Hot rolled sheet steel for cold forming and making method thereof
A technology for a hot-rolled steel sheet and a manufacturing method, which is applied in the field of high-strength hot-rolled steel sheet for cold forming with a yield strength of 750 MPa and the preparation thereof, can solve the problems of difficult production process and high production cost, and achieves reduced production cost and strong adaptability. , Simple effect of rolling process control
Inactive Publication Date: 2014-09-24
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP +1
View PDF7 Cites 2 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0006] The purpose of the present invention is to provide a new high-strength steel plate for cold forming with a yield strength of 750 MPa in order to overcome the defects of high production cost and difficult production process of high-strength hot-rolled steel sheets with a yield strength of 750 MPa for cold forming in the prior art. Hot-rolled steel sheet and manufacturing method thereof
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1-5
[0029] After the steelmaking step (see Table 1 for the composition of the molten steel after steelmaking), the molten steel is cast in an integral argon gas seal, and the molten steel is injected into the tundish through the sliding nozzle at the bottom of the ladle. The temperature of the tundish is 1538°C. The casting speed of the slab is 0.7m / min, and the thickness of the continuous casting slab is 200mm~230mm; the continuous casting slab is heated in the heating furnace, and the heated slab is dephosphorized by high-pressure water to remove the oxide scale formed on the surface, and then enters the In the reversible rough rolling unit, the intermediate billet after rough rolling enters the hot coil box, the strip head and tail are exchanged, and then the finish rolling is carried out. After the finish rolling, laminar cooling and coiling are carried out to obtain hot-rolled steel plates. Among them, The temperature of slab heating, the exit temperature of rough rolling, the...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| thickness | aaaaa | aaaaa |
| thickness | aaaaa | aaaaa |
| yield strength | aaaaa | aaaaa |
Login to View More
Abstract
The invention discloses a hot rolled sheet steel for cold forming and a making method thereof, the making method of the hot rolled sheet steel for cold forming includes the steps of steelmaking, continuous casting, heating, hot continuous rolling and coiling, and the steelmaking molten steel is characterized by comprising the following components: 0.05 to 0.1 wt% of C, less than or equal to 0.1 wt% of Si, 1.7 to 1.95 wt% of Mn, 0.03 to 0.07 wt% of Nb, 0.09 to 0.14 wt% of Ti, 0.1 to 0.3 wt% of Mo, less than or equal to 0.025 wt% of P, less than or equal to 0.01 wt% of S, and the balance of Fe and unavoidable impurities; the precision rolling finish rolling temperature of the hot continuous rolling step is 850-900 DEG C; and the coiling temperature of the coiling step is 530 to 580 DEG C. According to the method, the high-strength hot rolled sheet steel for cold forming with yield strength of 750MPa is provided.
Description
technical field [0001] The invention relates to a hot-rolled steel plate for cold forming and a manufacturing method thereof, in particular to a high-strength hot-rolled steel plate for cold forming with a yield strength of 750 MPa and a preparation method thereof. Background technique [0002] In order to avoid the influence of hot-forming process on the softening of hot-rolled steel plate material, in practical application, it is an economical and practical method to use cold-forming process to process cold-bent parts for hot-rolled steel plate with small thickness. Hot-rolled steel sheets for forming have been greatly developed, and hot-rolled steel sheets for cold forming are widely used in automobiles, engineering machinery, steel structures, construction and other fields. [0003] The yield strength of the hot-rolled steel plate first used in the cold forming process is within 400MPa. With the development of various industries, in order to reduce production costs and i...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/14C22C33/04C21D8/04
Inventor 张开华叶晓瑜翁建军邹小波刘勇罗许王海云任守斌
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP