Mineral halogen-free flame retardant geocell master batch

A geocell masterbatch and mine-used technology, which is applied in the field of construction, can solve problems affecting on-site construction and later effects, and achieve good flame retardancy, good compatibility, and improved adaptability

Inactive Publication Date: 2015-01-07
ANHUI JIEAOMAKE SYNTHETIC MATERIAL TECH
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the preparation of materials for geocells is relatively simple, and most of them are directly extruded from high molecular polymers and carbon black and other reinforcing agents. With the continuous development and progress of society, the research on soil environment, climate environment, etc. Or indirectly affect on-site construction and post-effects, therefore, it is necessary to further improve the performance of traditional simple geocells;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A halogen-free flame-retardant geocell masterbatch for mining, which is composed of the following raw materials in parts by weight:

[0024] High-density polyethylene 130, sodium dinitrophenolate 0.7, red phosphorus 3, talcum powder 12, decabromodiphenylethane 2, diphenylthiourea 0.2, sorbitol 2, coconut acid diethanolamide 0.5, poly Amide wax powder 3, ricinoleic acid 0.6, tributyl citrate 2, blast furnace slag 12, rare earth additive 2;

[0025] Described rare earth additive is made up of the following raw materials of weight part:

[0026] Boron carbide 40, rare earth chloride 6, attapulgite 18, silicic acid 15, aluminum tripolyphosphate 2, calcium acetate 1, phosphite 0.8, potassium carbonate 3, polyvinylpyrrolidone 0.4, silane coupling agent KH560 0.2,

[0027] Mix calcium acetate with attapulgite, ball mill evenly, add phosphite, keep stirring at 50°C for 10 minutes to obtain a mixture;

[0028] Add aluminum tripolyphosphate to 20-30 times of water, stir evenly,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a mineral halogen-free flame retardant geocell master batch which comprises the following raw materials in parts by weight: 121-130 parts of high density polyethylene, 0.7-2 parts of dinitrophenol, 2-3 parts of red phosphorus, 10-12 parts of talcum powder, 1-2 parts of decabromodiphenyl ethane, 0.1-0.2 part of diphenylthiourea, 1-2 parts of sorbitol, 0.5-1 part of coco fatty acid diethanol amide, 2-3 parts of polyamide wax powder, 0.6-1 parts of ricinoleic acid, 1-2 parts of tributyl citrate, 10-12 parts of blast furnace slag and 2-3 parts of rare earth additive. According to the mineral halogen-free flame retardant geocell master batch disclosed by the invention, high-strength boron carbide, attapulgite and rare earth elements are fully mixed by the added rare earth additive; the mixture is matched with calcium acetate as a preservative and polyvinylpyrrolidone as a stabilizer; under the surface treatment action of a silane coupling agent, the formed additive has the advantages of good surface strength, toughness, wear resistance and corrosion resistance as well as good stability; the comprehensive quality of the master batch can be effectively improved, and the adaptability to soil and the resistance to the outside pressure are improved.

Description

technical field [0001] The invention mainly relates to the construction field, in particular to a mine-used halogen-free flame-retardant geocell masterbatch. Background technique [0002] At present, the preparation of materials for geocells is relatively simple, and most of them are directly extruded from high molecular polymers and carbon black and other reinforcing agents. With the continuous development and progress of society, the research on soil environment, climate environment, etc. Or indirectly affect on-site construction and post-effects, therefore, it is necessary to further improve the performance of traditional simple geocells; [0003] Blast furnace slag is the waste discharged from the blast furnace when smelting pig iron. The main components are CaO, SiO2 and Al2O3. A lot of blast furnace slag waste is produced every year in my country. At present, it is widely used in roads, airports, foundation projects, railway ballast, Concrete aggregate and asphalt ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L77/00C08L39/06C08K13/02C08K3/38C08K3/16C08K3/34C08K3/32C08K5/098C08K5/524C08K3/26
CPCC08L23/06C08K2201/014C08L2201/02C08L2201/22C08L2205/03C08L2207/062C08L77/00C08L39/06C08K13/06C08K9/06C08K3/38C08K3/16C08K3/346C08K3/34C08K2003/327C08K5/098C08K2003/262C08K2003/026C08K5/03C08K5/11C08K5/524
Inventor 叶磊
Owner ANHUI JIEAOMAKE SYNTHETIC MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products