Teflon glass fiber cloth adhesive tape

A technology of polytetrafluoroethylene and glass fiber cloth, which is applied in the direction of fiber treatment, adhesive, film/sheet adhesive, etc., can solve the problems of poor insulation performance, difficult to clean, high and low temperature resistance, etc., and achieve high insulation performance effect

Inactive Publication Date: 2014-12-31
曹建林
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. The insulation performance is poor, and it cannot prevent ultraviolet rays and static electricity well;
[0004] 2. It is not easy to clean various oil stains, stains or other attachments attached to its surface; almost all adhesive substances such as paste, resin, and paint cannot be easily removed;
[0005] 3. Not resistant to high and low temperature;
[0006] 4. Not resistant to chemical corrosion, such as strong acid, strong alkali, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] After degreasing at high temperature, the non-alkali glass fiber cloth is repeatedly coated with polytetrafluoroethylene emulsion by dipping machine to form anti-adhesive polytetrafluoroethylene glass fiber cloth, and then the polytetrafluoroethylene glass fiber cloth is activated on one side. Double the surface area of ​​the activated surface so that it can be glued in the future. Finally, use a coating machine to coat the activated PTFE glass fiber cloth with silicone self-adhesive. According to different industries, apply different thicknesses of silicone. 50m per roll is a standard package. The polytetrafluoroethylene glass fiber cloth adhesive tape contains 40% non-alkali glass fiber yarn, 53% polytetrafluoroethylene emulsion and 7% organic silica gel.

Embodiment 2

[0020] After degreasing at high temperature, the non-alkali glass fiber cloth is repeatedly coated with polytetrafluoroethylene emulsion by dipping machine to form anti-adhesive polytetrafluoroethylene glass fiber cloth, and then the polytetrafluoroethylene glass fiber cloth is activated on one side. Double the surface area of ​​the activated surface so that it can be glued in the future. Finally, use a coating machine to coat the activated PTFE glass fiber cloth with silicone self-adhesive. According to different industries, apply different thicknesses of silicone. 50m per roll is a standard package. The polytetrafluoroethylene glass fiber cloth adhesive tape contains 50% non-alkali glass fiber yarn, 45% polytetrafluoroethylene emulsion and 5% organic silica gel. Example 3

Embodiment 3

[0021] After degreasing at high temperature, the non-alkali glass fiber cloth is repeatedly coated with polytetrafluoroethylene emulsion by dipping machine to form anti-adhesive polytetrafluoroethylene glass fiber cloth, and then the polytetrafluoroethylene glass fiber cloth is activated on one side. Double the surface area of ​​the activated surface so that it can be glued in the future. Finally, use a coating machine to coat the activated PTFE glass fiber cloth with silicone self-adhesive. According to different industries, apply different thicknesses of silicone. 50m per roll is a standard package. The polytetrafluoroethylene glass fiber cloth adhesive tape contains 45% non-alkali glass fiber yarn, 50% polytetrafluoroethylene emulsion and 5% organic silica gel.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a Teflon glass fiber cloth adhesive tape. The Teflon glass fiber cloth adhesive tape is prepared from 40-50% of alkali-free glass fiber yarn, 45-55% of a Teflon emulsion and 5-8% of organic silica gel. The Teflon glass fiber cloth adhesive tape has the characteristics of high insulating properties, ultraviolet resistance and static resistance, various oil stains, dirty spots or other attachments on the surface of the Teflon glass fiber cloth adhesive tape can be cleaned easily, the Teflon glass fiber cloth adhesive tape can be used in a temperature range of -196 to 300 DEG C and has effects of resisting chemical corrosion, strong acid corrosion, strong alkali corrosion, aqua regia corrosion and various organic solvent corrosion.

Description

technical field [0001] The invention relates to an insulating tape, in particular to a polytetrafluoroethylene glass fiber cloth adhesive tape. Background technique [0002] PTFE has the characteristics of high and low temperature resistance, anti-sticking and anti-corrosion. The PTFE glass fiber cloth is made into tape, which is widely used in anti-sticking, corrosion-resistant and high-temperature-resistant surface paste; packaging, sealing heat sealing, electronic Insulation and other industries; it can also be used in non-woven drying drums, thermoplastic demoulding and other industries. PTFE fiberglass cloth adhesive tape has the advantages of high temperature resistance, anti-sticking and anti-corrosion. However, the polytetrafluoroethylene glass fiber cloth adhesive tape currently on the market has the following disadvantages due to improper composition and proportioning: [0003] 1. The insulation performance is poor, and it cannot prevent ultraviolet rays and stat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J7/04C09J183/04D06M15/256
Inventor 曹建林
Owner 曹建林
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products