Calcium silicate hydrate gel solution early strength agent and preparation method thereof

A technology of hydrated calcium silicate and gel solution, applied in the field of building material production, can solve the problems of difficult storage and weighing, unsatisfactory early strength effect, complicated preparation process, etc., to reduce equipment investment, facilitate transportation and weighing good dispersion uniformity and stability

Inactive Publication Date: 2015-03-11
SHANGHAI CONSTRUCTION GROUP
View PDF6 Cites 37 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to provide a calcium silicate hydrate gel solution early strength agent and its preparation method, to solve the ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Calcium silicate hydrate gel solution early strength agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A calcium silicate hydrate gel solution early strength agent, its raw materials include: calcium material, siliceous material, gel dispersant and water, wherein the weight ratio of calcium material and siliceous material is 0.3-3: 1. The weight ratio of water to the total weight of calcareous material and siliceous material is 5-30:1, and the mass fraction of gel dispersant is 0.01%-0.50%.

[0024] Specifically, for the convenience of obtaining materials, the siliceous material is sodium silicate powder, and the calcium material is calcium nitrate crystal. According to the weight ratio of water to the total weight of calcareous material and siliceous material (i.e. water-solid ratio), the weight ratio of calcareous material and siliceous material (calcium-silicon ratio), calculate the ratio of sodium silicate, calcium nitrate and water respectively. Dosage, and accurately weighed spare. Moreover, the present invention selects high-molecular polymers such as naphthalene...

Embodiment 2

[0026] The raw material of calcium silicate hydrate gel solution early strength agent is: the molar ratio of calcium material and siliceous material is 1:1, the weight ratio of water to the total weight of calcium material and siliceous material is 5:1, The mass fraction of the gel dispersant is 0.20%. At this time, when preparing the calcium silicate hydrate gel solution, the aqueous solution of sodium silicate and the aqueous solution of calcium nitrate need to be stirred for 20 s respectively, and the dispersant needs to be stirred for 30 s respectively after adding the dispersant. Moreover, the aqueous solution of sodium silicate and calcium nitrate When the aqueous solution reacts, it needs to be stirred for 360s. Finally, the product obtained is milky white gel liquid, which is calcium silicate hydrate gel mixed solution. At this time, the mass fraction of calcium silicate hydrate in the calcium silicate hydrate gel mixed solution is about 5%.

Embodiment 3

[0028] The raw material of calcium silicate hydrate gel solution early strength agent is: the molar ratio of calcareous material to siliceous material is 0.8:1, the weight ratio of water to the total weight of calcium material and siliceous material is 10:1, The mass fraction of the gel dispersant is 0.30%. At this time, when preparing the calcium silicate hydrate gel solution, the aqueous solution of sodium silicate and the aqueous solution of calcium nitrate need to be stirred for 25 seconds respectively. , After adding the dispersant, it needs to be stirred for 45s, and when the aqueous solution of sodium silicate and the aqueous solution of calcium nitrate react, it needs to be stirred for 300s. Finally, the product obtained is milky white gel liquid, which is calcium silicate hydrate gel mixed solution. At this time, the mass fraction of calcium silicate hydrate in the calcium silicate hydrate gel mixed solution is about 3%.

[0029] In particular, in order to facilitat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a calcium silicate hydrate gel solution early strength agent and a preparation method thereof, and relates to the technical field of construction material production. The early strength agent and the method are used for solving problems of complicated preparation process, high cost, storage difficulty, weighing difficulty, and poor early strength effect of traditional calcium silicate hydrate powder. The calcium silicate hydrate gel solution early strength agent comprises a calcareous material, a siliceous material, a gel dispersant, and water. A weight ratio of the calcareous material to the siliceous material is 0.3-3:1. A weight ratio of water to the total of the calcareous material and the siliceous material is 5-30:1. The mass percentage of the gel dispersant is 0.01-0.50%. The preparation method of the early strength agent comprises the following steps: reaction materials are weighed; a sodium silicate water solution and a calcium nitrate water solution are respectively prepared; the gel dispersant is respectively added into the solutions; and the two solutions are mixed and allowed to react for a certain period of time. The early strength agent is convenient to store, transport and weigh, and have good product stability. With the early strength agent, cement-based material early strength can be effectively improved.

Description

technical field [0001] The invention relates to the technical field of building material production, in particular to a calcium silicate hydrate gel solution accelerator and a preparation method thereof. Background technique [0002] The early strength agent is an additive that accelerates the hydration of cement and improves the early strength of cement-based materials. Calcium silicate hydrate (C-S-H) is a common accelerator. Usually, sodium silicate and calcium nitrate are selected as siliceous materials and calcium materials, and the solution reaction method is used to prepare calcium silicate hydrate. Specifically, in the laboratory preparation process, first weigh sodium silicate and calcium nitrate according to a certain calcium-silicon ratio and water-solid ratio and add water to dissolve; then mix the dissolved sodium silicate solution and calcium nitrate solution, and simultaneously Add deionized water and react under water bath conditions; finally, after the rea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B24/22C04B22/08
Inventor 许永和徐俊王圣怡周云史晓婉
Owner SHANGHAI CONSTRUCTION GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap