NBR/PVC elastomer by taking LNBR as plasticizer and preparation method of elastomer

A technology of plasticizer and elastomer, which is applied in the field of NBR/PVC elastomer and its preparation, can solve the problems that have not been reported in the research, and achieve the effects of good oil resistance, improved compression performance, and reduced Mooney viscosity

Inactive Publication Date: 2015-01-21
SHENYANG INSTITUTE OF CHEMICAL TECHNOLOGY
View PDF2 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Some documents and patents have been reported on NBR / PVC blends, but the research on NBR / PVC elastomers with LNBR as a plasticizer has not been reported, so the research on NBR / PVC elastomers with LNBR as a plasticizer research is very meaningful

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • NBR/PVC elastomer by taking LNBR as plasticizer and preparation method of elastomer
  • NBR/PVC elastomer by taking LNBR as plasticizer and preparation method of elastomer
  • NBR/PVC elastomer by taking LNBR as plasticizer and preparation method of elastomer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Example 1 According to the following parts by mass: NBR: 70 parts, PVC: 30 parts, carbon black (N330): 50 parts, LNBR: 30 parts, RD: 1.5 parts, 4010NA: 1.5 parts, sulfur: 1.2 parts, DCP: 0.5 parts, CZ: 1.2 parts, TMTD: 0.3 parts, stabilizer: 1.8 parts, ZnO: 5.0 parts, stearic acid: 1.5 parts.

[0025] A kind of NBR / PVC elastomer with LNBR described in the present embodiment as plasticizer, the preparation steps of its compounded rubber and its vulcanized rubber:

[0026] (1) NBR mastication: masticate NBR on an open rubber mixer, and add anti-aging agent to mix evenly;

[0027] (2) NBR / PVC blending: Heat the plastic mixer to 150~160°C, put the PVC / stabilizer evenly mixed with a high-mix mixer on the roller of the plastic mixer for plasticization, and when it reaches the plasticized state Add NBR for blending, mix evenly and then slice, cool for later use;

[0028] (3) Preparation of mixed rubber: put the NBR / PVC blended rubber obtained in step (2) on the roller of the...

Embodiment 2

[0031] Example 2 According to the following parts by mass: NBR: 70 parts, PVC: 30 parts, carbon black (N330): 30 parts, LNBR: 30 parts, RD: 1.5 parts, 4010NA: 1.5 parts, sulfur: 1.2 parts, DCP: 0.5 parts, CZ: 1.2 parts, TMTD: 0.3 parts, stabilizer: 1.8 parts, ZnO: 5.0 parts, stearic acid: 1.5 parts. The difference between the ratio of this example and Example 1 is that 30 parts of carbon black (N330) are used.

[0032] The preparation method and performance testing standard of this embodiment are the same as those of Embodiment 1, and will not be repeated here.

Embodiment 3

[0033] Example 3 Ingredients are prepared according to the following parts by mass: NBR: 70 parts, PVC: 30 parts, carbon black (N220): 30 parts, LNBR: 30 parts, RD: 1.5 parts, 4010NA: 1.5 parts, sulfur: 1.2 parts, DCP: 0.5 parts, CZ: 1.2 parts, TMTD: 0.3 parts, stabilizer: 1.8 parts, ZnO: 5.0 parts, stearic acid: 1.5 parts. The difference between the ratio of this example and Example 1 is that 30 parts of carbon black (N220) are used.

[0034]The preparation method and performance testing standard of this embodiment are the same as those of Embodiment 1, and will not be repeated here.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an NBR / PVC elastomer by taking LNBR as a plasticizer and a preparation method of the elastomer and relates to a rubber blended elastic material and a preparation method thereof. The elastomer consists of the following components in parts by mass: 70 parts of butadiene-acrylonitrile rubber, 30 parts of polyvinyl chloride (PVC), 10-50 parts of reinforcing agent, 10-30 parts of plasticizer, 2.5-3.5 parts of anti-aging agent, 1.0-2.0 parts of vulcanizing agent, 5.0-7.0 parts of vulcanizing activator, 1.0-2.0 parts of vulcanization accelerator and 1.5-2.0 parts of stabilizer. According to the preparation method of the elastomer, the used vulcanizing temperature is 165 DEG C, so that the elastomer has excellent performances such as hot air aging resistance, wear resistance, fatigue resistance and solvent extraction resistance. The elastomer can be widely applied to the industries such as printing rubber rolls, fuel oil rubber tubes and accumulator capsules.

Description

technical field [0001] The invention relates to a rubber blended elastic material and a preparation method thereof, in particular to an NBR / PVC elastomer with LNBR as a plasticizer and a preparation method thereof. Background technique [0002] Nitrile rubber (NBR) has excellent oil resistance, heat resistance and physical and mechanical properties, but its ozone aging resistance is poor; while general-purpose synthetic resin polyvinyl chloride (PVC) has excellent flame retardancy and self-extinguishing properties As well as ozone aging resistance, chemical corrosion resistance, electrical insulation, chemical stability and thermoplasticity, but its toughness is low, it is not impact resistant, and its heat resistance is poor. [0003] Both NBR and PVC are polar polymers, the solubility parameters of the two are similar (9.64, 9.6 respectively), the compatibility is very good, and they can be blended in any proportion. The composite material made of the two blends is not...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L27/06C08K13/02C08K3/04
CPCC08L9/02B29C35/02C08L2205/03
Inventor 王重陈慧胡嘉文李雪玉张宏泽
Owner SHENYANG INSTITUTE OF CHEMICAL TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap