An antibacterial layer and oxide technology, applied in metal layered products, metal material coating processes, coatings, etc., can solve problems such as product pollution, synthetic resin deformation, glasses or mobile phone pollution, etc., to improve scratch resistance. , the effect of improving antibacterial properties
Active Publication Date: 2014-10-01
CO DON AG
View PDF5 Cites 8 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0011] Synthetic resin products are more likely to be polluted than glass products. With the help of simple cleaning, bacteria as the source of pollution cannot be removed. Disinfection in boiling water will cause deformation of synthetic resin. In recent years, it has been reported that the bacterial contamination of telephone microphones is serious (please refer to The twelfth collection of papers of Shangzhi University (1991.9) pp67-81)
[0012] But in fact, most ordinary people cannot recognize that synthetic resin products have been polluted
[0013] Recently, the number of glasses wearers has increased rapidly, reaching about 1 / 3 of the total population, and mobile phone holders account for more than 70% of the total population of Korea, but there are no measures or countermeasures against the pollution of such glasses or mobile phones
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment
[0030] Using zinc oxide, calcium oxide, and a 1:1 mixture of zinc oxide and calcium oxide, an antibacterial layer with a thickness of 20 nm is formed.
[0031] For lenses formed with such an antibacterial layer, the antibacterial performance was measured according to the following test method.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| Thickness | aaaaa | aaaaa |
Login to View More
Abstract
The invention relates to an antibiotic layer composed of a metal oxide, and relates to an antibiotic thin film which utilizes a metal oxide, namely zinc oxide and / or calcium oxide, and a preparing method thereof. More particularly, the invention relates to the antibiotic layer which is formed through vacuum-plating one or two selected from a group which is composed of metal oxides, namely the zinc oxide and calcium oxide outside a panel that is made of synthetic resin, namely a glass lens, a mobile phone display screen, a food container, a medical container, etc.
Description
technical field [0001] The present invention relates to an antibacterial film using metal oxides, ie, zinc oxide and / or calcium oxide, and a method for producing the same. More specifically, it relates to a method for vacuum coating the exterior of flat panels made of synthetic resin, such as spectacle lenses, mobile phone display screens, food containers, medical containers, etc. Antibacterial film formed by one or two kinds of the group and its manufacturing method. Background technique [0002] As substances exhibiting antibacterial properties known so far, there are silver, copper, wood acetic acid, organic chemicals, antibiotics, and the like. However, these materials cannot be used for synthetic resin flat panels, and titanium oxide or metal oxide composites including it exhibiting photocatalytic activity can be used for purposes such as antibacterial and deodorizing due to their photocatalytic activity. It is also widely known (for example, Patent Document 1, etc.)....
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More IPC IPC(8): C09D1/00C09D5/14B32B33/00
CPCB32B15/08C23C2/06G02B1/10
Inventor 申度铉
Owner CO DON AG