Process for producing extra-large tension shoelace
A production process and tension technology, which is applied in the direction of footwear, shoe bindings, layered products, etc., to achieve the effect of increased tension
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0017] Example 1:
[0018] The production process of an extra-large tension shoelace of the present invention includes the following steps:
[0019] a. Use a microfiber woven from a 1.0-mm thick fiber yarn as the base of the blank. After the hot pressing pressure is 450 kg for 20 seconds, it is sanded, and then yellow glue is applied to the surface 4 times, and the temperature is Bake in a high-temperature oven at 120 degrees Celsius for 2 minutes, and finally press and paste the PU surface that simulates the skin texture on the surface through the hot press laminator;
[0020] b. The bottom of the microfiber blank with the PU surface attached, after the slitting machine is finished and slit, first coat the bottom surface with methyl ethyl ketone treatment liquid 3 times, and then coat 36 times water-based PU glue on the back;
[0021] c. The processed microfiber base and bulletproof yarns are dried in an oven at a temperature of 100 degrees Celsius for 4 minutes, pasted by an iron mo...
Example Embodiment
[0023] Example 2:
[0024] The production process of an extra-large tension shoelace of the present invention includes the following steps:
[0025] a. Use the superfiber woven from 1.5mm thick fiber yarn as the base of the blank. After the hot pressing pressure is 480 kg for 27 seconds, it is sanded, and then yellow glue is applied to the surface 5 times, and the temperature is 138 Bake in a high-temperature oven at degrees Celsius for 2 minutes, and finally press and paste the PU surface that simulates the skin texture on the surface through the hot press laminator;
[0026] b. The bottom of the microfiber blank with the PU surface attached, after being cut by the slitting machine, first coat the bottom surface with acetone treatment potion 4 times, and then coat 4-6 times water-based PU glue on the back ;
[0027] c. The processed microfiber base and bulletproof yarns are dried in an oven at a temperature of 129 degrees Celsius for 5 minutes, pasted through an iron mold, and then ...
Example Embodiment
[0030] Example 3:
[0031] The production process of an extra-large tension shoelace of the present invention includes the following steps:
[0032] a. Superfiber woven with 2mm thick fiber yarn is used as the base of the blank. After the hot pressing pressure is 500 kg for 29 seconds, it is sanded, and then yellow glue is applied to the surface 5 times, and the temperature is 150 degrees Celsius. Bake in the high-temperature oven for 3 minutes, and finally press and paste the PU surface of the simulated leather texture on the surface through the hot press laminator;
[0033] b. The bottom of the microfiber blank with the PU surface attached, after being cut by the slitting machine, first coat the bottom surface with Tianna water treatment solution 6 times, and then coat the back side with 6 times water-based PU glue ;
[0034] c. The processed microfiber base and bulletproof yarns are dried in an oven at a temperature of 150 degrees Celsius for 6 minutes, pasted by iron molds, and t...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap