Plant straw, recycled plastic and reclaimed rubber composite plate stool surface

A technology of plant straw and regenerated rubber, which is applied to rubber layered products, synthetic resin layered products, lamination, etc. It can solve the problems of too hard and uncomfortable sitting, underutilization, poor thermal insulation performance, etc., and achieve thermal insulation Good performance, low density and low cost

Active Publication Date: 2015-04-08
SHANDONG LVSEN WOOD PLASTIC COMPOSITE
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the increase of crop production, various plant stalks such as rice, wheat, corn, etc. remain relatively large and are not fully utilized. The smog weather caused by burning straws is gradually increasing every year; recycled plastics and reclaimed rubber are relatively cheap because of their low prices. In recent years, it has become more and more widely used; most of the stool surfaces used in the market are high-density boards or plastics, which mainly have problems such as high density, poor thermal insulation performance, and too hard and uncomfortable sitting feeling; the combination of plant straw and recycled plastic And recycled rubber compound, can prepare light weight, heat preservation, comfortable, environment-friendly bench surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plant straw, recycled plastic and reclaimed rubber composite plate stool surface

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Corn stalks are selected and processed into straw powder with a particle size of about 160-180um after being dried and crushed.

[0015] Weigh the parts by weight of each raw material of the wood-plastic foam layer according to the formula, put the material in a high-mixer at 80-100°C, store the material at high-speed mixing for 10-20 minutes, put the mixed material into the bench surface mold, and use it as Bottom material: Weigh the parts by weight of the raw materials of the regenerated rubber foam layer according to the formula, plasticize and knead on the open mill for 3-5 minutes, and then produce the regenerated film, cut it and put it into the bench surface mold, and use it as the surface layer material.

[0016] Put the loaded mold in a flat press, press it at 170-190°C and 5-10Mpa for 10-20min, remove the mold and cool it to room temperature, and open the mold to get the finished bench surface.

Embodiment 2

[0018] Wheat straw is selected and processed into straw powder with a particle size of about 160-180um after being dried and crushed.

[0019] Weigh the parts by weight of each raw material of the wood-plastic foam layer according to the formula, put the material in a high-mixer at 80-100°C, store the material at high-speed mixing for 10-20 minutes, put the mixed material into the bench surface mold, and use it as Bottom material: Weigh the parts by weight of the raw materials of the regenerated rubber foam layer according to the formula, plasticize and knead on the open mill for 3-5 minutes, and then produce the regenerated film, cut it and put it into the bench surface mold, and use it as the surface layer material.

[0020] Put the loaded mold in a flat press, press it at 170-190°C and 5-10Mpa for 10-20min, remove the mold and cool it to room temperature, and open the mold to get the finished bench surface.

Embodiment 3

[0022] Wheat straw is selected and processed into straw powder with a particle size of about 160-180um after being dried and crushed.

[0023] Weigh the parts by weight of each raw material of the wood-plastic foam layer according to the formula, put the material in a high-mixer at 80-100°C, store the material at high-speed mixing for 10-20 minutes, put the mixed material into the bench surface mold, and use it as Bottom material: Weigh the parts by weight of the raw materials of the regenerated rubber foam layer according to the formula, plasticize and knead on the open mill for 3-5 minutes, and then produce the regenerated film, cut it and put it into the bench surface mold, and use it as the surface layer material.

[0024] Put the loaded mold in a flat press, press it at 170-190°C and 5-10Mpa for 10-20min, remove the mold and cool it to room temperature, and open the mold to get the finished bench surface.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a plant straw, recycled plastic and reclaimed rubber composite plate stool surface which is characterized by being prepared from: I, a reclaimed rubber foamed layer which is prepared from the following raw materials in parts by weight: 100 parts of reclaimed rubber, 5-7 parts of a composite foaming agent, 1-2 parts of sulfur, 2-3 parts of zinc oxide, 1-2 parts of stearic acid, 1-2 parts of an accelerant M and 20-50 parts of light calcium, and II, a sythetic-wood foamed layer which is prepared from the following raw materials in parts by weight: 100 parts of recycled polyolefin, 30-50 parts of plant straw powder, 6-8 parts of a composite foaming agent and 10 parts of light calcium. The plant straw, recycled plastic and reclaimed rubber composite plate stool surface has the beneficial effects that the bending resistance of the stool surface is greater than 10Mpa, the tensile strength of the stool surface is greater than 20Mpa, the Shore type A hardness of the reclaimed rubber is 40-50 degrees, and the stool surface has the advantages that the waste is turned into wealthy, the cost is low, the density is relatively small, the heat preservation property is good, the heat is insulated, the external temperature influence is avoided, the surface is flexible, rich in elasticity and comfortable to sit, and the environment can be protected.

Description

technical field [0001] The invention relates to a composite bench surface of plant stalks, recycled plastics and regenerated rubber. Background technique [0002] With the increase of crop production, various plant stalks such as rice, wheat, corn, etc. remain relatively large and are not fully utilized. The smog weather caused by burning straws is gradually increasing every year; recycled plastics and reclaimed rubber are relatively cheap because of their low prices. In recent years, it has become more and more widely used; most of the stool surfaces used in the market are high-density boards or plastics, which mainly have problems such as high density, poor thermal insulation performance, and too hard and uncomfortable sitting feeling; the combination of plant straw and recycled plastic And recycled rubber compound, can prepare light weight, heat preservation, comfortable, environment-friendly bench surface. Contents of the invention [0003] The purpose of the present ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L17/00C08K13/02C08K3/26C08K3/06C08K3/22C08K5/09C08L23/00C08L97/02B32B25/08B32B27/06B32B27/32B32B27/18B32B5/32B32B37/06
Inventor 安云鹏冯起杨洁周峰张金伟
Owner SHANDONG LVSEN WOOD PLASTIC COMPOSITE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com