Polyether sulfone ultrafiltration membrane preparation method capable of improving permeability and selectivity simultaneously

A polyethersulfone ultrafiltration membrane, a selective technology, applied in chemical instruments and methods, semi-permeable membrane separation, membrane technology and other directions, can solve the problems of low permeability of polyethersulfone ultrafiltration membrane, and achieve high industrial applications Value, porosity increase, effect of separation layer thickness increase

Active Publication Date: 2014-09-24
NANJING UNIV OF SCI & TECH
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to solve the problem of low permeability of polyethersulfone ultrafiltration membrane, and propose a polyethersulfone ultrafiltration that uses water-soluble polyethyleneimine as an additive to regulate the membrane structure in the phase inversion process while improving permeability and selectivity Membrane preparation method, specifically a preparation method of polyethersulfone ultrafiltration membrane with improved permeability and selectivity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyether sulfone ultrafiltration membrane preparation method capable of improving permeability and selectivity simultaneously
  • Polyether sulfone ultrafiltration membrane preparation method capable of improving permeability and selectivity simultaneously
  • Polyether sulfone ultrafiltration membrane preparation method capable of improving permeability and selectivity simultaneously

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] A method for preparing a polyethersulfone ultrafiltration membrane with improved permeability and selectivity simultaneously, the method comprising:

[0026] (1) Preparation of casting solution: Mix four components of polyethersulfone, polyethyleneimine, polyvinylpyrrolidone and solvent to make a casting solution, heat and stir to dissolve, and after forming a homogeneous solution, let it stand for defoaming for later use ;

[0027] The ratio of polyethersulfone, polyvinylpyrrolidone, polyethyleneimine, and N-N dimethylformamide is as follows, and its component content is:

[0028]

[0029] All percentages are by weight;

[0030] (2) Use a scraper to form a uniform solution layer on a glass plate with the above-mentioned degassed solution, pre-evaporate, the pre-evaporation medium is air, and then immerse in a coagulation bath to form a film; after the film is formed, fully wash it with ultrapure water , remove solvent, and save.

Embodiment 1

[0033] Dissolve 0.1 g of polyethyleneimine in 78.9 g of N-N dimethylformamide, add 16 g of polyethersulfone (PES) and 5 g of polyvinylpyrrolidone (PVP) after it is completely dissolved, and place it in a 60°C oil bath Continue to stir for 6-8 hours to form a homogeneous casting solution. The casting solution is left to stand for more than 12 hours for defoaming.

[0034] The defoamed casting solution was scraped on a clean glass plate at 25°C and 60% relative humidity, and stayed in the air for 30 seconds, then soaked in a coagulation bath for half an hour, taken out and soaked in deionized water, and Store in deionized water until use. Its pure water flux is 239L / m 2 ·h·bar, bovine serum albumin (67000MW) rejection rate is 95.5%.

Embodiment 2

[0036] Dissolve 0.3 grams of polyethyleneimine in 78.7 grams of N-N dimethylformamide, add 16 grams of polyethersulfone (PES) and 5 grams of polyvinylpyrrolidone (PVP) after it is completely dissolved, and place it in an oil bath at 60 ° C Continue to stir for 6-8 hours to form a homogeneous casting solution. The casting solution is left to stand for more than 12 hours for defoaming.

[0037] The defoamed casting solution was scraped on a clean glass plate at 25°C and 60% relative humidity, and stayed in the air for 30 seconds, then soaked in a coagulation bath for half an hour, taken out and soaked in deionized water, and Store in deionized water until use. Its pure water flux is 359L / m 2 ·h·bar, bovine serum albumin (67000MW) rejection rate is 96.1%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a polyether sulfone ultrafiltration membrane preparation method capable of improving permeability and selectivity simultaneously. An ultrafiltration membrane is prepared by adopting a phase inversion method, and PEI (polyetherimide) is used as an additive, and is added to change the phase inversion process and regulate the structure of the PES ultrafiltration membrane to achieve high permeability and high selectivity. The preparation method comprises the following steps of (1) dissolving the PEI in a solvent (DMF) (dimethyl formamide), adding polyether sulfone and PVP (polyvinylpyrrolidone), and performing heating to dissolve the polyether sulfone and the PVP to form a homogeneous membrane coating solution; and (2) controlling membrane forming conditions, and preparing the flat membrane. According to the method, the structure of the PES ultrafiltration membrane is effectively regulated, and the aperture ratio of the PES ultrafiltration membrane and the thickness of a selective layer are increased to greatly improve the permeability and the selectivity; the preparation method is simple and suitable for being used in the industrial production and the preparation of a basic membrane of a nanofiltration membrane.

Description

technical field [0001] The invention belongs to the technical field of separation and purification ultrafiltration membranes, preparation and modification, and in particular relates to a preparation method of polyethersulfone ultrafiltration membranes with improved permeability and selectivity. Background technique [0002] Polyethersulfone (PES) has good chemical stability, high temperature resistance, acid and alkali resistance, strong mechanical stability, high oxidation resistance and chlorine resistance, and is currently one of the most commonly used ultrafiltration membrane materials. However, the low permeability of PES membrane and the inability to increase the water flux and rejection rate of the membrane limit its application and treatment efficiency. [0003] At present, researchers mainly focus on improving the permeability of ultrafiltration membranes to improve their hydrophilicity. The methods adopted are mainly three types: one is surface coating, which is si...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01D71/68B01D69/02B01D67/00
Inventor 李健生王连军方小峰陆锐孙秀云沈锦优韩卫清刘晓东
Owner NANJING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com