A method for preparing foam insulation building materials using soot carbon powder as foaming agent

A technology of soot carbon powder and foaming agent, which is applied in the field of foam insulation building materials manufacturing, can solve the problems of land occupation, manpower and material resources, and pollution of underground water quality, and achieve high yield, low production cost, and good promotion and use value Effect

Active Publication Date: 2016-06-08
CHINA UNIV OF GEOSCIENCES (BEIJING)
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the landfill of soot carbon powder not only consumes manpower and material resources, occupies land, but also pollutes groundwater quality.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing foam insulation building materials using soot carbon powder as foaming agent
  • A method for preparing foam insulation building materials using soot carbon powder as foaming agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The technical solution adopted by the present invention is a method for preparing foam insulation building materials using soot carbon powder as a foaming agent. The steps of the method include:

[0028] (1) Mixture treatment: Weigh the soot toner foaming agent, raw materials, fluxing agent, and foam stabilizer according to the mass percentage of the mixture, add them into a ball mill tank to obtain the mixture, and then carry out dry pressing molding of the mixture. The formed blank is put into the mould;

[0029] In this step, the mass percentages of each component in the mixture are: 3% ball-milled soot carbon powder foaming agent, 85% ball-milled raw materials, 9% flux, and 3% foam stabilizer. The raw material is waste glass. The flux is borax; the foam stabilizer is sodium phosphate. The particle size of the mixture obtained after ball milling in the ball mill tank is less than 200 mesh. Ensure the smaller particle size, so as to ensure the uniformity and produc...

Embodiment 2

[0038] On the basis of Example 1, this example is a method for preparing a foam insulation building material using soot carbon powder as a foaming agent. The steps of the method include:

[0039] (1) Mixture treatment: Weigh the soot toner foaming agent, raw materials, fluxing agent, and foam stabilizer according to the mass percentage of the mixture, add them into a ball mill tank to obtain the mixture, and then carry out dry pressing molding of the mixture. The formed blank is put into the mould;

[0040] In this step, the mass percentage of each component in the mixture is: 2% of ball-milled soot carbon powder foaming agent, 80% of ball-milled raw material, 16% of flux, and 2% of foam stabilizer. The raw material is fly ash. The flux is borax; the foam stabilizer is sodium phosphate. The particle size of the mixture obtained after ball milling in the ball milling tank is less than 200 mesh.

[0041] (2) Preheating stage treatment: The resistance furnace is heated to 200°C ...

Embodiment 3

[0048] On the basis of Embodiment 1, this embodiment is a method for preparing foam thermal insulation building materials by using soot carbon powder as a foaming agent, and the steps of the method include:

[0049] (1) Mixture treatment: Weigh the soot and carbon powder foaming agent, raw materials, fluxing agent, and foam stabilizer according to the mass percentage of the mixture, add it into a ball mill tank and ball-mill to obtain a mixture, and then dry-press the mixture to form the mixture. The formed blank is put into the mold;

[0050] In this step, the mass percentages of each component in the mixture are: 4% ball-milled soot carbon powder foaming agent, 75% ball-milled raw material, 16% fluxing agent, and 5% foam stabilizer. The raw material is fly ash. The flux is borax; the foam stabilizer is sodium phosphate. The particle size of the mixture obtained after ball milling in the ball milling tank is less than 200 mesh.

[0051] (2) Preheating stage treatment: The ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
densityaaaaaaaaaa
strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing a foam thermal insulation building material by using soot carbon powder as a foaming agent. The steps of the method include: processing a mixture; processing in a preheating stage; processing in a foaming stage; processing in a foam stabilizing stage; and cooling processing . The preparation method uses soot carbon powder as a foaming agent, can effectively and rationally utilize natural resources, effectively reduce the production cost of foam insulation building materials, reduce environmental pollution, save natural resources, effectively utilize waste materials, and reduce environmental pollution of materials and building material cost; the foam insulation building material prepared by the inventive method has a density of 0.27-0.62g / cm3, a strength of 2.32-8.96MPa, a porosity of 76-88%, and good building insulation performance, which is better than existing foam insulation Building materials have higher performance and lower production costs, and have greater promotion and application value.

Description

technical field [0001] The invention relates to a method for manufacturing a foam thermal insulation building material, in particular to a method for preparing a foam thermal insulation building material by using soot carbon powder as a foaming agent. Background technique [0002] my country's high-pollution and high-emission industries mainly include non-metallic mineral product processing industry and power industry. With the acceleration of China's urbanization process and rapid economic development, the market size of my country's steel structure will grow steadily, and the metallurgical industry, metal abrasives and shot (spray) pills will also develop further. In the process of using high-frequency electric furnaces and medium-frequency induction furnaces to recycle scrap metal, high-molecular organic matter such as impurities, coatings, paints, and electroplating protective layers attached to scrap metal materials are carbonized at high temperatures into fine industri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/02
Inventor 张以河黄洪伟郭禹希刘洋洋涂姝臣李宝迎孟祥海
Owner CHINA UNIV OF GEOSCIENCES (BEIJING)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products