Method for producing aerated building block by using doping carbide slag

A hollow brick, carbide slag technology, applied in the direction of climate sustainability, sustainable waste treatment, solid waste management, etc., to solve the problem of environmental pollution, use a large amount, and achieve the effect of high strength

Inactive Publication Date: 2014-09-17
HEFEI RISINE HEATEK
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In summary, there have been reports on the production of cement, wall bricks, and road materials with calcium carbide slag as auxiliary raw materials, but there have been no reports on the use of inorganic waste as the main raw material for the production of aerated blocks.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing aerated building block by using doping carbide slag
  • Method for producing aerated building block by using doping carbide slag
  • Method for producing aerated building block by using doping carbide slag

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] A method of doping calcium carbide slag to produce aerated hollow bricks, the method includes the following steps:

[0021] (1), mix the raw materials according to the following dry basis mass parts:

[0022]

[0023] (2), take 60-70 parts of inorganic garbage and 2-3.5 parts of aluminum powder in mass parts before fine grinding, and mix the modified fly ash, cement, dihydrate gypsum and calcium carbide slag after crushing with inorganic Garbage and aluminum powder are mixed evenly and finely ground;

[0024] (3), put the broken ceramic waste and finely ground dry material into the mixing equipment, and add water to fully stir;

[0025] (4), according to above-mentioned steps (3) 0.05% of stirring material quality adds waste aluminum powder, 0.004% of stirring material adds foam stabilizer;

[0026] (5) Put the slurry stirred in the above step (4) at a temperature of 60-75° C., the foaming time of static stop is 2-3 hours, and the external temperature of static sto...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for producing an aerated building block by using doping carbide slag. The method comprises the following steps: 1) mixing raw materials consisting of, on a dry basis, 55 to 65 parts by mass of modified fly ash, 6 to 10 parts by mass of dihydrate gypsum, 20 to 35 parts by mass of cement and 10 to 12 parts of carbide slag; 2) before fine grinding, weighing 60 to 70 parts by mass of inorganic garbage and 2 to 3.5 parts by mass of aluminum powder, uniformly mixing crushed fly ash, cement, dihydrate gypsum and carbide slag with inorganic garbage and aluminum powder and then carrying out fine grinding; and 3) putting a crushed ceramic waste material and a dry material obtained after fine grinding into a stirring apparatus, adding water and carrying out full mixing. According to the invention, the usage amount of the inorganic garbage is great, energy conservation and environmental protection are realized, the problem of environmental pollution caused by stockpiling treatment of inorganic garbage is alleviated, and a novel raw material is provided for a hollow brick.

Description

technical field [0001] The invention relates to the field of new building materials, in particular to a method for producing aerated hollow bricks by doping carbide slag. Background technique [0002] For a long time, the comprehensive utilization of carbide slag has been a worldwide problem. Although a lot of research has been done on the comprehensive utilization of carbide slag at home and abroad, most of them have not been put into industrial realization due to various technical and economic reasons. [0003] In conclusion, it has been reported that carbide slag is used as an auxiliary raw material to produce cement, wall bricks, and road materials, but the production of aerated blocks with inorganic waste as the main raw material has not been reported. Contents of the invention [0004] The purpose of the present invention is to provide a method for producing aerated hollow bricks doped with calcium carbide slag, which consumes a large amount of inorganic waste, is en...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B38/02C04B18/30C04B22/14
CPCY02W30/91
Inventor 张时利王建跃王皓静
Owner HEFEI RISINE HEATEK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap