Special material for stainless steel-based composite coating for thin valve plate and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A composite coating, stainless steel technology, applied in heating inorganic powder coating and other directions, can solve the problems of oxidative decomposition of coating materials, poor coating adhesion, thin coating thickness, etc., to increase coating thickness and improve interface bonding The effect of sufficient strength and plastic deformation
Inactive Publication Date: 2017-11-24
瑞安市博业激光应用技术有限公司 +1
View PDF2 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0009] The present invention aims at the above-mentioned deficiencies existing in the existing valve surface modification coating and its preparation technology, and provides a stainless steel substrate for surface modification of thin valve plates, which uses stainless steel as the bonding phase and hard phase particles as the reinforcing phase. The special material for wear-resistant and corrosion-resistant composite coating and its efficient preparation method solve the problems of oxidative decomposition of coating material, workpiece deformation, thin coating thickness and poor coating adhesion in the existing preparation technology
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0024] The present invention will be further described below in conjunction with the accompanying drawings and specific examples according to the technical solutions of the present invention, but the present invention is not limited to the following examples.
[0025] 316L stainless steel powder is selected as the binder phase of the composite coating and mixed with WC hard phase particles.
[0026] Among them: the content of each element in the composite coating is respectively: the content of each element in the composite coating is respectively: Cr8~9wt%, Ni 5~6wt%, Mo 1~2wt%, W 42~43wt%, C 2~ 3wt%, the balance is Fe.
[0027] 316L stainless steel powder and WC hard phase particle powder are mixed by ball milling at a volume ratio of 7:3. The ball milling method is planetary ball milling, the ball milling speed is 400r / min, the ball milling time is 3h, and the substrate is made of stainless steel with a large area and thin valve. plate, the valve plate area is 297cm 2 , T...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to the field of material-surface modification, particularly to a special material for stainless steel substrates composite coating for a thin valve plate and a preparation method of the special material. According to the special material for the stainless steel substrate composite coating for the thin valve plate, stainless steel metal powder is used as a composite coating bonding phase, and the wear resistance is improved through the introduction of hard-phase particles, wherein the stainless steel metal powder is 316L stainless steel powder, the hard-phase particles are WC, and the composite coating comprises the following elements in percentage by weight: 8-9% of Cr, 5-6% of Ni, 1-2% of Mo, 42-43% of W, 2-3% of C, and the balance of Fe. The wear-resistant corrosion-resistant stainless steel substrate composite coating which is disclosed by the invention, is prepared by a method based on cold spraying, the characteristic of low-temperature deposition of the cold spraying is kept, so that undesirable phenomena, such as decomposition, oxidation, phase transition, crystal grain growth and the like, of the coating material, which are caused by high-temperature deposition techniques, such as laser cladding, hot spraying and the like, are avoided.
Description
【Technical field】 [0001] The invention relates to the field of material surface modification, in particular to a special stainless steel-based composite coating material for thin valve plates and a preparation method thereof. 【Background technique】 [0002] Valves are one of the important components of the equipment manufacturing industry and the main control components in fluid delivery systems, widely used in chemical, petrochemical, petroleum, papermaking, mining, electric power, food, pharmaceuticals, water supply and drainage, mechanical equipment, electronics , urban construction and other fields, including ball valves, butterfly valves, gate valves, globe valves, regulating valves and other types. [0003] The sealing performance of the valve is the most important technical performance index of the valve. The sealing part of the valve (such as the contact between the opening and closing parts and the two sealing surfaces of the valve seat, the joint between the packin...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.