figure 1 Shown, a kind of method for preparing high flatness pure tungsten metal plate, its steps are as follows:

[0025] (1) Put the pure tungsten metal plate with a thickness of 0.1 to 0.4 mm into the preheated rolling mill for warm rolling. The feeding method is single sheet feeding, with a pressure of about 12 tons and a speed of 200~600r / min. Rolling to a deformation of 30%;

[0026] (2) Divide the rolled p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing a high-flatness pure-tungsten metal sheet. The method comprises the following steps of placing a pure-tungsten metal plate with a thickness of 0.1 to 0.4mm on a preheating roller mill for warm rolling, and rolling-milling the pure-tungsten metal plate until the deformation is 30 percent under the conditions of pressure of about 12T and speed of 200 to 600r / min, wherein a single feeding mode is adopted; uniformly dividing the rolled pure-tungsten metal plate along the length direction, and overlaying the uniformly-divided pure-tungsten metal plates along the thickness direction; performing subsequent warm rolling by adopting a double-layer overlaying feeding method, and rolling the pure-tungsten metal plates on the roller mill until the thickness of a single plate reaches a required thickness. According to the method, the number of intermediate annealing times is reduced, a production process is simplified, the rolling pressure and rolling passes are reduced, the energy consumption is effectively reduced, the production cost is lowered, and the production efficiency is improved.

Description

technical field [0001] The invention belongs to the technical field of pure tungsten metal processing, in particular to a method for preparing a high flatness pure tungsten metal thin plate. Background technique [0002] Due to its high melting point, high elastic modulus, good shock resistance and corrosion resistance, high electrical conductivity, thermal conductivity and excellent thermal fatigue resistance, and low expansion coefficient and other excellent properties, tungsten metal is widely used in medical treatment , metallurgy, electric light source, semiconductor device, high temperature structural parts and nuclear industry and other fields, among which the plate is the most widely used. In the field of medical CT collimator and detector. With the development of CT machines, the flatness requirements of collimators have been increased from less than 0.03 to less than 0.015, which poses new challenges to the preparation of pure tungsten thin materials. [0003] Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B21B1/38
Inventor 张丽娟朱玉斌
Owner 上海六晶科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products