ABS / PA6 material for extrusion technology and preparation method thereof

An extrusion process and ABS resin technology, applied in the field of ABS/PA6 materials for extrusion process and their preparation, can solve the problems of low viscosity, difficult extrusion molding, low melt strength, etc., and achieve excellent extrusion moldability, The effect of extrusion products with excellent performance, great economic value and social value

Inactive Publication Date: 2014-10-29
SHANGHAI GENIUS ADVANCED MATERIAL (GRP) CO LTD
View PDF13 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high crystallization rate of PA6, low viscosity and low melt strength, it is difficult to extrude

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • ABS / PA6 material for extrusion technology and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] (1) Weigh the raw materials of each component according to the following parts by weight:

[0034] ABS resin (flow coefficient 6.5) 100 parts,

[0035] PA6 resin (viscosity 1.8) 10 parts,

[0036] Glass fiber (diameter 7μm) 20 parts,

[0037] ABS-g-MAH 5 parts,

[0038] 0.3 parts of polyethylene glycol epoxy resin

[0039] 0.2 parts of calcium stearate,

[0040] Antioxidant 1076 0.1 parts,

[0041] Antioxidant 168 0.2 parts;

[0042] Mix the above raw materials at high speed with a high-speed mixer, control the speed of the high-mixer to 700rmp, the mixing temperature to 80°C, and mix for 3 minutes;

[0043] (2) Pass the mixed material through a twin-screw extruder. The temperature of each zone is controlled at 190-220°C. The extruder strands are cut into pellets to obtain ABS / PA6 materials. The mechanical properties of the test are shown in Table 1.

Embodiment 2

[0045] (1) Weigh the raw materials of each component according to the following parts by weight:

[0046] ABS resin (flow coefficient 4.5) 100 parts,

[0047] PA6 resin (viscosity 2.4) 20 parts,

[0048] Glass fiber (diameter 11μm) 32 parts,

[0049] SMA 8 parts,

[0050] TDI 0.5 parts

[0051] EBS 0.5 share,

[0052] Antioxidant 1010 0.2 parts,

[0053] Antioxidant 168 0.3 parts;

[0054] The above raw materials were mixed at high speed by a high-speed mixer, the speed of the high-mixer was controlled to 700rmp, the mixing temperature was 60°C, and the mixing was carried out for 6 minutes;

[0055] (2) Pass the mixed material through a twin-screw extruder, and control the temperature of each zone at 195-230°C, and then pelletize the strands to obtain ABS / PA6 material. The mechanical properties of the test are shown in Table 1.

Embodiment 3

[0057] (1) Weigh the raw materials of each component according to the following parts by weight:

[0058] ABS resin (flow coefficient 3.4) 100 parts,

[0059] PA6 resin (viscosity 2.6) 30 parts,

[0060] 20 parts of glass fiber (10μm in diameter),

[0061] MDI 0.8 parts

[0062] ABS-g-MAH 10 parts,

[0063] 0.3 parts of paraffin,

[0064] Antioxidant 1076 0.2 parts,

[0065] Antioxidant 168 0.4 parts;

[0066] The above raw materials were mixed at a high speed by a high-speed mixer, the speed of the high-mixer was 700rmp, the mixing temperature was 60°C, and the mixture was mixed for 5 minutes;

[0067] (2) Pass the mixed material through a twin-screw extruder, and control the temperature of each zone at 220-235°C, and then pelletize the strands to obtain ABS / PA6 material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of polymer materials, and relates to an ABS / PA6 material and a preparation method thereof. The ABS / PA6 material comprises the following components by weight: 100 portions of an ABS resin, 10-50 portions of PA6 resin, 20-80 portions of glass fiber, 5-15 portions of a compatible agent, 0.3-1.8 portions of a chain extension agent, 0.2-1.5 portions of a lubricant and 0.3-1.0 portion of an antioxidant. The ABS / PA6 material provided by the invention has excellent extrusion resistance, and weather resistance, oil resistance, solvent resistance and mechanical properties obviously superior to those of an unmodified ABS material, and extrusion products also have excellent performance. The ABS / PA6 material can be widely used in various areas of social life, such as pipelines, architectural section and sheet, and has great economic and social values.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and relates to an ABS / PA6 material for an extrusion process and a preparation method thereof. Background technique [0002] Acrylonitrile-butadiene-styrene (ABS) is widely used in various fields of social life because of its excellent mechanical properties, dimensional stability, easy processing, coloring, and convenient post-processing. One of the wide range of polymers, while ABS has the advantages of high melt strength and good extrusion performance. But at the same time, due to the disadvantages of low heat distortion temperature, poor chemical resistance, especially oil resistance and weather resistance of ABS plastic, its application is limited. [0003] Polycaprolactam (PA6) is a crystalline thermoplastic polyester with the advantages of non-toxicity, good weather resistance, good stability against chemicals, high mechanical strength and outstanding oil and solvent resistance. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L55/02C08L77/02C08K7/14B29C47/92B29B9/06B29C48/92
Inventor 杨桂生赵敏
Owner SHANGHAI GENIUS ADVANCED MATERIAL (GRP) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com