A kind of finishing method of anti-wrinkle and anti-pilling pure cotton fabric

A technology of pure cotton fabric and anti-wrinkle finishing agent, which is applied in fiber treatment, plant fiber, textiles and papermaking, etc., can solve the problems of poor anti-pilling strength and anti-wrinkle performance, and achieve improved anti-wrinkle strength and anti-pilling strength, The effect of large anti-wrinkle recovery angle

Inactive Publication Date: 2016-05-18
诸暨市荣恩针纺织有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Technical problem to be solved: due to its specific material, pure cotton fabric has poor pilling strength and wrinkle resistance after repeated use. The purpose of this invention is to improve the pilling strength and wrinkle resistance of pure cotton fabric strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] (1) Prepare anti-wrinkle finishing agent, take polyoxypropylene glyceryl ether as 20Kg, triethanolamine borate as 8Kg, sulfosuccinic acid-1,4-dipentyl sodium as 16Kg, ethylene glycol as 6Kg, water as 150Kg, the above ingredients are heated and mixed evenly to be an anti-wrinkle finishing agent; (2) preparing an anti-pilling finishing agent, taking melamine as 4Kg, trimethylolpropane as 8Kg, urethane as 5Kg, glycerin as 20Kg, The water is 105Kg, and the above ingredients are heated and mixed to form an anti-pilling finishing agent; (3) Take pure cotton fabric, immerse the pure cotton fabric in the anti-wrinkle finishing agent, soak for 3 hours at 40°C, soak twice, The remaining rate is 90%, and it is dried at 90°C; (4) After drying, the pure cotton fabric that has undergone anti-wrinkle finishing is immersed in the anti-pilling finishing agent, soaked at 40°C for 2 hours, dipped twice and rolled twice, rolled The remaining rate is 85%, and it is dried at 90°C. After the ...

Embodiment 2

[0020] (1) prepare anti-wrinkle finishing agent, take polyoxypropylene glyceryl ether as 14Kg, triethanolamine borate as 16Kg, sulfosuccinic acid-1,4-dipentyl sodium as 24Kg, ethylene glycol as 12Kg, water as 90Kg, the above ingredients are heated and mixed evenly to be an anti-wrinkle finishing agent; (2) preparing an anti-pilling finishing agent, taking melamine as 8Kg, trimethylolpropane as 11Kg, urethane as 9Kg, glycerin as 15Kg, The water is 140Kg, and the above ingredients are heated and mixed to form an anti-pilling finishing agent; (3) Take pure cotton fabric, immerse the pure cotton fabric in the anti-wrinkle finishing agent, soak at 40°C for 1 hour, dip twice and roll twice, The residual rate is 70%, and it is dried at 90°C; (4) After drying, the pure cotton fabric that has undergone anti-wrinkle finishing is immersed in the anti-pilling finishing agent, soaked at 40°C for 2 hours, dipped twice and rolled twice, rolled The remaining rate is 75%, and it is dried at 90...

Embodiment 3

[0023] (1) Prepare anti-wrinkle finishing agent, take polyoxypropylene glyceryl ether as 19Kg, triethanolamine borate as 10Kg, sulfosuccinic acid-1,4-dipentyl sodium as 22Kg, ethylene glycol as 7Kg, water as 110Kg, the above ingredients are heated and mixed evenly to be an anti-wrinkle finishing agent; (2) preparing an anti-pilling finishing agent, taking melamine as 6Kg, trimethylolpropane as 10Kg, urethane as 6Kg, glycerin as 18Kg, The water is 115Kg, and the above ingredients are heated and mixed to form an anti-pilling finishing agent; (3) Take pure cotton fabric, immerse the pure cotton fabric in the anti-wrinkle finishing agent, soak for 2 hours at 40°C, soak twice, roll twice, The remaining rate is 90%, and it is dried at 90°C; (4) After drying, the pure cotton fabric that has undergone anti-wrinkle finishing is immersed in the anti-pilling finishing agent, soaked at 40°C for 2 hours, dipped twice and rolled twice, rolled The remaining rate is 85%, and it is dried at 90...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a treatment method of a novel anti-wrinkle anti-pilling pure cotton fabric. The treatment method comprises the following steps: (1) respectively taking polyoxypropylene glycerol ether, triethanolamine borate, sulfosuccinic acid-1,4-sodium diamyl, glycol and water, and heating and uniformly mixing the components, so as to obtain an anti-wrinkle treatment agent; (2) respectively taking melamine, trimethylolpropane, ethyl carbamate, glycerin and water, and heating and uniformly mixing the components, so as to obtain an anti-pilling treatment agent; (3) immersing a pure cotton fabric in the anti-wrinkle treatment agent at 40 DEG C for 1-3 hours, immersing and rolling twice until the liquid detention rate is 70%-90%, and drying at 90 DEG C; and (4) after drying, immersing the pure cotton fabric which is subjected to anti-wrinkle treatment in the anti-pilling treatment agent at 40 DEG C for 2 hours, immersing and rolling twice until the liquid detention rate is 75%-85%, and drying at 90 DEG C, so as to obtained the treated anti-wrinkle anti-pilling pure cotton fabric.

Description

technical field [0001] The invention belongs to the field of textile material finishing, and relates to a finishing method for anti-wrinkle and anti-pilling pure cotton fabrics. Background technique [0002] There are some problems in conventional wrinkle-resistant finishing methods for pure cotton fabrics. The first is that the mechanical properties of pure cotton fabrics after wrinkle-resistant finishing have undergone significant changes, such as breaking strength, breaking elongation, and tearing strength, which have all declined to varying degrees. The second is that a large amount of formaldehyde will be released during the anti-wrinkle finishing process, which will seriously affect human health and pollute the environment. Moreover, pure cotton fabrics will also decompose formaldehyde during storage or wearing to irritate human skin and respiratory mucosa, which may cause cancer. Therefore, non-irritating and non-carcinogenic finishing agents are needed to finish pu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/53D06M13/224D06M13/148D06M13/364D06M13/425D06M101/06
Inventor 郭圣
Owner 诸暨市荣恩针纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com