Conductive polyvinyl chloride foamed sole material and preparation method thereof

A polyvinyl chloride and shoe sole material technology, which is applied in the field of shoe sole materials, can solve problems such as poor electrical conductivity, and achieve the effects of not easy surface oxidation, good electrical conductivity, excellent electrical conductivity and processing performance

Inactive Publication Date: 2015-01-07
SUZHOU JINGRO TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing polyvinyl chloride foamed shoe sole materials have good i...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Conductive polyvinyl chloride foamed sole material and preparation method thereof
  • Conductive polyvinyl chloride foamed sole material and preparation method thereof
  • Conductive polyvinyl chloride foamed sole material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of conductive polyvinyl chloride foam sole material, its parts by weight consist of:

[0028]

[0029] Its manufacturing method comprises the following steps:

[0030] (1) Add the stainless steel fiber into the propanol solution of the coupling agent, stir at 60°C for 20 minutes, wash the propanol and dry to obtain the modified stainless steel fiber;

[0031] (2) adding other components and the modified stainless steel fiber obtained in step (1) into a kneader for heating and kneading, and discharging after kneading for 1.5 hours;

[0032] (3) Add the kneaded mixture into a twin-roller plastic mixer to masticate the pull sheet, and the mastication temperature is 125° C. to obtain the sheet material;

[0033] (4) The sheet material is sent into a hot press machine for heating and plasticizing, foaming, cooling and shaping after foaming, and obtaining a blank after demoulding;

[0034] (5) Send the billet into the drying room to heat and foam for 25 minutes at...

Embodiment 2

[0037] A kind of conductive polyvinyl chloride foam sole material, its parts by weight consist of:

[0038]

[0039] Its manufacturing method comprises the following steps:

[0040] (1) Add the stainless steel fiber into the propanol solution of the coupling agent, stir at 60°C for 20 minutes, wash the propanol and dry to obtain the modified stainless steel fiber;

[0041] (2) adding other components and the modified stainless steel fiber obtained in step (1) into a kneader for heating and kneading, and discharging after kneading for 1.5 hours;

[0042] (3) Add the kneaded mixture into a twin-roller plastic mixer to masticate the pull sheet, and the mastication temperature is 125° C. to obtain the sheet material;

[0043] (4) The sheet material is sent into a hot press machine for heating and plasticizing, foaming, cooling and shaping after foaming, and obtaining a blank after demoulding;

[0044] (5) Send the billet into the drying room to heat and foam for 25 minutes at...

Embodiment 3

[0047] A kind of conductive polyvinyl chloride foam sole material, its parts by weight consist of:

[0048]

[0049] Its manufacturing method comprises the following steps:

[0050] (1) Add the stainless steel fiber into the propanol solution of the coupling agent, stir at 60°C for 20 minutes, wash the propanol and dry to obtain the modified stainless steel fiber;

[0051] (2) adding other components and the modified stainless steel fiber obtained in step (1) into a kneader for heating and kneading, and discharging after kneading for 1.5 hours;

[0052] (3) Add the kneaded mixture into a twin-roller plastic mixer to masticate the pull sheet, and the mastication temperature is 125° C. to obtain the sheet material;

[0053] (4) The sheet material is sent into a hot press machine for heating and plasticizing, foaming, cooling and shaping after foaming, and obtaining a blank after demoulding;

[0054] (5) Send the billet into the drying room to heat and foam for 25 minutes at...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a conductive polyvinyl chloride foamed sole material. The conductive polyvinyl chloride foamed sole material is prepared from the following components in parts by weight: 50-65 parts of polyvinyl chloride, 15-25 parts of a plasticizer, 10-15 parts of stainless steel fiber, 0.5-3 parts of a foaming agent, 0.5-7 parts of a stabilizing agent, 1-5 parts of a coupling agent, 0.5-1 part of a lubricating agent and 6-8 parts of titanium dioxide. The invention also discloses a preparation method of the conductive polyvinyl chloride foamed sole material. The polyvinyl chloride foamed sole material provided by the invention has good conductivity and can be applied to conductive shoes.

Description

Technical field: [0001] The invention relates to a sole material, in particular to a conductive polyvinyl chloride foamed sole material and a manufacturing method thereof. Background technique: [0002] Polyvinyl chloride foam sole material has the advantages of good strength, low price, convenient processing, clear sole pattern, bright coloring, etc., so it occupies a certain proportion in the foam sole market, and is more and more favored by manufacturers. Static electricity is very common in daily work and life. The human body will generate static electricity, which will contact the sole of the human body with the sole of the shoe, and then form a loop with the earth through the sole of the shoe. Static electricity is harmful to a certain extent. In some occasions, static electricity cannot appear. In this case, people must wear clothes, footwear, etc. that can eliminate static electricity. Among them, conductive shoes have emerged as the times require. Existing polyviny...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08K13/06C08K9/06C08K5/10C08J9/10A43B13/04
CPCC08K2003/2241C08L27/06A43B13/04C08J9/103C08L2205/03C08L23/06C08L91/06C08K13/06C08K9/06C08K7/06C08K5/10C08K5/098
Inventor 黄超
Owner SUZHOU JINGRO TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap