Platelet-rich plasma separation gel and platelet-rich plasma preparation method
A technology of platelet-rich plasma and separation gel, which is applied in the field of platelet-rich plasma separation gel and the preparation of platelet-rich plasma using the separation gel, can solve the problems of preparation system pollution, easy inhalation of blood cells, incomplete recovery of platelets, etc. and easy dispersibility, prevent external contamination, and reduce the effect of application risk
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0055] [Example 1]
[0056] Such as figure 2 The manufacturing method of the platelet-rich plasma separation gel of this embodiment is:
[0057] Step1: Synthesize basic polymer:
[0058]
[0059] The raw materials are mixed according to the above formula, placed in a sealed reactor, mixed, heated to 80-120°C, reacted for 6-8 hours to synthesize the basic compound.
[0060] Step2. High-temperature and high-vacuum distillation purification: Use water jet-Roots two-stage series vacuum pump to make the system vacuum lower than -0.098Mpa, and the temperature rises to 190-200 degrees for 6-8 hours to obtain relatively pure polymer polymerization Material, that is, resin.
[0061] Step3. Fine filtration: 250 mesh fine filtration to the mixing tank to remove impurities and accurately weigh the resin.
[0062] Step4, the specific gravity agent accurately adjusts the specific gravity: After the previous step, the weight of the basic polymer compound obtained is 600kg. Select 24 kg of nano-grade...
Example Embodiment
[0068] [Example 2]
[0069] In the platelet-rich plasma separation gel of this embodiment, the product formula of the basic polymer compound is:
[0070]
[0071] The weight ratio of the added silica to the base polymer and the weight ratio of BYK-420 organic thixotropic agent to the base polymer are 4.6:100 and 1.1:100, respectively. The preparation method is the same as that of Example 1, and it is prepared according to the above formula The obtained plasma separator gel has a measured specific gravity of 1.075, which can separate and enrich leukocytes and platelets, obtain leukocyte-rich platelet plasma (L-PRP), and increase the effect of anti-inflammatory treatment while repairing tissue.
Example Embodiment
[0072] [Example 3]
[0073] In the platelet-rich plasma separation gel of this embodiment, the product formula of the basic polymer compound is:
[0074]
[0075] The weight ratio of the added silica to the base polymer and the weight ratio of BYK-420 organic thixotropic agent to the base polymer are 5:100 and 1.2:100, respectively. The preparation method is the same as that of Example 1, and it is prepared according to the above formula. The obtained plasma separator gel has a measured specific gravity of 1.080, which can separate and enrich lymphocytes, monocytes and platelets to obtain mononuclear cell-rich platelet plasma (M-PRP), which is used for lymphocyte immune function detection, human leukocyte antigen ( HLA) or residual leukemia gene detection, and used for simple arteriosclerosis obliterans, thromboangiitis obliterans, diabetic lower limb ischemia and other diseases and treatments.
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap